Crosslinked vinyl acetate-maleic anhydride heteropolymers and derivatives prepared from them
Assignee: NL Chemicals Inc
•
Filing: 1974-12-24
•
Granted: 1976-05-11
•
Expires: 1994-12-24
Abstract
Abstract Novel crosslinked heteropolymers of vinyl acetate and maleic anhydride are provided which are useful as aqueous thickeners for aqueous formulations such as cosmetics and latex paints. Ester and amide derivatives of the combined maleic anhydride portion of the heteropolymer are also provided. The process for preparing the crosslinked heteropolymers comprises adding a maleic anhydride monomer, and crosslinking agent monomer, and catalyst in controlled amounts to a monomer solution of vinyl acetate.
Inventors
- 👤 William G. Carpenter
- 👤 Daniel F. Herman
- 👤 Rudolph J. Berndlmaier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:19
CPC Classifications
C; C08; C08L; C08L31/00; C08L31/02; C08L31/04; A; A61; A61K; A61K8/00; A61K8/18; A61K8/72; A61K8/81; A61K8/8164; A61Q; A61Q19/00; C02; C02F; C02F1/00; C02F1/52; C02F1/54; C08F; C08F218/00; C08F218/02; C08F218/04; C08F218/08; C08F8/00; C08F8/14; C08F8/44; A61Q11/00; C08F2800/00; C08F2800/10; C08F2810/00; C08F2810/20
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
238 words
A process for preparing crosslinked heteropolymers of vinyl ester and maleic derivatives by combining vinyl ester monomers, maleic derivative monomers, and crosslinking agent monomers, wherein the mole ratio of vinyl ester monomers to maleic derivative monomers is from 1.1:1 to 3:1 and wherein the amount of crosslinking agent monomers is from 0.2 to 3 weight percent based on the total amount of monomers which comprises the steps of: a. providing a vinyl ester monomer solution wherein the vinyl ester monomer solution is the reaction solution; b. providing a maleic derivation monomer-crosslinking agent monomer solution; c. providing a catalyst solution; d. adding an amount of the maleic derivative monomer-crosslinking agent monomer solution to the reaction solution to form a polymerizable solution wherein the added amount is such that the unreacted amounts of the maleic derivative monomer and cross-linking agent monomer in the reaction solution do not exceed 1/15th of the total amounts to be added. e. adding an amount of catalyst solution wherein the added amount is sufficient to promote heteropolymerization but in an insufficient amount to promote homopolymerization of the vinyl ester; f. polymerizing the reaction solution at a polymerizable temperature; and g. repeating steps (d), (e), and (f) until all the maleic derivative monomers, crosslinking agent monomers, and catalyst has been added and the heteropolymer formed wherein the mole ratio of the combined vinyl ester to combined maleic derivatives in the heteropolymer is from 1.1:1 to 3:1.
Claim 2
Dependent Claim
238 words
A process for preparing crosslinked heteropolymers of vinyl ester and maleic derivatives by combining vinyl ester monomers, maleic derivative monomers, and crosslinking agent monomers, wherein the mole ratio of vinyl ester monomers to maleic derivative monomers is from 1.1:1 to 3:1 and wherein the amount of crosslinking agent monomers is from 0.2 to 3 weight percent based on the total amount of monomers which comprises the steps of: a. providing a vinyl ester monomer solution wherein the vinyl ester monomer solution is the reaction solution; b. providing a maleic derivation monomer-crosslinking agent monomer solution; c. providing a catalyst solution; d. adding an amount of the maleic derivative monomer-crosslinking agent monomer solution to the reaction solution to form a polymerizable solution wherein the added amount is such that the unreacted amounts of the maleic derivative monomer and cross-linking agent monomer in the reaction solution do not exceed 1/15th of the total amounts to be added. e. adding an amount of catalyst solution wherein the added amount is sufficient to promote heteropolymerization but in an insufficient amount to promote homopolymerization of the vinyl ester; f. polymerizing the reaction solution at a polymerizable temperature; and g. repeating steps (d), (e), and (f) until all the maleic derivative monomers, crosslinking agent monomers, and catalyst has been added and the heteropolymer formed wherein the mole ratio of the combined vinyl ester to combined maleic derivatives in the heteropolymer is from 1.1:1 to 3:1.
Claim 3
Dependent Claim
23 words
The process according to claim 1 wherein the mole ratio of vinyl ester monomers to maleic derivative monomers is from 1.2:1 to 1.5:1.
Claim 4
Dependent Claim
27 words
The process according to claim 1 wherein the amount of crosslinking agent monomers is from 0.5 to 2.0 weight percent based on the total amount of monomers.
Claim 5
Dependent Claim
13 words
The process according to claim 1 wherein the vinyl ester is vinyl acetate.
Claim 6
Dependent Claim
13 words
The process according to claim 1 wherein the cross-linking agent is allyl methacrylate.
Claim 7
Dependent Claim
33 words
The process according to claim 1 wherein the maleic derivative is selected from the group consisting of maleic anhydride, maleic acid, maleic acid salts, esters of maleic acid and amides of maleic acid.
Claim 8
Dependent Claim
13 words
The process according to claim 6 wherein the maleic derivative is maleic anhydride.
Claim 9
Dependent Claim
36 words
The process according to claim 1 wherein the maleic derivative is represented by the formula: ##EQU2## wherein R is a radical selected from the group consisting of hydroxyl, alcoholate, substituted alcoholate, glycolate, amino and substituted amino.
Claim 10
Dependent Claim
24 words
The process according to claim 1 wherein the catalyst is selected from the group consisting of isopropyl peroxydicarbonate, dichlorobenzoyl peroxide, benzoyl peroxide and azobisisobutyronitrile.
Claim 11
Dependent Claim
12 words
The process according to claim 9 wherein the catalyst is benzoyl peroxide.
Claim 12
Dependent Claim
239 words
A crosslinked heteropolymers of vinyl ester and maleic derivatives prepared by the process of combining vinyl ester monomers, maleic derivative monomers, and crosslinking agent monomers, wherein the mole ratio of vinyl ester monomers to maleic derivative monomers is from 1.1:1 to 3:1 and wherein the amount of crosslinking agent monomers is from 0.2 to 3 weight percent based on the total amount of monomers which comprises the steps of: a. providing a vinyl ester monomer solution wherein the vinyl ester monomer solution is the reaction solution; b. providing a maleic derivative monomer-crosslinking agent monomer solution; c. providing a catalyst solution; d. adding an amount of the maleic derivative monomer-crosslinking agent monomer solution to the reaction solution to form a polymerizable solution wherein the added amount is such that the unreacted amounts of the maleic derivative monomer and crosslinking agent monomer in the reaction solution do not exceed 1/15th of the total amounts to be added; e. adding an amount of catalyst solution wherein the added amount is sufficient to promote heteropolymerization but in an insufficient amount of promote homopolymerization of the vinyl ester; f. polymerizing the reaction solution at a polymerizable temperature; and g. repeating steps (d), (e), and (f) until all the maleic derivative monomers, crosslinking agent monomers, and catalyst has been added and the heteropolymer formed wherein the mole ratio of the combined vinyl ester to combined maleic derivatives in the heteropolymer is form 1.1:1 to 3:1.
Claim 13
Dependent Claim
239 words
A crosslinked heteropolymers of vinyl ester and maleic derivatives prepared by the process of combining vinyl ester monomers, maleic derivative monomers, and crosslinking agent monomers, wherein the mole ratio of vinyl ester monomers to maleic derivative monomers is from 1.1:1 to 3:1 and wherein the amount of crosslinking agent monomers is from 0.2 to 3 weight percent based on the total amount of monomers which comprises the steps of: a. providing a vinyl ester monomer solution wherein the vinyl ester monomer solution is the reaction solution; b. providing a maleic derivative monomer-crosslinking agent monomer solution; c. providing a catalyst solution; d. adding an amount of the maleic derivative monomer-crosslinking agent monomer solution to the reaction solution to form a polymerizable solution wherein the added amount is such that the unreacted amounts of the maleic derivative monomer and crosslinking agent monomer in the reaction solution do not exceed 1/15th of the total amounts to be added; e. adding an amount of catalyst solution wherein the added amount is sufficient to promote heteropolymerization but in an insufficient amount of promote homopolymerization of the vinyl ester; f. polymerizing the reaction solution at a polymerizable temperature; and g. repeating steps (d), (e), and (f) until all the maleic derivative monomers, crosslinking agent monomers, and catalyst has been added and the heteropolymer formed wherein the mole ratio of the combined vinyl ester to combined maleic derivatives in the heteropolymer is form 1.1:1 to 3:1.
References Cited (Backward Citations)
US3165486A
Cited
US2971939A
Cited
US3085986A
Cited
US3398092A
Cited
US3554985A
Cited
US3415745A
Cited
US3557067A
Cited
US3660339A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-11 | 1979-11-10 | 1980-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-11 | 1983-11-10 | 1984-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-11 | 1987-11-10 | 1988-05-11 | $7700.00 | Window Closed / Lapsed |