Method of manufacturing a transparent light conducting element of synthetic resin having refractive index gradient
Assignee: Nippon Selfoc Co Ltd
•
Filing: 1973-10-18
•
Granted: 1976-05-04
•
Expires: 1993-10-18
Abstract
Abstract A method of manufacturing a light conducting element of synthetic resin in which a continuous change takes place in refractive index from the surface of the element toward its interior, which comprises bringing a transparent solid article of a network polymer which is in the incompletely polymerized state and contains 2 to 80% of a solvent-soluble component, into contact at its surface with a monomer capable of forming a polymer having a different refractive index from the network polymer thereby to cause the diffusion and migration of the monomer into the interior of the article through the contact surface, thereby setting up a gradient in the concentration of the monomer component in the interior of the above article which gradually decreases from the contact surface toward the interior, and simultaneously with, or after, this diffusion step, polymerizing the monomer in the interior of the article and completing the polymerization of the network polymer of the article. The article may be in the form of a fiber, rod, sheet or hollow cylinder.
Inventors
- 👤 Yasuji Ohtsuka
- 👤 Motoaki Yoshida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:50
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/02; G02B6/02033; G02B6/02038; C; C08; C08F; C08F291/00; C08J; C08J7/00; C08J7/12; C08J7/16; G02B1/00; G02B1/04; G02B1/045; B; B29; B29C; B29C48/00; B29C48/03; B29C48/05; B29C48/06; B29C48/07; B29C48/08; B29C48/09; Y; Y10; Y10S; Y10S525/00; Y10S525/932
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
289 words
A method of manufacturing a transparent light conducting element of synthetic resin in which a continuous change takes place in the refractive index progressively from the surface of the element to its interior, said method comprising, in combination, the steps of 1. submitting a monomer A to a prepolymerization reaction, said monomer A being one that can form a transparent network polymer by the polymerization reaction, and before completion of the polymerization reaction and at a stage wherein 2 - 80% by weight of a solvent-soluble component is contained, interrupting the polymerization reaction to form a prepolymer; 2. imparting a desired form to the prepolymer to obtain an article thereof having a uniform refractive index; 3. contacting for a predetermined time said prepolymeric article on at least a part of the surface thereof with a monomer B, said monomer B being one which forms a transparent completely polymerized polymer having a refractive index different from that of the completely polymerized polymer formed from said monomer A, said predetermined time being selected such that a gradient in the concentration of the monomer B diffused within said article is set up, said concentration gradient being one which gradually decreases from the contact surface to the interior of the article, wherein when a part or all of the diffused monomer has been polymerized, the amount of the monomer B corresponding to that which has been polymerized being included in calculating the concentration; and 4. carrying out a postpolymerization step consisting of polymerizing the monomer B present in the article and completing the polymerization of the prepolymer, whereby said gradient in the concentration of the monomer B forms said continuous change of the refractive index without causing objectionable turbidity, concurrently with step (3).
Claim 2
Independent Claim
289 words
A method of manufacturing a transparent light conducting element of synthetic resin in which a continuous change takes place in the refractive index progressively from the surface of the element to its interior, said method comprising, in combination, the steps of 1. submitting a monomer A to a prepolymerization reaction, said monomer A being one that can form a transparent network polymer by the polymerization reaction, and before completion of the polymerization reaction and at a stage wherein 2 - 80% by weight of a solvent-soluble component is contained, interrupting the polymerization reaction to form a prepolymer; 2. imparting a desired form to the prepolymer to obtain an article thereof having a uniform refractive index; 3. contacting for a predetermined time said prepolymeric article on at least a part of the surface thereof with a monomer B, said monomer B being one which forms a transparent completely polymerized polymer having a refractive index different from that of the completely polymerized polymer formed from said monomer A, said predetermined time being selected such that a gradient in the concentration of the monomer B diffused within said article is set up, said concentration gradient being one which gradually decreases from the contact surface to the interior of the article, wherein when a part or all of the diffused monomer has been polymerized, the amount of the monomer B corresponding to that which has been polymerized being included in calculating the concentration; and 4. carrying out a postpolymerization step consisting of polymerizing the monomer B present in the article and completing the polymerization of the prepolymer, whereby said gradient in the concentration of the monomer B forms said continuous change of the refractive index without causing objectionable turbidity, concurrently with step (3).
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein said monomer A is at least one monomer selected from the group consisting of diallyl phthalate, unsaturated acid allyl esters, and divinyl esters.
Claim 4
Dependent Claim
21 words
The method of claim 1 wherein said solvent-soluble component is contained in an amount of 30 - 70 % by weight.
Claim 5
Dependent Claim
17 words
The method of claim 1 wherein said desired form is a fiber, rod, sheet or hollow cylinder.
Claim 6
Dependent Claim
32 words
The method of claim 1 wherein the difference in the refractive indices of the finished polymer of said monomer A and the finished polymer of said monomer B is at least 0.005.
Claim 7
Dependent Claim
32 words
The method of claim 1 wherein said monomer B is at least one monomer selected from the group consisting of styrene, methacrylic esters, acrylic esters, vinyl acetate, vinyl chloride, acrylonitrile and butadiene.
Claim 8
Dependent Claim
110 words
The method of claim 1, wherein said desired form is that of a fiber or a rod, and which comprises contacting said monomer B with the whole of the outer peripheral surface of said fibrous or rodlike prepolymeric article, the time of contact being so chosen that the migration of the monomer B takes place towards the center of the article, whereby the finally obtained synthetic resin light conducting element has a lens action and a refractive index distribution which varies from the center of the element to the peripheral surface thereof at a rate nearly proportional to the square of the distance in a radial direction from the center.
Claim 9
Dependent Claim
90 words
The method of claim 1, wherein said network polymer of the monomer A and the monomer B are selected from the combinations of diallyl phthalate polymer-methyl methacrylate, diallyl phthalate polymer-mixture of methyl acrylate and methyl methacrylate, diallyl isophthalate polymer-methyl methacrylate, copolymer of diallyl phthalate and styrene-methacrylic ester, copolymer of diallyl isophthalate and styrene-acrylic ester, copolymer of divinyl phthalate and vinyl benzoate-methacrylic ester, copolymer of divinyl isophthalate and vinyl benzoate-methacrylic ester, copolymer of vinyl benzoate and diallyl isophthalate-methacrylic ester, diethylene glycol bisallyl carbonate polymer-styrene and diethylene glycol bisallyl carbonate polymer-diallyl isophthalate.
Claim 10
Independent Claim
287 words
A method of manufacturing a transparent light conducting element of synthetic resin in which a continuous change takes place in the refractive index progressively from the surface of the element to its interior, said method comprising, in combination, the steps of: 1. submitting a monomer A to a prepolymerization reaction, said monomer A being one that can form a transparent network polymer by the polymerization reaction, and before completion of the polymerization reaction and at a stage wherein 2-80% by weight of a solvent-soluble component is contained, interrupting the polymerization reaction to form a prepolymer; 2. imparting a desired form to the prepolymer to obtain an article thereof having a uniform refractive index; 3. contacting for a predetermined time said prepolymeric article on at least a part of the surface thereof with a monomer B, said monomer B being one which forms a transparent completely polymerized polymer having a refractive index different from that of the completely polymerized polymer formed from said monomer A, said predetermined time being selected such that a gradient in the concentration of the monomer B diffused within said article is set up, said concentration gradient being one which gradually decreases from the contact surface to the interior of the article, wherein when a part or all of the diffused monomer has been polymerized, the amount of the monomer B corresponding to that which has been polymerized being included in calculating the concentration; and 4. carrying out a postpolymerization step consisting of polymerizing the monomer B present in the article and completing the polymerization of the prepolymer, whereby said gradient in the concentration of the monomer B forms said continuous change of the refractive index without causing objectionable turbidity, subsequent to step (3).
