Titanium-activated lanthanum oxysulfide phosphor and method of preparing same
Assignee: GTE Sylvania Inc
•
Filing: 1974-12-23
•
Granted: 1976-04-06
•
Expires: 1994-12-23
Abstract
Abstract An orange broad-band emitting phosphor is a titanium-activated lanthanum oxysulfide containing up to about 0.05 moles of titanium per mole of lanthanum oxysulfide host. The phosphor is prepared by incorporating titanium oxide in the desired ratio to lanthanum into the mixture at the time the lanthanum is sulfurized in the presence of an alkali metal carbonate, to form lanthanum oxysulfide.
Inventors
- 👤 John L. Ferri
- 👤 James E. Mathers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:17
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7701
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
28 words
A luminescent composition consisting essentially of a lanthanum oxysulfide host and from about 0.001 moles to about 0.05 moles of titanium per mole of host as an activator.
Claim 2
Dependent Claim
28 words
A luminescent composition consisting essentially of a lanthanum oxysulfide host and from about 0.001 moles to about 0.05 moles of titanium per mole of host as an activator.
Claim 3
Dependent Claim
26 words
A composition according to claim 1 wherein said activator is present in amounts of from about 0.005 moles to about 0.015 moles per mole of host.
Claim 4
Dependent Claim
137 words
A process for producing a titanium-activated lanthanum oxysulfide comprising: forming a relatively uniform admixture of a lanthanum source selected from the group consisting of lanthanum oxide and lanthanum carbonate, titanium dioxide, sulfur and an alkali metal carbonate as a flux, said sulfur being greater than 15 weight percent in excess of the stoichiometrical amount required to form lanthanum oxysulfide, said alkali metal carbonate is from about 15 to 25 weight percent of the admixture and the amount of titanium dioxide being from about 0.0001 moles to about 0.05 moles per mole of lanthanum source, b. heating said admixture in a non-oxidizing atmosphere at a temperature of at least 1,200°C for a time sufficient to form lanthanum oxysulfide, c. washing the resulting mixture with sufficient water to remove any water soluble material, and d. drying the washed oxysulfide.
Claim 5
Dependent Claim
137 words
A process for producing a titanium-activated lanthanum oxysulfide comprising: forming a relatively uniform admixture of a lanthanum source selected from the group consisting of lanthanum oxide and lanthanum carbonate, titanium dioxide, sulfur and an alkali metal carbonate as a flux, said sulfur being greater than 15 weight percent in excess of the stoichiometrical amount required to form lanthanum oxysulfide, said alkali metal carbonate is from about 15 to 25 weight percent of the admixture and the amount of titanium dioxide being from about 0.0001 moles to about 0.05 moles per mole of lanthanum source, b. heating said admixture in a non-oxidizing atmosphere at a temperature of at least 1,200°C for a time sufficient to form lanthanum oxysulfide, c. washing the resulting mixture with sufficient water to remove any water soluble material, and d. drying the washed oxysulfide.
Claim 6
Dependent Claim
12 words
A process according to claim 3 wherein said flux is sodium carbonate.
Claim 7
Dependent Claim
13 words
A process according to claim 3 wherein said lanthanum source is lanthanum oxide.
Claim 8
Dependent Claim
13 words
A process according to claim 3 wherein said lanthanum source is lanthanum carbonate.
Claim 9
Dependent Claim
22 words
A process according to claim 3 wherein the amount of sulfur is from about 2 to about 6 times said stoichiometrical amount.
Claim 10
Dependent Claim
24 words
A process according to claim 3 wherein said titanium dioxide is from about 0.005 to about 0.015 moles pe r mole of lanthanum source.
References Cited (Backward Citations)
US3418246A
Cited
US3502590A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-06 | 1979-10-06 | 1980-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-06 | 1983-10-06 | 1984-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-06 | 1987-10-06 | 1988-04-06 | $7700.00 | Window Closed / Lapsed |