US3947550A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making a silicon carbide article of less than full density
Assignee: Ceradyne Inc
•
Filing: 1973-08-20
•
Granted: 1976-03-30
•
Expires: 1993-08-20
Abstract
Abstract This disclosure teaches a method of making a silicon carbide article of less than full density. A mixture of silicon carbide particles, silicon particles and a thermosetting polymeric material are molded to form an article as a green body. The green body is pyrolyzed to change the polymer into carbon and the carbon is then changed into silicon carbide by the silicon contained in the mixture.
Inventors
- 👤 Douglas R. Fitchmun
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 09:37
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/573; C01; C01B; C01B32/00; C01B32/90; C01B32/914; C01B32/956; C01B32/963; C01B32/984; C01P; C01P2006/00; C01P2006/10; C01P2006/90
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
227 words
A method of making a silicon carbide article which comprises the steps of: 1. mixing (a) 26 to 58 parts by weight of silicon carbide particles, (b) 44 to 25 parts by weight silicon particles, and (c) 30 to 17 parts by weight of a thermosetting, polymeric material which originally contains aromatic components or produces such aromatic components upon pyrolysis; 2. molding said mixture formed in step 1, said molding carried out by (a) preheating said mixture to a temperature whereat said polymeric material is in a liquid phase, (b) introducing said heated mixture into a mold, (c) filling said mold with said introduced mixture, and (d) developing a uniform, constant pressure throughout said mixture within said mold thereby to develop a continuous matrix of said polymeric material throughout said mold; 3. stiffening said mixture introduced into said mold to at least a degree sufficient to permit said molded article to be removed from said mold without substantial distortion thereof; 4. pyrolyzing said polymeric material of said molded article to produce a body in which said silicon carbide particles and said silicon particles are bonded together by substantially pure carbon; and 5. siliciding said carbon of said body produced in step 4 with said silicon particles of said body to form a finished article of substantially pure silicon carbide, said body being of less than full density.
Claim 2
Independent Claim
227 words
A method of making a silicon carbide article which comprises the steps of: 1. mixing (a) 26 to 58 parts by weight of silicon carbide particles, (b) 44 to 25 parts by weight silicon particles, and (c) 30 to 17 parts by weight of a thermosetting, polymeric material which originally contains aromatic components or produces such aromatic components upon pyrolysis; 2. molding said mixture formed in step 1, said molding carried out by (a) preheating said mixture to a temperature whereat said polymeric material is in a liquid phase, (b) introducing said heated mixture into a mold, (c) filling said mold with said introduced mixture, and (d) developing a uniform, constant pressure throughout said mixture within said mold thereby to develop a continuous matrix of said polymeric material throughout said mold; 3. stiffening said mixture introduced into said mold to at least a degree sufficient to permit said molded article to be removed from said mold without substantial distortion thereof; 4. pyrolyzing said polymeric material of said molded article to produce a body in which said silicon carbide particles and said silicon particles are bonded together by substantially pure carbon; and 5. siliciding said carbon of said body produced in step 4 with said silicon particles of said body to form a finished article of substantially pure silicon carbide, said body being of less than full density.
Claim 3
Independent Claim
230 words
A method of making a silicon carbide article which comprises the steps of: 1. mixing (a) 26 to 58 parts by weight of silicon carbide particles having a size less than about 80 microns, (b) 44 to 26 parts by weight of silicon particles of less than about 180 microns, and (c) 30 to 17 parts by weight of a thermosetting, polymeric material which (i) originally contains aromatic components or produces such aromatic components upon pyrolysis and (ii) is in a flowable, liquid phase at temperatures of a plastic molding operation; 2. injection molding said mixture formed in step 1, said injection molding carried out by (a) preheating said mixture to a temperature whereat said polymeric material is in a liquid phase, (b) introducing said heated mixture into a mold for an injection molding process, (c) filling said mold with said introduced mixture, and (d) developing a uniform, constant pressure throughout said mixture within said mold thereby to develop a matrix of said polymeric material throughout said mold with a greater amount of said polymeric material near the surface of said mold; 3. stiffening said mixture introduced into said mold to form a molded article, said stiffening of said mixture being accomplished by cross linking said thermosetting, polymeric material to at least a degree sufficient to permit said molded article to be removed from said mold without substantial distortion thereof;
Claim 4
Independent Claim
230 words
A method of making a silicon carbide article which comprises the steps of: 1. mixing (a) 26 to 58 parts by weight of silicon carbide particles having a size less than about 80 microns, (b) 44 to 26 parts by weight of silicon particles of less than about 180 microns, and (c) 30 to 17 parts by weight of a thermosetting, polymeric material which (i) originally contains aromatic components or produces such aromatic components upon pyrolysis and (ii) is in a flowable, liquid phase at temperatures of a plastic molding operation; 2. injection molding said mixture formed in step 1, said injection molding carried out by (a) preheating said mixture to a temperature whereat said polymeric material is in a liquid phase, (b) introducing said heated mixture into a mold for an injection molding process, (c) filling said mold with said introduced mixture, and (d) developing a uniform, constant pressure throughout said mixture within said mold thereby to develop a matrix of said polymeric material throughout said mold with a greater amount of said polymeric material near the surface of said mold; 3. stiffening said mixture introduced into said mold to form a molded article, said stiffening of said mixture being accomplished by cross linking said thermosetting, polymeric material to at least a degree sufficient to permit said molded article to be removed from said mold without substantial distortion thereof;
Claim 5
Dependent Claim
93 words
pyrolyzing said polymeric material of said molded article to produce a porous body in which said silicon carbide particles and silicon particles are bonded together by substantially pure carbon; and 5. siliciding said porous body produced in step 4 with said silicon particles of said body by heating said body in a suitable atmosphere to a temperature at which said silicon particles melt to form liquid silicon which reacts with said carbon thereby to form a finished article of substantially pure silicon carbide, which article has a dense skin and a porous core.
