Method for preparation of hydrocarbon liquid polymers
Assignee: Lion Corp
•
Filing: 1975-02-14
•
Granted: 1976-03-30
•
Expires: 1995-02-14
Abstract
Abstract A method of effecting polymerization of olefins having 6 or more carbon atoms or mixtures of such olefins (hereinafter referred to as the feed olefin), to produce a hydrocarbon liquid polymer which comprises mixing a catalyst composed of aluminum chloride, ketone having 4 or more carbon atoms and olefin catalyst constituent with 0.01 to 0.3 mole of ester, ether or alcohol per mole of said aluminum chloride and effecting the polymerization of the feed olefin at a reaction temperature of more than 60 DEG C.
Inventors
- 👤 Hiroshi Isa
- 👤 Toshiyuki Ukigai
- 👤 Anri Tominaga
- 👤 Ryozo Taniyasu
- 👤 Masuzo Nagayama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:39
CPC Classifications
C; C10; C10M; C10M3/00; C07; C07C; C07C2/00; C07C2/02; C07C2/04; C07C2/06; C07C2/08; C07C2/14; C07C2/20; C07C2/22; C07C2527/00; C07C2527/06; C07C2527/125; C07C2527/126; C07C2531/00; C07C2531/02; C07C2531/26; C10M2205/00; C10M2205/02; C10M2205/028
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
148 words
A method of polymerizing feed olefins having at least 6 carbon atoms or mixtures of such feed olefins, to produce a hydrocarbon liquid polymer, which comprises: polymerizing said feed olefin at a temperature of more than 60°C, in contact with a catalyst prepared by reacting at a temperature of more than 60°C, catalyst constituents consisting essentially of (a) aluminum chloride, (b) ketone having at least 4 carbon atoms, (c) olefin catalyst constituent selected from the group consisting of said feed olefin and olefins of lower carbon atom number, and (d) ester, ether or alcohol, the amount of (a) being from 0.1 to 5 mole percent based on the feed olefin, the molar ratio of (a)/(b) being from 1/1 to 1/1.2, the amount of (c) being more than 1 mole percent based on (a) and the amount of (d) being from 0.01 to 0.3 mole per mole of (a).
Claim 2
Independent Claim
148 words
A method of polymerizing feed olefins having at least 6 carbon atoms or mixtures of such feed olefins, to produce a hydrocarbon liquid polymer, which comprises: polymerizing said feed olefin at a temperature of more than 60°C, in contact with a catalyst prepared by reacting at a temperature of more than 60°C, catalyst constituents consisting essentially of (a) aluminum chloride, (b) ketone having at least 4 carbon atoms, (c) olefin catalyst constituent selected from the group consisting of said feed olefin and olefins of lower carbon atom number, and (d) ester, ether or alcohol, the amount of (a) being from 0.1 to 5 mole percent based on the feed olefin, the molar ratio of (a)/(b) being from 1/1 to 1/1.2, the amount of (c) being more than 1 mole percent based on (a) and the amount of (d) being from 0.01 to 0.3 mole per mole of (a).
Claim 3
Dependent Claim
27 words
A method according to claim 1, wherein said feed olefin is selected from the group consisting of olefins having 8 to 10 carbon atoms and mixtures thereof.
Claim 4
Dependent Claim
28 words
A method according to claim 1, wherein said ketone (b) is selected from the group consisting of methyl ethyl ketone, diethyl ketone, diisobutyl ketone, dioctyl ketone and cyclohexanone.
Claim 5
Dependent Claim
29 words
A method according to claim 1, wherein the amount of said ketone (b) is in the range of from 1.02 to 1.10 mole, per mole of aluminum chloride (a).
Claim 6
Dependent Claim
17 words
A method according to claim 1, wherein said olefin catalyst constituent (c) is the feed olefin itself.
Claim 7
Dependent Claim
50 words
A method acccording to claim 1, wherein said catalyst constituent (d) is selected from the group consisting of alkyl esters of fatty acids, said esters having less than 10 carbon atoms, alkyl ethers having less than 10 carbon atoms, and monohydric or polyhydric alcohols having less than 10 carbon atoms.
Claim 8
Dependent Claim
29 words
A method according to claim 1, wherein the amount of said aluminum chloride (a) is in the range of from 1.0 to 3.0 mol.%, relative to the feed olefin.
Claim 9
Dependent Claim
19 words
A method according to claim 1, wherein the polymerization temperature is in the range of from 60° to 200°C.
Claim 10
Dependent Claim
22 words
A method according to claim 1, wherein the polymerization reaction is effected while controlling the heat of reaction by adding a solvent.
Claim 11
Dependent Claim
21 words
A method according to claim 9, wherein said solvent is selected from the group consisting of n-pentane, isooctane, trichloroethane and tetrachloroethane.
Claim 12
Dependent Claim
27 words
A method according to claim 9, wherein the weight of said solvent is in the range of from 0.5 to 4 times that of the feed olefin.
Claim 13
Dependent Claim
26 words
A method according to claim 1 wherein ammonia is introduced into the polymer reaction product thereby to decompose the catalyst dissolved in said polymer reaction product.
Claim 14
Dependent Claim
29 words
A method according to claim 1, wherein unreacted olefins and olefin dimers contained in the polymer reaction product are removed by means of a distillation process or extraction process.
Claim 15
Dependent Claim
18 words
A method according to claim 1, wherein the double bonds remaining in the polymer reaction product are hydrogenated.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-30 | 1979-09-29 | 1980-03-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-30 | 1983-09-29 | 1984-03-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-30 | 1987-09-29 | 1988-03-30 | $7700.00 | Window Closed / Lapsed |