Composite rotor housing with wear-resistant coating

Assignee: Ford Motor Co
•
Filing: 1973-08-20
•
Granted: 1976-04-06
•
Expires: 1993-08-20
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A method is disclosed for fabricating a rotor housing for a rotary internal combustion engine. A conductive mandrel is prepared having an outer surface complimentary to the resultant rotor housing inner wall, the mandrel is provided with an exterior surface smoothness in the range of 4-12 r.m.s. A functional coating of a composite particle wear-resistant material is electrolytically deposited onto the mandrel (acting as a cathode) to form an assembly, the exposed surface of the assembly is controlled to have a roughness characterized by projections no less than 0.030 inches and concentrated in a number no less than 5/cm 2 . The assembly is placed in a die-casting machine where a molten metallic medium is cast thereabout forming a casting which is substantially mechanically locked to the assembly. The mandrel is then stripped from the coating to leave the resultant rotor housing. The resultant rotor housing is characterized by wear-resistant inner surface which is almost totally non-porous, its as-deposited surface roughness is at least 24 r.m.s., has a high heat transfer coefficient, is non-brittle and experiences no micro-cracking due to heat checking in service. The composite is economically fabricated and is strongly adherent.

Inventors

  • 👤 Leonard G. Cordone
  • 👤 Yeshwant P. Telang

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-27 10:22
CPC Classifications
B; B22; B22D; B22D19/00; B22D19/0009; F; F02; F02B; F02B53/00; F02B2053/005; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/4998; Y10T29/49988; Y10T29/49989

Claims Analysis

Total Claims: 10
Claim 1
Independent Claim 106 words
A method of preparing a coated rotor housing for a rotary internal combustion engine comprising: a. defining a conductive mandrel having an outer surface complimentary to the resultant rotary housing surface, b. electrolytically depositing a functional coating of a composite particle wear-resistant material onto said mandrel to form an assembly, the exposed surface of said assembly having a roughness characterized by projections at least 0.030 inches and concentrated in a number of 5-100 per cm 2 , c. casting a molten metallic material about said assembly, the casting material upon cooling being predominantly mechanically locked to said assembly, and d. stripping said mandrel from said coating.
Claim 2
Independent Claim 106 words
A method of preparing a coated rotor housing for a rotary internal combustion engine comprising: a. defining a conductive mandrel having an outer surface complimentary to the resultant rotary housing surface, b. electrolytically depositing a functional coating of a composite particle wear-resistant material onto said mandrel to form an assembly, the exposed surface of said assembly having a roughness characterized by projections at least 0.030 inches and concentrated in a number of 5-100 per cm 2 , c. casting a molten metallic material about said assembly, the casting material upon cooling being predominantly mechanically locked to said assembly, and d. stripping said mandrel from said coating.
Claim 3
Dependent Claim 22 words
A method as in claim 1, in which the as-deposited coating is characterized by a thickness in the range of 10-40 mils.
Claim 4
Dependent Claim 31 words
A method as in claim 2, in which the as-deposited coating is subjected to a finishing operation where no greater than 5 mils of said coating thickness is removed by machining.
Claim 5
Dependent Claim 37 words
The method as in claim 1, in which the composite particle wear-resistant material is comprised of a deposit of nickel containing a distribution of 2-8% silicon carbide particles having an average grain size of approximately 1 micron.
Claim 6
Dependent Claim 38 words
The method as in claim 4, in which the electro-deposited nickel material has fine particles of silicon carbide dispersed and oriented therein so that the hardness of the coating is in the range of 70-100 R c .
Claim 7
Dependent Claim 48 words
A method as in claim 1, in which the exposed surface of said assembly has a predetermined roughness obtained by maintaining the current density for said electrolytic deposition step initially in the range of 40-100 amps./ft 2 and subsequently raising said current density to 400-1000 amps./ft 2 .
Claim 8
Dependent Claim 62 words
The method as in claim 1, in which an electrolyte for the electro deposit step comprises a concentration of nickel sulfamate and nickel chlorhydrate, the silicon carbide particles being present in the electrolyte in the amount of about 100-150 grams per liter of electrolyte, the PH value being maintained in the range of 3-5 and the temperature being between ambient and 70°C.
Claim 9
Dependent Claim 29 words
The method as in claim 1, in which the resultant coating is substantially mechanically locked to said cast material, the electrolytically deposited coating having a porosity of substantially 0.
Claim 10
Dependent Claim 29 words
The method as in claim 1, in which the exposed surface resulting from step (d) of said coating has an interior surface roughness in the range of 4-12 r.m.s.

References Cited (Backward Citations)

GB873012A Cited
US3083424A Cited
US3061525A Cited
US3098270A Cited
US3293109A Cited
US3640799A Cited
US3616288A Cited
US3628237A Cited
US3797101A Cited
US3856635A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1979-04-06 1979-10-06 1980-04-06 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1983-04-06 1983-10-06 1984-04-06 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1987-04-06 1987-10-06 1988-04-06 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag