Method of and apparatus for producing metal fibers in a magnetic field
Assignee: Kloeckner Werke AG
•
Filing: 1975-04-14
•
Granted: 1976-05-11
•
Expires: 1995-04-14
Abstract
Abstract A magnetic field is generated whose flux lines extend normal to a planar supporting surface which is located in an enclosed annular space. Carbonyls of metallic material are fed into the enclosed space so that they travel lengthwise of the flux lines and normal to the plane of the supporting surface. The space is then heated to a decomposition temperature at which the carbonyls undergo thermal decomposition and liberate metal atoms which agglomerate under the influence of the flux lines on the supporting surface and form on the latter metal fibers which project from the supporting surface in a direction normal thereto, i.e., opposite to the direction of travel of the carbonyls themselves.
Inventors
- 👤 Walter Dawihl
- 👤 Walter Eicke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:36
CPC Classifications
C; C30; C30B; C30B25/00; C30B25/005; B; B22; B22F; B22F1/00; B22F1/06; B22F1/062; B22F9/00; B22F9/16; B22F9/30
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
100 words
A method of producing metal fibers in a magnetic field, comprising the steps of generating magnetic flux lines which extend normal to a planar supporting surface located in an enclosed space; feeding carbonyls of metallic materials into said enclosed space for travel lengthwise of said flux lines and normal to said supporting surface; and heating said space to a decomposition temperature at which the carbonyls undergo thermal decomposition and liberate metal atoms which agglomerate under the influence of said flux lines on said supporting surface and form thereon metal fibers which project from the supporting surface in direction normal thereto.
Claim 2
Independent Claim
100 words
A method of producing metal fibers in a magnetic field, comprising the steps of generating magnetic flux lines which extend normal to a planar supporting surface located in an enclosed space; feeding carbonyls of metallic materials into said enclosed space for travel lengthwise of said flux lines and normal to said supporting surface; and heating said space to a decomposition temperature at which the carbonyls undergo thermal decomposition and liberate metal atoms which agglomerate under the influence of said flux lines on said supporting surface and form thereon metal fibers which project from the supporting surface in direction normal thereto.
Claim 3
Dependent Claim
25 words
A method as defined in claim 1, said space being annular, and wherein said flux lines extend parallel to a longitudinal axis of the space.
Claim 4
Dependent Claim
36 words
A method as defined in claim 2, said space being bounded by inner and outer circumferential walls; and wherein the step of heating comprises supplying a heating medium to said space through the inner wall thereof.
Claim 5
Dependent Claim
25 words
A method as defined in claim 2, wherein the step of heating comprises establishing in said space a temperature gradient transversely of said longitudinal axis.
Claim 6
Dependent Claim
45 words
A method as defined in claim 4, wherein said space is bounded by inner and outer circumferential walls; and wherein the step of heating comprises establishing the said space a temperature gradient transversely of said longitudinal axis and from said inner to said outer wall.
Claim 7
Dependent Claim
29 words
A method as defined in claim 5, wherein the step of establishing said temperature gradient comprises heating said inner wall to a temperature substantially higher than said decomposition temperature.
Claim 8
Dependent Claim
34 words
A method as defined in claim 5, the carbonyls being iron carbonyls; and wherein the step of establishing said temperature gradient comprises heating said inner wall to a temperature on the order of 500°C.
Claim 9
Dependent Claim
48 words
A method as defined in claim 1, said space being annular and bounded by inner and outer circumferential walls to which said flux lines extend in axial parallelism; and wherein the step of heating comprises heating said outer wall to a temperature substantially lower than said decomposition temperature.
Claim 10
Dependent Claim
32 words
A method as defined in claim 8, wherein the corbonyls are iron carbonyls; and wherein the step of heating comprises heating said outer wall to a temperature on the order of 120°C.
Claim 11
Dependent Claim
27 words
A method as defined in claim 1; and further comprising the step of moving said supporting surface in said space in longitudinal direction of said flux lines.
Claim 12
Dependent Claim
40 words
A method as defined in claim 1; and further comprising the step of moving said supporting surface in said space in longitudinal direction of said flux lines and in dependence upon the rate of longitudinal growth of said metal fibers.
Claim 13
Dependent Claim
28 words
A method as defined in claim 1; further comprising the step of vaporizing the carbonyls outside said space preliminary to feeding of the resulting vapors into said space.