Claim 6
Dependent Claim
93 words
pyrolyzing said polymeric material of said molded article to produce a porous body in which said silicon carbide particles and silicon particles are bonded together by substantially pure carbon; and 5. siliciding said porous body produced in step 4 with said silicon particles of said body by heating said body in a suitable atmosphere to a temperature at which said silicon particles melt to form liquid silicon which reacts with said carbon thereby to form a finished article of substantially pure silicon carbide, which article has a dense skin and a porous core.
Claim 7
Dependent Claim
45 words
The method of making a silicon carbide article as defined in claim 2 wherein: a small quantity of a mold release agent is added to the mixture formed in step 1 to permit easy removal of the molded silicon carbide article from the injection mold.
Claim 8
Dependent Claim
21 words
The method of making a silicon carbide article as defined in claim 3 wherein: said mold release agent is zine stearate.
Claim 9
Dependent Claim
41 words
The method of making a silicon carbide article as defined in claim 2 wherein: said polymeric, thermosetting material which originally contains aromatic components is selected from the group of resins consisting of phenol furfural, phenol formaldehyde, polybenzimidazole, phenolicnapthalenediol terpolymer and polyphenylenes.
Claim 10
Dependent Claim
40 words
The method of making a silicon carbide article as defined in claim 2 wherein: said polymeric, thermosetting material which produces aromatic components upon pyrolysis is selected from the group of resins consisting of polyvinyl chloride, polyvinylidine chloride, and polyphenyl polymer.
Claim 11
Dependent Claim
63 words
The method of making a silicon carbide article as defined in claim 2 wherein: said pyrolyzing step is carried out by: positioning said molded article in a chamber having an inert atmosphere, slowly heating said body to a temperature of about 1000°C thereby progressively to (a) convert said polymeric material to aromatic components and (b) convert said aromatic components to substantially pure carbon.
Claim 12
Dependent Claim
50 words
The method of making a silicon carbide article as defined in claim 7 wherein: said body is heated to said temperature of 1000°C at a rate of about 40°C per hours, and wherein said body is cooled from said temperature of 1000°C at a rate of about 40°C per hour.
Claim 13
Dependent Claim
89 words
The method of making a silicon carbide article as defined in claim 2 wherein: said siliciding step is carried out by (a) positioning said pyrolyzed body in an heatable chamber, (b) establishing an inert atmosphere in the chamber, (c) heating said body to a temperature in the range of 1450° to 1550°C to melt the silicon particles of the body, (d) reacting said melted silicon particles with said carbon of said body to form a body of silicon carbide, and (e) cooling said silicon carbide body to room temperature.
Claim 14
Dependent Claim
67 words
The method of making silicon carbide article as defined in claim 9 wherein: said body is heated from room temperature to a temperature of 1450°C in a period from 2 to 3 hours, wherein said body is heated from 1450° to 1550°C in a period from 1 to 2 hours, and wherein said body is held at said 1550°C for a period of 20 to 40 minutes.
Claim 15
Independent Claim
132 words
A method of making a silicon carbide article which comprises the steps of: 1. mixing (a) 26 to 58 parts by weight of silicon carbide particles, (b) 44 to 25 parts by weight silicon particles, (c) 30 to 17 parts by weight of a thermosetting, polymeric material which originally contains aromatic components or produces such aromatic components upon pyrolysis and (d) a small amount of a blowing agent; 2. molding said mixture formed in step 1, said molding carried out by (a) preheating said mixture to a temperature whereat said polymeric material is in a liquid phase, (b) introducing said heated mixture into a mold, (c) filling less than all of said mold with said introduced mixture, and (d) reacting said blowing agent to developing a uniform, constant pressure throughout said mold;
Claim 16
Independent Claim
132 words
A method of making a silicon carbide article which comprises the steps of: 1. mixing (a) 26 to 58 parts by weight of silicon carbide particles, (b) 44 to 25 parts by weight silicon particles, (c) 30 to 17 parts by weight of a thermosetting, polymeric material which originally contains aromatic components or produces such aromatic components upon pyrolysis and (d) a small amount of a blowing agent; 2. molding said mixture formed in step 1, said molding carried out by (a) preheating said mixture to a temperature whereat said polymeric material is in a liquid phase, (b) introducing said heated mixture into a mold, (c) filling less than all of said mold with said introduced mixture, and (d) reacting said blowing agent to developing a uniform, constant pressure throughout said mold;
Claim 17
Dependent Claim
95 words
stiffening said mixture introduced into said mold to at least a degree sufficient to permit said molded article to be removed from said mold without substantial distortion thereof; 4. pyrolyzing said polymeric material of said molded article to produce a body in which said silicon carbide particles and said silicon particles are bonded together by substantially pure carbon; and 5. siliciding said carbon of said body produced in step 4 with said silicon particles of said body to form a finished article of substantially pure silicon carbide, said body being of less than full density.
Claim 18
Dependent Claim
95 words
stiffening said mixture introduced into said mold to at least a degree sufficient to permit said molded article to be removed from said mold without substantial distortion thereof; 4. pyrolyzing said polymeric material of said molded article to produce a body in which said silicon carbide particles and said silicon particles are bonded together by substantially pure carbon; and 5. siliciding said carbon of said body produced in step 4 with said silicon particles of said body to form a finished article of substantially pure silicon carbide, said body being of less than full density.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-30 | 1979-09-29 | 1980-03-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-30 | 1983-09-29 | 1984-03-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-30 | 1987-09-29 | 1988-03-30 | $7700.00 | Window Closed / Lapsed |