Blown thermoplastic bottle and method for making same
Assignee: Rexam Beverage Can Co
•
Filing: 1973-08-01
•
Granted: 1976-04-06
•
Expires: 1993-08-01
Abstract
Abstract A thermoplastic bottle having a unique combination of properties. The bottle is characterized by a very high level of molecular orientation, and possesses the properties of high impact strength, low gas permeability and excellent resistance to creep strain under tensile load. A blowing process for fabricating the bottle is also taught which features a means for substantially improving the resistance to creep strain.
Inventors
- 👤 Charles Edmund McChesney
- 👤 Robert J. McHenry
- 👤 James Alan Wachtel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 21:15
CPC Classifications
B; B29; B29C; B29C49/00; B29C49/08; B65; B65D; B65D1/00; B65D1/02; B65D1/0207; B29C2949/00; B29C2949/07; B29C2949/0715; B29C2949/072; B29C2949/076; B29C2949/0768; B29C2949/077; B29C2949/081; B29C2949/0811; B29C2949/082; B29C2949/0829; B29C2949/0861; B29C2949/0872; B29C49/02; B29C49/06
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
161 words
A method for improving the resistance to creep strain in a container made from a thermoplastic polymeric material comprising a polymer containing moieties derived from a conjugated diene monomer and a polymer containing moieties derived from an alpha, beta-olefinically unsaturated mononitrile having the structure ##EQU3## where R is selected from the group consisting of hydrogen, an alkyl group having from 1 to 4 carbon atoms, and a halogen, said method comprising the steps of forming a parison from said thermoplastic polymeric material, temperature conditioning the parison to bring the thermoplastic polymeric material to within the orientation temperature range wherein the polymeric material is in a leathery state, blow molding the temperature conditioned parison in a mold cavity to form the parison into the desired container shape and to stretch the polymeric material to molecularly orient at least the sidewall of the container to an orientation release stress between 500 and 2500 p.s.i., and removing the oriented container from the mold cavity.
Claim 2
Independent Claim
161 words
A method for improving the resistance to creep strain in a container made from a thermoplastic polymeric material comprising a polymer containing moieties derived from a conjugated diene monomer and a polymer containing moieties derived from an alpha, beta-olefinically unsaturated mononitrile having the structure ##EQU3## where R is selected from the group consisting of hydrogen, an alkyl group having from 1 to 4 carbon atoms, and a halogen, said method comprising the steps of forming a parison from said thermoplastic polymeric material, temperature conditioning the parison to bring the thermoplastic polymeric material to within the orientation temperature range wherein the polymeric material is in a leathery state, blow molding the temperature conditioned parison in a mold cavity to form the parison into the desired container shape and to stretch the polymeric material to molecularly orient at least the sidewall of the container to an orientation release stress between 500 and 2500 p.s.i., and removing the oriented container from the mold cavity.
Claim 3
Dependent Claim
162 words
The method of claim 1 wherein the thermoplastic polymeric material is derived from (A) about 60 to 90 parts by weight of an alpha, beta-olefinically unsaturated mononitrile having the structure CH 2 =C(--R 1 )--CN where --R 1 is selected from the group consisting of hydrogen, halogen, and lower alkyl groups, (B) about 40 to 10 parts by weight of an ester of an olefinically unsaturated carboxylic acid having the structure CH 2 =C(--R 1 )--C(O)O--R 2 where --R.sub. 1 is as defined above and --R 2 is an alkyl group having from 1 to 6 carbon atoms, (A) and (B) together comprising 100 parts by weight, polymerized in the presence of (C) about 1 to 20 parts by weight of a nitrile rubber containing about 60 to 80 % by weight of moieties derived from a conjugated diene monomer and about 40 to 20 % by weight of moieties derived from a mononitrile having said CH 2 =C(--R 1 )--CN structure.
Claim 4
Dependent Claim
16 words
The method of claim 2 wherein the orientation release stress is between 500 and 1600 p.s.i.
Claim 5
Dependent Claim
37 words
The method of claim 3 wherein the mononitrile is acrylonitrile or methacrylonitrile, the ester is selected from the group consisting of methyl acrylate, ethyl acrylate and methyl methacrylate, and the conjugated diene monomer is butadiene or isoprene.
Claim 6
Dependent Claim
16 words
The method of claim 4 wherein the orientation release stress is between 800 and 1000 p.s.i.
Claim 7
Dependent Claim
60 words
The method of claim 5 wherein the polymer is derived from 73 to 77 parts by weight acrylonitrile and 27 to 23 parts by weight of methyl acrylate, polymerized in the presence of 8 to 10 additional parts by weight of a nitrile rubber containing about 70 % by weight butadiene moieties and about 30 % by weight acrylonitrile moieties.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-06 | 1979-10-06 | 1980-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-06 | 1983-10-06 | 1984-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-06 | 1987-10-06 | 1988-04-06 | $7700.00 | Window Closed / Lapsed |