Claim 2

In the production of a laminated film by melt extruding a covering resin film on a substrate resin film thereby to form a laminated film and cooling said laminated film, an improved process for producing a laminated film to be laterally stretched by clamping tools clamping the lateral edge parts thereof, which process comprises (1) applying a pressing force to the laminated film undergoing cooling, at a part thereof where said covering resin film can be plastically deformed more easily than the substrate resin film, at parts thereof to be clamped by said clamping tools, from the side of the substrate resin film, and toward and against a hard surface thereby to cause the substrate film to deflect elastically and concavely under said pressing force while retaining the original thickness thereof, the covering resin film undergoing cooling thereby being squeezed and plastically reduced in thickness at its part between said hard surface and the substrate resin film thus deflected, and (2) removing said pressing force from the laminated film thereby to permit the substrate resin film to return from its deflected state substantially to its undeformed planar state, whereby the covering resin film at said part thereof thus reduced in thickness, continuing to retain its reduced thickness and to retain its bonded state to the substrate resin film, follows the substrate resin film as it thus returns to its planar state, and a depressed region of thin film is thereby formed in the laminated film at a part thereof corresponding to said part of reduced thickness of the covering resin film and can be advantageously utilized for positive gripping by said clamping tools.

Claim 3

An improved process for producing a laminated film as set forth in claim 1 in which said pressing force is applied continuously by pressing a disk-shaped roll against the substrate resin film along each of its lateral edge parts, thereby to form continuously a thin film part along each of the lateral edge parts of the laminated film.

Claim 4

A process for producing a laminated film as set forth in claim 2 in which the principal surface of the disk-shaped roll for contacting the substrate resin film is parallel to the resin film.

Claim 5

A process for producing a laminated film as set forth in claim 2 in which the principal surface of the disk-shaped roll for contacting the substrate resin film has a shape with a crown in a section taken along a plane including the axial centerline of the roll.

Claim 6

A process for producing a laminated film as set forth in claim 2 in which the principal surface of the disk-shaped roll for contacting the substrate resin film has a peaked wedge-like shape in a section taken along a plane including the axial centerline of the roll.

Claim 7

A process for producing a laminated film as set forth in claim 2 in which the disk-shaped roll has a plurality of gear teeth thereon and forms thin film parts intermittently along the corresponding lateral edge part of the laminated film.

Claim 8

A process for producing a laminated film as set forth in claim 1 in which the cooling of the laminated film is accomplished by contacting a cooling roll in contact with the covering resin film, the surface of said cooling roll constituting said hard surface.

Claim 9

A process for producing a laminated film as set forth in claim 1 in which the substrate resin is a member selected from the group consisting of polyethylene, isotactic polypropylene, and resinous ethylene-propylene polymers.

Claim 10

A process for producing a laminated film as set forth in claim 1 in which the covering resin is a member selected from the group consisting of polyethylene, isotactic polypropylene, and resinous ethylene-propylene polymers.

Claim 11

An improved process for producing a laminated film as set forth in claim 1 in which said pressing force is applied continuously by pressing a roll against the substrate resin film along each of its lateral edge parts, the profile of the roll in a section taken along a plane including the axial center line of the row having a plurality of peaked portions separated from each other by recesses.

Claim 12

A process for producing a laminated film as set forth in claim 10 in which the peaked portions are all of the same shape and dimensions.

Claim 13

In the production of a laminated film by melt extruding a covering resin film of a first α-olefin polymer on a substrate resin film of a second α-olefin polymer thereby to form continuously a laminated film and cooling said laminated film, each of said first and second α-olefin polymers being selected from the group consisting of polyethylene, isotactic polypropylene, and resinous ethylene-propylene copolymers, an improved process for producing a laminated film to be laterally stretched by clamping tools clamping the lateral edge parts thereof, which process comprises (1) applying a pressing force to the laminated film undergoing cooling, at a part thereof where said covering resin film can be plastically deformed more easily than the substrate resin film, at parts thereof to be clamped by said clamping tools, from the side of the substrate resin film, and toward and against a hard surface by means of disk-shaped pressing rolls thereby to cause the substrate film to deflect elastically and concavely under said pressing force while retaining the original thickness thereof, the covering resin film undergoing cooling thereby being squeezed and reduced in thickness at its part between said hard surface and the substrate resin film thus deflected, and (2) removing said pressing force from the laminated film thereby to permit the substrate resin film to return from its deflected state substantially to its undeformed planar state whereby the covering resin film at said parts thereof thus reduced in thickness, continuing to retain its reduced thickness and to retain its bonded state to the substrate resin film, follows the substrate resin film as it thus returns to its planar state, and depressed regions of thin film are thereby formed in the laminated film continuously along said lateral edge parts thereof corresponding to said part of reduced thickness of the covering resin film and can be advantageously utilized for positive gripping by said clamping tools.

Claim 14

In the production of a laminated film by melt extruding a covering resin film of a first α-olefin polymer on a substrate resin film of a second α-olefin polymer thereby to form continuously a laminated film and cooling said laminated film, each of said first and second α-olefin polymers being selected from the group consisting of polyethylene, isotactic polypropylene, and resinous ethylene-propylene copolymers, an improved process for producing a laminated film to be laterally stretched by clamping tools clamping the lateral edge parts thereof, which process comprises (1) applying a pressing force to the laminated film undergoing cooling, at a part thereof where said covering resin film can be plastically deformed more easily than the substrate resin film, at parts thereof to be clamped by said clamping tools, from the side of the substrate resin film, and toward and against a hard surface by means of disk-shaped pressing rolls thereby to cause the substrate film to deflect elastically and concavely under said pressing force while retaining the original thickness thereof, the covering resin film undergoing cooling thereby being squeezed and reduced in thickness at its part between said hard surface and the substrate resin film thus deflected, and (2) removing said pressing force from the laminated film thereby to permit the substrate resin film to return from its deflected state substantially to its undeformed planar state whereby the covering resin film at said parts thereof thus reduced in thickness, continuing to retain its reduced thickness and to retain its bonded state to the substrate resin film, follows the substrate resin film as it thus returns to its planar state, and depressed regions of thin film are thereby formed in the laminated film continuously along said lateral edge parts thereof corresponding to said part of reduced thickness of the covering resin film and can be advantageously utilized for positive gripping by said clamping tools.