Claim 14
Dependent Claim
32 words
A method as defined in claim 12, wherein said space is annular, and wherein the step of feeding comprises admitting the vapors into said annular space from the radially outer side thereof.
Claim 15
Dependent Claim
27 words
A method as defined in claim 12, wherein said space is annular, and wherein the step of feeding comprises admitting said vapors tangentially into said annular chamber.
Claim 16
Dependent Claim
24 words
A method as defined in claim 12, wherein the step of vaporizing comprises carrying out the vaporization in a plurality of separate vaporizing devices.
Claim 17
Dependent Claim
26 words
A method as defined in claim 15, wherein the step of vaporizing comprises vaporizing in each of said devices a carbonyl of a different metallic material.
Claim 18
Dependent Claim
34 words
A method as defined in claim 16, wherein the step of feeding comprises admitting the vapors from at least two of said devices simultaneously into said space, so as to obtain alloyed metal fibers.
Claim 19
Dependent Claim
60 words
A method as defined in claim 1; and further comprising the steps of admitting, upon formation of said fibers on said supporting surface, additional carbonyls of metallic material different from said fibers, and effecting the thermal decomposition of said additional carbonyls, so as to coat the originally formed fibers with the metal liberated by thermal decomposition of said additional carbonyls.
Claim 20
Dependent Claim
127 words
Apparatus for producing metal fibers in a magnetic field, comprising a reaction chamber; magnetic means for producing in said reaction chamber magnetic flux lines extending in a predetermined direction; feeding means for feeding into said reaction chamber vaporized metal carbonyls for travel in said chamber along said flux lines in said direction; heating means for heating the interior of said chamber to a temperature at which said carbonyls undergo thermal decomposition and liberate metal atoms; and intercepting means in said chamber for said metal atoms and having a supporting surface extending normal to said direction and on which said metal atoms agglomerate under the influence of said flux lines and form metal fibers which project from said supporting surface normal thereto and opposite to said predetermined direction.
Claim 21
Dependent Claim
127 words
Apparatus for producing metal fibers in a magnetic field, comprising a reaction chamber; magnetic means for producing in said reaction chamber magnetic flux lines extending in a predetermined direction; feeding means for feeding into said reaction chamber vaporized metal carbonyls for travel in said chamber along said flux lines in said direction; heating means for heating the interior of said chamber to a temperature at which said carbonyls undergo thermal decomposition and liberate metal atoms; and intercepting means in said chamber for said metal atoms and having a supporting surface extending normal to said direction and on which said metal atoms agglomerate under the influence of said flux lines and form metal fibers which project from said supporting surface normal thereto and opposite to said predetermined direction.
Claim 22
Dependent Claim
24 words
Apparatus as defined in claim 19, wherein said intercepting means is composed, at least at said supporting surface thereof, of a magnetically inactive material.
Claim 23
Dependent Claim
18 words
Apparatus as defined in claim 19, wherein said intercepting means is a wire mesh of magnetically inactive material.
Claim 24
Dependent Claim
68 words
Apparatus as defined in claim 19, wherein said reaction chamber is annular and bounded by tubular inner and outer circumferential walls; said inner wall being in part perforate, and said heating means comprising a heater device located within the confines of said inner tubular wall and from which heated gas issues into said confines to heat said inner wall and thereupon enters into said chamber through the perforations.
Claim 25
Dependent Claim
29 words
Apparatus as defined in claim 19; further comprising at least one vaporizer for vaporizing the carbonyl, said one vaporizer being outside said chamber and connected with said feeding means.
Claim 26
Dependent Claim
33 words
Apparatus as defined in claim 19; further comprising a plurality of vaporizers for vaporizing the carbonyl, said vaporizers being arranged in an annulus about said reaction chamber and connected with said feeding means.
Claim 27
Dependent Claim
36 words
Apparatus as defined in claim 19; further comprising a plurality of vaporizers, each for vaporizing the carbonyl of a different metallic material, said vaporizers being arranged about said reaction chamber and connected with said feeding means.
Claim 28
Dependent Claim
44 words
Apparatus as defined in claim 19, said reaction chamber being annular; and further comprising a plurality of vaporizers for metallic carbonyls arranged about said reaction chamber offset relative to one another in axial direction of the chamber and being connected with said feeding means.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-11 | 1979-11-10 | 1980-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-11 | 1983-11-10 | 1984-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-11 | 1987-11-10 | 1988-05-11 | $7700.00 | Window Closed / Lapsed |