Homogeneous styrene/isoolefin copolymers
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1971-02-17
•
Granted: 1976-04-06
•
Expires: 1991-02-17
Abstract
Abstract A process for preparing a homogeneous random polymer of two or more cationically polymerizable monomers having the general formula: R2 ¦ H2C=C-R1 wherein R1 is alkyl, alkenyl, phenyl, aralkyl or alkaryl, R2 is H, alkenyl or alkyl and where R2 is H, R1 must be phenyl or alkylaryl, which comprises continuously reacting said monomers in a mixed solvent system comprising a polar organic solvent and a nonpolar, nonaromatic hydrocarbon solvent, said polymerization being carried out in a well-stirred reactor in the presence of a Friedel-Crafts catalyst. The preferred polymer is a homogeneous random styrene-isobutylene copolymer which is prepared by continuously reacting in solution about 10 to about 90 parts by weight of styrene with about 90 to about 10 parts by weight of isobutylene in a mixed solvent system comprising a polar organic solvent and a nonpolar nonaromatic hydrocarbon solvent.
Inventors
- 👤 Kenneth W. Powers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 20:25
CPC Classifications
C; C08; C08F; C08F210/00; C08F210/04; C08F210/08; C08F210/10; C08F212/00; C08F212/02; C08F212/04; C08F212/06
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
164 words
A process for preparing a substantially homogeneous random terpolymer, wherein said homogeneous random terpolymer has a single glass transition temperature as determined by differential thermal analysis, which comprises continuously terpolymerizing a feed compositon of between about 0.5 and about 30.0 wt. % styrene, between about 0.5 and about 30.0 wt. % of a conjugated multi-olefin monomer, the remainder of the feed composition being an isoolefinic monomer, utilizing a Friedel-Crafts catalyst, in a well stirred reactor, said reaction being carried out in a solvent for the resulting terpolymer, said solvent comprising a mixture of about 20 to about 80 volume % of at least one polar nonaromatic organic solvent and about 80 to about 20 volume % of at least one nonaromatic nonpolar hydrocarbon solvent, based on the solvent mixture; the ratio of polar to nonpolar solvents being so selected that the ratio of the reactivity ratio of styrene to the reactivity ratio of the isoolefin monomer is maintained at about 0.4 to about 3.0.
Claim 2
Dependent Claim
164 words
A process for preparing a substantially homogeneous random terpolymer, wherein said homogeneous random terpolymer has a single glass transition temperature as determined by differential thermal analysis, which comprises continuously terpolymerizing a feed compositon of between about 0.5 and about 30.0 wt. % styrene, between about 0.5 and about 30.0 wt. % of a conjugated multi-olefin monomer, the remainder of the feed composition being an isoolefinic monomer, utilizing a Friedel-Crafts catalyst, in a well stirred reactor, said reaction being carried out in a solvent for the resulting terpolymer, said solvent comprising a mixture of about 20 to about 80 volume % of at least one polar nonaromatic organic solvent and about 80 to about 20 volume % of at least one nonaromatic nonpolar hydrocarbon solvent, based on the solvent mixture; the ratio of polar to nonpolar solvents being so selected that the ratio of the reactivity ratio of styrene to the reactivity ratio of the isoolefin monomer is maintained at about 0.4 to about 3.0.
Claim 3
Dependent Claim
33 words
The process of claim 1 wherein the Friedel-Crafts catalyst is selected from the group consisting of aluminum trichloride, aluminum ethyl dichloride, aluminum tribromide, boron trifluoride, isobutyl aluminum dichloride, titanium tetrachloride and mixtures thereof.
Claim 4
Dependent Claim
11 words
The process of claim 1 wherein the isoolefinic monomer is isobutylene.
Claim 5
Dependent Claim
23 words
The process of claim 3 wherein the catalyst is aluminum trichloride and the monomer to catalyst ratio is about 1000:1 to about 1500:1.
Claim 6
Dependent Claim
25 words
The process of claim 3 wherein the catalyst is aluminum ethyl dichloride and the ratio of monomer to catalyst is about 600:1 to about 1000:1.
Claim 7
Dependent Claim
31 words
The process of claim 1 wherein the polar nonaromatic organic solvent is selected from the group consisting of methyl chloride, ethyl chloride, methylene chloride, carbon disulfide, ethyl bromide and mixtures thereof.
Claim 8
Dependent Claim
27 words
The process of claim 1 wherein the nonaromatic nonpolar hydrocarbon solvent is selected from the group consisting of pentane, hexane, methylcyclopentane, 2- methyl pentane, and 2,3-dimethyl butane.
Claim 9
Dependent Claim
20 words
The process of claim 1 wherein the reaction is carried out at a temperature of about -30° to about -100°C.
Claim 10
Dependent Claim
17 words
The process of claim 8 wherein the reaction is carried out at about -40° to about -97°C.
Claim 11
Dependent Claim
14 words
The process of claim 1 wherein said conjugated multiolefin monomer is isoprene or butadiene.
Claim 12
Dependent Claim
12 words
The process of claim 10 wherein the conjugated multiolefin monomer is isoprene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-06 | 1979-10-06 | 1980-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-06 | 1983-10-06 | 1984-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-06 | 1987-10-06 | 1988-04-06 | $7700.00 | Window Closed / Lapsed |