Manufacture of granular lead compounds
Assignee: Mizusawa Industrial Chemicals Ltd
•
Filing: 1973-02-27
•
Granted: 1976-05-11
•
Expires: 1993-02-27
Abstract
Abstract This invention relates to a process for manufacturing granular lead oxides such as granular lead monoxide (litharge) and granular red lead at high purities from lead suboxide without formation of harmful dusts or fumes. Furthermore, the invention concerns novel lead bearing additives for use in ceramic industry, for instance, for formation of lead glasses and ceramic glazes to be employed for the manufacture of various optical glasses, cut glasses, tube lamp glasses, etc., and a process for the manufacture of such lead bearing additives.
Inventors
- 👤 Yujiro Sugahara
- 👤 Yoshibumi Noshi
- 👤 Hiroyuki Naito
- 👤 Katsuya Toki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:07
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/02; C03C1/028; C01; C01G; C01G21/00; C01G21/02; C01G21/06; C03C1/026; C01P; C01P2002/00; C01P2002/50; C01P2002/70; C01P2002/72; C01P2004/00; C01P2004/60; C01P2006/00; C01P2006/10; C01P2006/60; C01P2006/66; C01P2006/80
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
231 words
A solid lead-bearing additive for use in the ceramic industry which consists essentially of brickettes obtained by calcining the granular mixture of a lead oxide and silicon dioxide, wherein the weight ratio of the lead oxide calculated as PbO and silicon dioxide calculated as SiO 2 is within the following range: PbO : SiO.sub.2 = 93 : 7 ˜ 30 : 70, said brickettes having the particle size of from 0.1 to 10 mm, said brickettes having an apparent density expressed by the following formula: D = Kd ( Xd.sub.x + Yd.sub.y ) wherein D is an apparent density in g/cc of the brickettes, d x represents a true density of the lead oxide component, X represents the weight ratio of the lead oxide component contained in the brickettes, d y represents a true density of silicon dioxide, Y represents the weight ratio of silicon dioxide contained in the brickettes, and Kd is a number from 0.2 to 0.85 and having a nitric acid reactivity (RN) of 10 to 96.5%, where RN is defined by the formula ##EQU4## wherein X O is the weight in grams of the lead oxide contained in 5 g of the brickettes, and X 1 is the weight in grams of the lead oxide which is dissolved when 5 g of the brickettes are agitated for 20 minutes in 50 ml. of 1.34 N nitric acid.
Claim 2
Dependent Claim
231 words
A solid lead-bearing additive for use in the ceramic industry which consists essentially of brickettes obtained by calcining the granular mixture of a lead oxide and silicon dioxide, wherein the weight ratio of the lead oxide calculated as PbO and silicon dioxide calculated as SiO 2 is within the following range: PbO : SiO.sub.2 = 93 : 7 ˜ 30 : 70, said brickettes having the particle size of from 0.1 to 10 mm, said brickettes having an apparent density expressed by the following formula: D = Kd ( Xd.sub.x + Yd.sub.y ) wherein D is an apparent density in g/cc of the brickettes, d x represents a true density of the lead oxide component, X represents the weight ratio of the lead oxide component contained in the brickettes, d y represents a true density of silicon dioxide, Y represents the weight ratio of silicon dioxide contained in the brickettes, and Kd is a number from 0.2 to 0.85 and having a nitric acid reactivity (RN) of 10 to 96.5%, where RN is defined by the formula ##EQU4## wherein X O is the weight in grams of the lead oxide contained in 5 g of the brickettes, and X 1 is the weight in grams of the lead oxide which is dissolved when 5 g of the brickettes are agitated for 20 minutes in 50 ml. of 1.34 N nitric acid.
Claim 3
Dependent Claim
37 words
The solid lead-bearing additive of claim 1 wherein said brickettes contain at last 0.01% by weight, based on the total weight of the brickettes, of boric compound selected from the group consisting of borax and boric acid.
Claim 4
Dependent Claim
39 words
The solid lead-bearing additive of claim 1 wherein said brickettes contain at least 0.01% by weight, based on the total weight of the brickettes, of aluminum compound selected from the group consisting of aluminum oxide and hydroxide and aluminates.
Claim 5
Dependent Claim
49 words
The solid lead-bearing additive of claim 1 wherein said brickettes contain at least 0.01% by weight, based on the total weight of the brickettes, of alkaline earth metal compound selected from the group consisting of the alkali and alkaline earth metal oxides, hydroxides, carbonates, nitrates and sulfates and halides.
Claim 6
Dependent Claim
34 words
The solid lead-bearing additive of claim 1 wherein said brickettes contain at least 0.01% by weight, based on the total weight of the brickettes, of a coloring agent and said halide of alkali metal.
