Permeable cement composition and method
Assignee: Texaco Inc
•
Filing: 1974-09-26
•
Granted: 1976-04-06
•
Expires: 1994-09-26
Abstract
Abstract The invention relates to an improved method of and composition for the treatment of an incompetent formation penetrated by a wellbore to prevent the movement of sand particles from the formation to the wellbore during recovery of the formation fluids by forming a treating composition of sand, cement, water and xanthan gum in a hydrocarbon carrier oil, injecting the treating composition into the formation under pressure, permitting the cement to set and form a permeable barrier film between the formation and wellbore and recovering fluids from the formation through the formed permeable cement barrier.
Inventors
- 👤 Bobby G. Harnsberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:46
CPC Classifications
E; E21; E21B; E21B43/00; E21B43/02; E21B43/025; C; C09; C09K; C09K8/00; C09K8/50; C09K8/502
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
132 words
A treating composition suspended in a hydrocarbon carrier oil consisting of a diesel oil containing from 100 to 800 ppm of naphthenic acids therein for use in forming a permeable cement barrier in the bore hole adjacent to an unconsolidated sand-containing producing formation, said composition consisting essentially of cement, from about 3 to about 12 parts by weight of sand particles having an average mesh size of from about 10 mesh to about 80 mesh, from about 0.7 to about 0.95 part by weight of salt water, each per part by weight of cement, and from 0.1 to 1.0% by weight of xanthan gum, based on the amount of water, and wherein said suspension contains from about 0.5 to 5 pounds of said treating composition per gallon of the hydrocarbon oil fraction.
Claim 2
Dependent Claim
132 words
A treating composition suspended in a hydrocarbon carrier oil consisting of a diesel oil containing from 100 to 800 ppm of naphthenic acids therein for use in forming a permeable cement barrier in the bore hole adjacent to an unconsolidated sand-containing producing formation, said composition consisting essentially of cement, from about 3 to about 12 parts by weight of sand particles having an average mesh size of from about 10 mesh to about 80 mesh, from about 0.7 to about 0.95 part by weight of salt water, each per part by weight of cement, and from 0.1 to 1.0% by weight of xanthan gum, based on the amount of water, and wherein said suspension contains from about 0.5 to 5 pounds of said treating composition per gallon of the hydrocarbon oil fraction.
Claim 3
Dependent Claim
38 words
A treating composition as claimed in claim 1 wherein the sand particles are of 20-40 mesh size and are present in an amount of from about 5 to 6 parts by weight per part by weight of cement.
Claim 4
Dependent Claim
29 words
A treating composition as claimed in claim 1 wherein the hydrocarbon carrier oil is a diesel oil fraction containing from about 100 to 500 ppm of naphthenic acids therein.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-06 | 1979-10-06 | 1980-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-06 | 1983-10-06 | 1984-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-06 | 1987-10-06 | 1988-04-06 | $7700.00 | Window Closed / Lapsed |