Seamed article
Assignee: Individual
•
Filing: 1974-07-09
•
Granted: 1976-04-13
•
Expires: 1994-07-09
Abstract
Abstract Metal cans are welded by frictional treatment of the materials joined. The treatment is provided by a rapidly rotating smooth hard friction tool e.g. wheel contacting a surface of the metal above the join while the parts joined are held in pressure contact by independent pressure exerting means and/or by the wheel itself. In the formation of can side-seams the wheel and the can are relatively traversed and a longitudinal continuous side-seam is formed which in the case of the metal to metal joints is metallurgically homogeneous and may be characterized in that no signs of melting of the base metal are visible at the welded interfaces.
Inventors
- 👤 Penelope Jane Vesey Luc
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:21
CPC Classifications
B; B65; B65D; B65D7/00; B65D7/42; B21; B21D; B21D51/00; B21D51/16; B21D51/26; B21D51/2676; B23; B23K; B23K20/00; B23K20/12; B23K20/122; B23K20/1245; B23K20/1255; B23K20/126; B23K20/1265; B23K2101/00; B23K2101/04; B23K2101/06
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
224 words
A seamed article formed from metal sheet material and having at least one seam disposed along an interface between intimately contacting facing surfaces of juxtaposed portions of metal sheet each having an original grain structure, the seam joining the portions of metal sheet at the interface being a metallurgically homogeneous continuous line weld between the metal portions produced by energy supplied by dynamic rubbing friction applied by an external and independent tool in contact with a surface of at least one of the juxtaposed portions of metal sheet opposite to and adjacent the facing surfaces of the interface thereof while the facing surfaces of the metal portions at the interface are substantially stationary relative to one another, the line weld between the portions having: i. substantially uniform metallurgical grain characteristics at all points along the weld; ii. reorientation of the crystallization of the metal of the facing surfaces of the portions at the interface; iii. an absence at the interface of macroscopic disorientation of the metal grain structure of the type which would be caused by the melting of portions of the metal at the interface; and iv. through the thickness of the portions of the metal sheet extending from the line weld, the substantial preservation of the original metal grain structure of the portions of metal extending from the interface of the portions.
Claim 2
Dependent Claim
224 words
A seamed article formed from metal sheet material and having at least one seam disposed along an interface between intimately contacting facing surfaces of juxtaposed portions of metal sheet each having an original grain structure, the seam joining the portions of metal sheet at the interface being a metallurgically homogeneous continuous line weld between the metal portions produced by energy supplied by dynamic rubbing friction applied by an external and independent tool in contact with a surface of at least one of the juxtaposed portions of metal sheet opposite to and adjacent the facing surfaces of the interface thereof while the facing surfaces of the metal portions at the interface are substantially stationary relative to one another, the line weld between the portions having: i. substantially uniform metallurgical grain characteristics at all points along the weld; ii. reorientation of the crystallization of the metal of the facing surfaces of the portions at the interface; iii. an absence at the interface of macroscopic disorientation of the metal grain structure of the type which would be caused by the melting of portions of the metal at the interface; and iv. through the thickness of the portions of the metal sheet extending from the line weld, the substantial preservation of the original metal grain structure of the portions of metal extending from the interface of the portions.
Claim 3
Dependent Claim
22 words
A seamed article according to claim 1 wherein the portions of metal sheet seamed are tin-plated steel and the line-weld is steel-to-steel.
Claim 4
Dependent Claim
22 words
A seamed article according to claim 1 wherein the portions of metal sheet seamed are tin-plated steel and the line-weld is tin-to-tin.
Claim 5
Dependent Claim
41 words
A seamed article according to claim 1 wherein the portions of metal sheet seamed are tin-free steel coated with one of chrome and chrome oxide, the one of chrome and chrome oxide coating not having been removed prior to the seaming.
Claim 6
Dependent Claim
17 words
A seamed article according to claim 1 wherein the portions of metal sheet seamed are aluminum portions.
Claim 7
Dependent Claim
18 words
A seamed article according to claim 1 wherein the seam is a side seam of a tubular container.
Claim 8
Dependent Claim
264 words
A seamed article formed from cold rolled metal sheet material having a flattened grain structure at a surface and an original grain structure extending through the thickness thereof, the container having at least one seam disposed along an interface between intimately contacting facing surfaces of juxtaposed portions of the metal sheet material, the seam joining the portions of metal sheet at the interface being a metallurgically homogeneous continuous line weld between the metal portions produced by energy supplied by dynamic rubbing friction applied by an external and independent tool in contact with a surface of at least one of the juxtaposed portions of metal sheet opposite to and adjacent the facing surfaces of the interface thereof while the facing surfaces of the metal portions at the interface are substantially stationary relative to one another, the line weld between the portions having: i. substantially uniform metallurgical grain characteristics at all points along the weld; ii. metallurgical grain growth across the interface of the juxtaposed portions of metal sheet; iii. reorientation of the crystallization of the grain structure at the interface, including the formation of an equi-axial grain structure at the interface between the juxtaposed portions; iv. an absence at the interface of macroscopic disorientation of the metal grain structure of the type which would be caused by the melting of portions of the metal at the interface; and v. through the thickness of the portions of the metal sheet extending from the line weld, the substantial preservation of the original metal grain structure of the portions of metal extending from the interface of the portions.
Claim 9
Dependent Claim
264 words
A seamed article formed from cold rolled metal sheet material having a flattened grain structure at a surface and an original grain structure extending through the thickness thereof, the container having at least one seam disposed along an interface between intimately contacting facing surfaces of juxtaposed portions of the metal sheet material, the seam joining the portions of metal sheet at the interface being a metallurgically homogeneous continuous line weld between the metal portions produced by energy supplied by dynamic rubbing friction applied by an external and independent tool in contact with a surface of at least one of the juxtaposed portions of metal sheet opposite to and adjacent the facing surfaces of the interface thereof while the facing surfaces of the metal portions at the interface are substantially stationary relative to one another, the line weld between the portions having: i. substantially uniform metallurgical grain characteristics at all points along the weld; ii. metallurgical grain growth across the interface of the juxtaposed portions of metal sheet; iii. reorientation of the crystallization of the grain structure at the interface, including the formation of an equi-axial grain structure at the interface between the juxtaposed portions; iv. an absence at the interface of macroscopic disorientation of the metal grain structure of the type which would be caused by the melting of portions of the metal at the interface; and v. through the thickness of the portions of the metal sheet extending from the line weld, the substantial preservation of the original metal grain structure of the portions of metal extending from the interface of the portions.
Claim 10
Dependent Claim
227 words
A seamed article formed from metal sheet material and having at least one seam disposed along an interface between intimately contacting facing surfaces of juxtaposed portions of metal sheet each having an original grain structure, the seam joining the portions of metal sheet at the interface being a metallurgically homogeneous continuous line weld between the metal portions produced by energy supplied by dynamic rubbing friction applied by an external and independent tool in contact with a surface of at least one of the juxtaposed portions of metal sheet opposite to and adjacent the facing surfaces of the interface thereof while the facing surfaces of the metal portions at the interface are substantially stationary relative to one another, the line weld between the portions having: i. substantially uniform metallurgical grain characteristics at all points along the weld; ii. the conservation of the original grain structure of the metal at the facing surfaces of the portions at the interface; iii. an absence at the interface of macroscopic disorientation of the metal grain structure of the type which would be caused by the melting of portions of the metal at the interface; and iv. through the thickness of the portions of the metal sheet extending from the line weld, the substantial preservation of the original metal grain structure of the portions of metal extending from the interface of the portions.
Claim 11
Dependent Claim
227 words
A seamed article formed from metal sheet material and having at least one seam disposed along an interface between intimately contacting facing surfaces of juxtaposed portions of metal sheet each having an original grain structure, the seam joining the portions of metal sheet at the interface being a metallurgically homogeneous continuous line weld between the metal portions produced by energy supplied by dynamic rubbing friction applied by an external and independent tool in contact with a surface of at least one of the juxtaposed portions of metal sheet opposite to and adjacent the facing surfaces of the interface thereof while the facing surfaces of the metal portions at the interface are substantially stationary relative to one another, the line weld between the portions having: i. substantially uniform metallurgical grain characteristics at all points along the weld; ii. the conservation of the original grain structure of the metal at the facing surfaces of the portions at the interface; iii. an absence at the interface of macroscopic disorientation of the metal grain structure of the type which would be caused by the melting of portions of the metal at the interface; and iv. through the thickness of the portions of the metal sheet extending from the line weld, the substantial preservation of the original metal grain structure of the portions of metal extending from the interface of the portions.
References Cited (Backward Citations)
US1601927A
Cited
US2013517A
Cited
US2092093A
Cited
US2205251A
Cited
US3358113A
Cited
US3435510A
Cited
US3591756A
Cited
US3618817A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-13 | 1979-10-13 | 1980-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-13 | 1983-10-13 | 1984-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-13 | 1987-10-13 | 1988-04-13 | $7700.00 | Window Closed / Lapsed |