Catalysts for production of cycloalkylaromatics
Assignee: Phillips Petroleum Co
•
Filing: 1974-05-09
•
Granted: 1976-05-11
•
Expires: 1994-05-09
Abstract
Abstract Cycloalkylaromatics are produced from aromatic hydrocarbons in the presence of hydrogen and an aqueous HF-treated ruthenium halide-active clay catalyst which has been promoted with at least one compound of iron, cobalt, and nickel. Preferably the catalyst has not been heated under calcination conditions prior to use. In a specific embodiment, benzene is converted to cyclohexylbenzene with good selectivity over an active clay impregnated with ruthenium chloride and hydrogen fluoride and at least one compound of iron, cobalt, and nickel.
Inventors
- 👤 Ernest A. Zuech
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:14
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/22; B01J37/26; B01J27/00; B01J27/06; B01J27/08; C; C07; C07C; C07C2/00; C07C2/74; C07C2521/00; C07C2521/16; C07C2601/00; C07C2601/12; C07C2601/14
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
85 words
A process for the preparation of a promoted ruthenium halide-active clay catalyst which comprises the steps of treating a particulate active clay with aqueous HF followed by impregnation with an alcoholic or aqueous solution of a ruthenium halide and a halide of at least one of iron, cobalt, or nickel, and removing the alcohol or water from the impregnated catalyst by heating at a temperature sufficient to volatilize said alcohol or water, and remove same from said catalyst but insufficient to calcine the catalyst composition.
Claim 2
Dependent Claim
85 words
A process for the preparation of a promoted ruthenium halide-active clay catalyst which comprises the steps of treating a particulate active clay with aqueous HF followed by impregnation with an alcoholic or aqueous solution of a ruthenium halide and a halide of at least one of iron, cobalt, or nickel, and removing the alcohol or water from the impregnated catalyst by heating at a temperature sufficient to volatilize said alcohol or water, and remove same from said catalyst but insufficient to calcine the catalyst composition.
Claim 3
Dependent Claim
29 words
A process according to claim 1 wherein said ruthenium halide is ruthenium trichloride and said solvent is ethanol and said heating is effected at a temperature below about 380°C.
Claim 4
Dependent Claim
76 words
A process according to claim 1 wherein the amount of ruthenium deposited on said active clay is in the range of 0.01 to 2 weight percent, the amount of metal promoter is in the range of 0.001 to 3 weight percent, the amount of HF based on active clay is in the range of 1 to 15 weight percent, and the weight ratio of ruthenium to metal promoter is in the range of 10:1 to 1:1.5.
Claim 5
Dependent Claim
56 words
A process according to claim 1 wherein aqueous HF is applied to the active clay followed by heating to remove water therefrom and then the HF-treated active clay is impregnated with an ethanolic solution of ruthenium trichloride and metal promoter chloride followed by heating to remove alcohol therefrom under conditions insufficient to calcine said catalyst composite.
Claim 6
Dependent Claim
37 words
A process according to claim 1 wherein the ruthenium halide-active clay catalyst is a ruthenium chloride-montmorillonite active clay catalyst promoted with nickel which has been treated with 1 to 15 weight percent HF based on active clay.
Claim 7
Dependent Claim
83 words
An active clay-ruthenium halide non-calcined catalyst composition effective for the conversion of aromatics to cycloalkylaromatics comprising 0.01 to about 2 weight percent ruthenium promoted with from 0.001 to about 3 weight percent of at least one promoter metal halide compound of iron, cobalt, and nickel in a weight ratio of ruthenium to promoter metal in the range 10:1 to 1:1.5 and which catalyst has been treated with aqueous HF in an amount ranging from 1 to 15 weight percent based on active clay.
Claim 8
Dependent Claim
83 words
An active clay-ruthenium halide non-calcined catalyst composition effective for the conversion of aromatics to cycloalkylaromatics comprising 0.01 to about 2 weight percent ruthenium promoted with from 0.001 to about 3 weight percent of at least one promoter metal halide compound of iron, cobalt, and nickel in a weight ratio of ruthenium to promoter metal in the range 10:1 to 1:1.5 and which catalyst has been treated with aqueous HF in an amount ranging from 1 to 15 weight percent based on active clay.
Claim 9
Dependent Claim
15 words
A catalyst according to claim 6 wherein said catalyst is a ruthenium chloride-montmorillonite active clay.
Claim 10
Dependent Claim
12 words
A catalyst according to claim 6 wherein the promoter metal is nickel.
Claim 11
Dependent Claim
52 words
A catalyst according to claim 6 wherein the catalyst contains from 0.1 to 1 weight percent ruthenium, 0.05 to 1 weight percent promoter metal, the weight ratio of ruthenium to promoter metal is 1:0.5 to 1:1, and the amount of HF present, based on active clay, is 5 to 10 weight percent.
Claim 12
Dependent Claim
12 words
A catalyst according to claim 7 wherein the promoter metal is nickel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-11 | 1979-11-10 | 1980-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-11 | 1983-11-10 | 1984-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-11 | 1987-11-10 | 1988-05-11 | $7700.00 | Window Closed / Lapsed |