Low profile molding composition and process for making same
Assignee: Dow Chemical Co
•
Filing: 1974-08-05
•
Granted: 1976-03-30
•
Expires: 1994-08-05
Abstract
Abstract Better wet-out of glass fiber, lower viscosity of the resin mix which allows for higher filler loadings and better stability are the improvements of this invention. The compositions are prepared by an improved process which comprises mixing a vinyl ester resin having pendant half ester groups and a copolymerizable monomer with a polymeric low profile additive, glass fiber reinforcing material, CaCO 3 filler and a viscosity reducing agent comprising a copolymer of a maleic acid half ester of a polyethylene glycol having a molecular weight of about 1450 to 6000 and a monoalkenyl aromatic monomer. A chemical thickening agent such as magnesium oxide may also be added.
Inventors
- 👤 Sammy Duane Tatum
- 👤 Jerry Marvin Hawkins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:22
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/06; C08F; C08F299/00; C08F299/02; C08F299/026; C08K; C08K3/00; C08K3/18; C08K3/24; C08K3/26; C08L25/00; C08L25/02; C08L25/04; C08L25/06; C08L47/00; C08L53/00; C08L53/02; C08L9/00
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
167 words
A reduced viscosity low profile molding composition comprising in combination about 100 parts of a mixture of a terminally unsaturated vinyl ester resin having pendant half ester groups and a copolymerizable monomer, about 0.1 to 5 parts of a viscosity reducing agent, about 5 to 25 parts of a polymeric low profile additive and about 10 to 150 parts of an inert filler; wherein said viscosity reducing agent is a copolymer of a maleic acid half ester of a polyethylene glycol having a weight average molecular weight of about 1450 to 6000 and a monoalkenyl aromatic monomer, said copolymer comprising about 0.5 to 2 moles of the half ester per 100 moles of the aromatic monomer and said copolymer having a weight average molecular weight of from about 15,000 to about 50,000; and wherein said vinyl ester resin is prepared by reacting about equivalent amounts of a polyepoxide and an unsaturated monocarboxylic acid and forming pendant half ester groups by further reaction with a dicarboxylic acid anhydride.
Claim 2
Dependent Claim
167 words
A reduced viscosity low profile molding composition comprising in combination about 100 parts of a mixture of a terminally unsaturated vinyl ester resin having pendant half ester groups and a copolymerizable monomer, about 0.1 to 5 parts of a viscosity reducing agent, about 5 to 25 parts of a polymeric low profile additive and about 10 to 150 parts of an inert filler; wherein said viscosity reducing agent is a copolymer of a maleic acid half ester of a polyethylene glycol having a weight average molecular weight of about 1450 to 6000 and a monoalkenyl aromatic monomer, said copolymer comprising about 0.5 to 2 moles of the half ester per 100 moles of the aromatic monomer and said copolymer having a weight average molecular weight of from about 15,000 to about 50,000; and wherein said vinyl ester resin is prepared by reacting about equivalent amounts of a polyepoxide and an unsaturated monocarboxylic acid and forming pendant half ester groups by further reaction with a dicarboxylic acid anhydride.
Claim 3
Dependent Claim
21 words
The composition of claim 1 further comprising a sufficient amount of an alkaline earth oxide or hydride to thicken the composition.
Claim 4
Dependent Claim
16 words
The composition of claim 2 further comprising up to 150 parts of a fibrous reinforcing material.
Claim 5
Dependent Claim
17 words
The composition of claim 1 wherein said polyglycol has a weight average molecular weight of about 4000.
Claim 6
Dependent Claim
17 words
The composition of claim 1 wherein said copolymer is a copolymer of styrene and the half ester.
Claim 7
Dependent Claim
46 words
The composition of claim 1 wherein said copolymer is a copolymer of styrene and a maleic acid half ester of a polyethylene glycol having a molecular weight of about 4000, and said copolymer having a weight average molecular weight of from about 18,000 to about 25,000.
Claim 8
Dependent Claim
40 words
The composition of claim 6 wherein said low profile additive is a polydiene rubber containing in polymerized form about 30 to 100 weight percent of a conjugated diene and the balance to make 100 percent of a monoalkenyl aromatic monomer.
Claim 9
Dependent Claim
18 words
The composition of claim 6 wherein said low profile additive is polystyrene, polybutadiene or a styrene-butadiene block copolymer.
Claim 10
Dependent Claim
20 words
The composition of claim 6 wherein said low profile additive is a mixture of polystyrene and a styrene-butadiene block copolymer.
Claim 11
Dependent Claim
167 words
An improved process for making glass fiber reinforced sheet molding compounds which comprises combining in any convenient order about 100 parts of a mixture of a terminally unsaturated vinyl ester resin having pendant half ester groups and a copolymerizable monomer, about 0.1 to 5 parts of a viscosity reducing agent, about 5 to 25 parts of a polymeric low profile additive, about 10 to 150 parts of an inert filler and up to about 150 parts of reinforcing glass fiber, wherein said viscosity reducing agent is a copolymer of a maleic acid half ester of a polyethylene glycol having an average molecular weight of about 1450 to 6000 and a monoalkenyl aromatic monomer, said copolymer comprising about 0.5 to 2 moles of the half ester per 100 moles of the aromatic monomer, and wherein said vinyl ester resin is prepared by reacting about equivalent amounts of a polyepoxide and an unsaturated monocarboxylic acid and forming pendant half ester groups by further reaction with a dicarboxylic acid anhydride.
Claim 12
Dependent Claim
167 words
An improved process for making glass fiber reinforced sheet molding compounds which comprises combining in any convenient order about 100 parts of a mixture of a terminally unsaturated vinyl ester resin having pendant half ester groups and a copolymerizable monomer, about 0.1 to 5 parts of a viscosity reducing agent, about 5 to 25 parts of a polymeric low profile additive, about 10 to 150 parts of an inert filler and up to about 150 parts of reinforcing glass fiber, wherein said viscosity reducing agent is a copolymer of a maleic acid half ester of a polyethylene glycol having an average molecular weight of about 1450 to 6000 and a monoalkenyl aromatic monomer, said copolymer comprising about 0.5 to 2 moles of the half ester per 100 moles of the aromatic monomer, and wherein said vinyl ester resin is prepared by reacting about equivalent amounts of a polyepoxide and an unsaturated monocarboxylic acid and forming pendant half ester groups by further reaction with a dicarboxylic acid anhydride.
Claim 13
Dependent Claim
24 words
The process of claim 10 further comprising the addition of a sufficient amount of an alkaline earth oxide or hydroxide to thicken the composition.
Claim 14
Dependent Claim
12 words
The process of claim 11 wherein said filler is CaCO 3 .
Claim 15
Dependent Claim
12 words
The composition of claim 1 wherein said filler is CaCO 3 .
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-30 | 1979-09-29 | 1980-03-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-30 | 1983-09-29 | 1984-03-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-30 | 1987-09-29 | 1988-03-30 | $7700.00 | Window Closed / Lapsed |