Claim 7
Dependent Claim
206 words
A process for the manufacture of lead-bearing additives for use in ceramic industry which comprises intimately mixing lead suboxide having a composition expressed by the following formula: PbO.sub.x wherein x is a number from 0.4 to 0.9, with silicon dioxide or a silicate so that the mixing weight ratio of the lead suboxide calculated as PbO and the silicon dioxide or silicate calculated as SiO 2 is within the following range: PbO : SiO.sub.2 = from 93 : 7 to 30 : 70, molding the resulting mixture into granules having a particle size of from 0.1 to 10 mm and having an apparent density expressed by the following formula: D = K(Xd.sub.x + Yd.sub.y) wherein D is an apparent density in g/cc of the granulated product, d x represents a true density of lead suboxide, X stands for the weight ratio of lead suboxide in the granulated product, d y represents a true density of silicon dioxide or silicate, Y represents the weight ratio of said silicon dioxide or silicate in the granulated product, and K is a number from 0.2 to 0.85, and heating the granules at a temperature of 350° to 700°C. in an oxygen-containing atmosphere so as to form the granules into brickettes.
Claim 8
Dependent Claim
206 words
A process for the manufacture of lead-bearing additives for use in ceramic industry which comprises intimately mixing lead suboxide having a composition expressed by the following formula: PbO.sub.x wherein x is a number from 0.4 to 0.9, with silicon dioxide or a silicate so that the mixing weight ratio of the lead suboxide calculated as PbO and the silicon dioxide or silicate calculated as SiO 2 is within the following range: PbO : SiO.sub.2 = from 93 : 7 to 30 : 70, molding the resulting mixture into granules having a particle size of from 0.1 to 10 mm and having an apparent density expressed by the following formula: D = K(Xd.sub.x + Yd.sub.y) wherein D is an apparent density in g/cc of the granulated product, d x represents a true density of lead suboxide, X stands for the weight ratio of lead suboxide in the granulated product, d y represents a true density of silicon dioxide or silicate, Y represents the weight ratio of said silicon dioxide or silicate in the granulated product, and K is a number from 0.2 to 0.85, and heating the granules at a temperature of 350° to 700°C. in an oxygen-containing atmosphere so as to form the granules into brickettes.
Claim 9
Dependent Claim
26 words
A process according to claim 6 wherein the powdery lead suboxide and the silicon dioxide or silicate are mixed in the presence of an aqueous medium.
Claim 10
Dependent Claim
204 words
A process for the manufacture of lead-bearing additives for use in the ceramic industry which comprises intimately mixing (a) a powder of a lead oxide selected from the group consisting of litharge and red lead with (b) a siliciferous component selected from the group consisting of silicon dioxide and silicates so that the mixing weight ratio of the lead oxide calculated as PbO and the siliciferous component calculated as SiO 2 is within the following range: PbO : SiO.sub.2 = from 93 : 7 to 30 : 70, molding the resulting mixture into granules having a particle size from 0.1 to 10 mm and having an apparent density expressed by the following formula: D = K(Xd.sub.x + Yd.sub.y) wherein D is an apparent density in g/cc of the granulated product, d x represents the true density of the lead oxide, X represents the weight ratio of the lead oxide in the granular product, d y represents a true density of the siliciferous component, Y represents the weight ratio of the siliciferous component in the granulated product, and K is a number from 0.2 to 0.85, and heat-treating the granules at a temperature of at least 200°C. so as to form the granules into brickettes.
Claim 11
Dependent Claim
204 words
A process for the manufacture of lead-bearing additives for use in the ceramic industry which comprises intimately mixing (a) a powder of a lead oxide selected from the group consisting of litharge and red lead with (b) a siliciferous component selected from the group consisting of silicon dioxide and silicates so that the mixing weight ratio of the lead oxide calculated as PbO and the siliciferous component calculated as SiO 2 is within the following range: PbO : SiO.sub.2 = from 93 : 7 to 30 : 70, molding the resulting mixture into granules having a particle size from 0.1 to 10 mm and having an apparent density expressed by the following formula: D = K(Xd.sub.x + Yd.sub.y) wherein D is an apparent density in g/cc of the granulated product, d x represents the true density of the lead oxide, X represents the weight ratio of the lead oxide in the granular product, d y represents a true density of the siliciferous component, Y represents the weight ratio of the siliciferous component in the granulated product, and K is a number from 0.2 to 0.85, and heat-treating the granules at a temperature of at least 200°C. so as to form the granules into brickettes.
Claim 12
Dependent Claim
22 words
A process according to claim 8 wherein the lead oxide and siliciferous component are mixed in the presence of an aqueous medium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-11 | 1979-11-10 | 1980-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-11 | 1983-11-10 | 1984-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-11 | 1987-11-10 | 1988-05-11 | $7700.00 | Window Closed / Lapsed |