Claim 11
Independent Claim
287 words
A method of manufacturing a transparent light conducting element of synthetic resin in which a continuous change takes place in the refractive index progressively from the surface of the element to its interior, said method comprising, in combination, the steps of: 1. submitting a monomer A to a prepolymerization reaction, said monomer A being one that can form a transparent network polymer by the polymerization reaction, and before completion of the polymerization reaction and at a stage wherein 2-80% by weight of a solvent-soluble component is contained, interrupting the polymerization reaction to form a prepolymer; 2. imparting a desired form to the prepolymer to obtain an article thereof having a uniform refractive index; 3. contacting for a predetermined time said prepolymeric article on at least a part of the surface thereof with a monomer B, said monomer B being one which forms a transparent completely polymerized polymer having a refractive index different from that of the completely polymerized polymer formed from said monomer A, said predetermined time being selected such that a gradient in the concentration of the monomer B diffused within said article is set up, said concentration gradient being one which gradually decreases from the contact surface to the interior of the article, wherein when a part or all of the diffused monomer has been polymerized, the amount of the monomer B corresponding to that which has been polymerized being included in calculating the concentration; and 4. carrying out a postpolymerization step consisting of polymerizing the monomer B present in the article and completing the polymerization of the prepolymer, whereby said gradient in the concentration of the monomer B forms said continuous change of the refractive index without causing objectionable turbidity, subsequent to step (3).
Claim 12
Dependent Claim
29 words
The method of claim 9 wherein said monomer A is at least one monomer selected from the group consisting of diallyl phthalate, unsaturated acid allyl esters, and divinyl esters.
Claim 13
Dependent Claim
18 words
The method of claim 9 wherein said solvent-soluble component is contained in an amount of 30-70% by weight.
Claim 14
Dependent Claim
17 words
The method of claim 9 wherein said desired form is a fiber, rod, sheet or hollow cylinder.
Claim 15
Dependent Claim
32 words
The method of claim 9 wherein the difference in the refractive indices of the finished polymer of said monomer A and the finished polymer of said monomer B is at least 0.005.
Claim 16
Dependent Claim
32 words
The method of claim 9 wherein said monomer B is at least one monomer selected from the group consisting of styrene, methacrylic esters, acrylic esters, vinyl acetate, vinyl chloride, acrylonitrile and butadiene.
Claim 17
Dependent Claim
110 words
The method of claim 9 wherein said desired form is that of a fiber or a rod, and which comprises contacting said monomer B with the whole of the outer peripheral surface of said fibrous or rodlike prepolymeric article, the time of contact being so chosen that the migration of the monomer B takes place towards the center of the article, whereby the finally obtained synthetic resin light conducting element has a lens action and a refractive index distribution which varies from the center of the element to the peripheral surface thereof at a rate nearly proportional to the square of the distance in a radial direction from the center.
Claim 18
Dependent Claim
90 words
The method of claim 9 wherein said network polymer of the monomer A and the monomer B are selected from the combinations of diallyl phthalate polymer-methyl methacrylate, diallyl phthalate polymer-mixture of methyl acrylate and methyl methacrylate, diallyl isophthalate polymer-methyl methacrylate, copolymer of diallyl phthalate and styrene-methacrylic ester, copolymer of diallyl isophthalate and styrene-acrylic ester, copolymer of divinyl phthalate and vinyl benzoate-methacrylic ester, copolymer of divinyl isophthalate and vinyl benzoate-methacrylic ester, copolymer of vinyl benzoate and diallyl isophthalate-methacrylic ester, diethylene glycol bisallyl carbonate polymer-styrene and diethylene glycol bisallyl carbonate polymer-diallyl isophthalate.
References Cited (Backward Citations)
US2332461A
Cited
US2331716A
Cited
US2912418A
Cited
US3083118A
Cited
US3485556A
Cited
US3801181A
Cited
US3658407A
Cited
US3819782A
Cited
US3816160A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-04 | 1979-11-03 | 1980-05-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-04 | 1983-11-03 | 1984-05-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-04 | 1987-11-03 | 1988-05-04 | $7700.00 | Window Closed / Lapsed |