Production of precipitated red iron (III) oxide pigment relatively free of α-FEOOH
Assignee: Bayer AG
•
Filing: 1973-09-19
•
Granted: 1976-03-23
•
Expires: 1993-09-19
Abstract
Abstract In the production of a precipitated red iron (III) oxide pigment of hematite structure wherein an aqueous iron (II) salt solution is mixed with an aqueous alkali solution in substantially equivalent quantities to produce an aqueous suspension of iron (II) hydroxide or carbonate, the suspension is oxidized by passing oxygen-containing gases through it with stirring under atmospheric pressure at a temperature of about 0° to 50°C, and the resulting iron (III) seed suspension is allowed to grow into precipitated red iron (III) oxide pigment by further oxidation with an oxygen-containing gas at a temperature of about 50° to 100°C in the presence of more iron (II) salt and alkali solution or in the presence of iron (II) salt and metallic iron at a pH-value kept in the acid range, the improvement which comprises producing the iron (III) seed suspension in the presence of a foreign modifying substance so that lattice-distorted, chemically reactive finely divided delta-FeOOH seeds are formed, whereby the resulting red iron (III) oxide pigment contains less than about 15 % by weight of α-FeOOH. The modifying substance may be a chloride of magnesium, calcium or aluminum, vanadium pentoxide, sodium phosphate, erythritol, mannitol, glyceric acid, K, Na-tartrate, Na-citrate, ribose, glucose, fructose, tannin, or NH 4 --, Ca--, Al--, Fe or Mg-lignin sulfonate.
Inventors
- 👤 Franz Hund
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:33
CPC Classifications
C; C09; C09C; C09C1/00; C09C1/22; C09C1/24; C01; C01P; C01P2002/00; C01P2002/50; C01P2002/52
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
218 words
In the production of a precipitated red iron (III) oxide pigment of hematite structure wherein an aqueous iron (II) salt solution is mixed with an aqueous alkali solution in substantially equivalent quantities to produce an aqueous suspension of iron (II) hydroxide or carbonate, the suspension is oxidized by passing oxygen-containing gases through it with stirring under atmospheric pressure at a temperature of about 0° to 50°C to form a suspension of iron (III) seed, and the resulting iron (III) seed suspension is allowed to grow into precipitated red iron (III) oxide pigment by further oxidation with an oxygen-containing gas at a temperature of about 50° to 100°C in the presence of more iron (II) salt and alkali solution or in the presence of iron (II) salt and metallic iron at a pH-value kept in the acid range, the improvement which comprises producing the iron (III) seed suspension by oxidation with the oxygen-contaning gases for about 4 to 30 minutes and in the presence of at least one foreign modifying substance selected from the group consisting of a compound of magnesium, calcium, copper, zinc, aluminum, antimony, phosphorus, arsenic, vandium and silicon, so that lattice-distorted chemically reactive finely divided delta--FeOOH seeds are formed, whereby the resulting red iron (III) oxide pigment contains less than about 15% by weight of α--FeOOH.
Claim 2
Dependent Claim
218 words
In the production of a precipitated red iron (III) oxide pigment of hematite structure wherein an aqueous iron (II) salt solution is mixed with an aqueous alkali solution in substantially equivalent quantities to produce an aqueous suspension of iron (II) hydroxide or carbonate, the suspension is oxidized by passing oxygen-containing gases through it with stirring under atmospheric pressure at a temperature of about 0° to 50°C to form a suspension of iron (III) seed, and the resulting iron (III) seed suspension is allowed to grow into precipitated red iron (III) oxide pigment by further oxidation with an oxygen-containing gas at a temperature of about 50° to 100°C in the presence of more iron (II) salt and alkali solution or in the presence of iron (II) salt and metallic iron at a pH-value kept in the acid range, the improvement which comprises producing the iron (III) seed suspension by oxidation with the oxygen-contaning gases for about 4 to 30 minutes and in the presence of at least one foreign modifying substance selected from the group consisting of a compound of magnesium, calcium, copper, zinc, aluminum, antimony, phosphorus, arsenic, vandium and silicon, so that lattice-distorted chemically reactive finely divided delta--FeOOH seeds are formed, whereby the resulting red iron (III) oxide pigment contains less than about 15% by weight of α--FeOOH.
Claim 3
Dependent Claim
33 words
A process as claimed in claim 1, wherein said compound is at least one member selected from the group consisting of chlorides of magnesium, calcium and aluminum, or vanadium pentoxide, and sodium phosphate.
Claim 4
Dependent Claim
29 words
A process as claimed in claim 1, wherein the seedmodifying foreign substance is used in about 1 to 30% by weight based on the iron present during seed formation.
Claim 5
Dependent Claim
35 words
A process as claimed in claim 1, wherein the seed formation is effected in the presence of about 0.8 to 2.0 equivalents of aqueous alkali solution, based on the quantity of iron (II) salt present.
Claim 6
Dependent Claim
45 words
A process as claimed in claim 1, wherein the newly formed seed prior to said further oxidation is subjected to a thermal treatment at a temperature above about 50°C and up to 100°C under normal pressure and above 100°C under excess pressure in an autoclave.
Claim 7
Dependent Claim
45 words
A process as claimed in claim 5, wherein the seedmodifying foreign substance is used in about 4 to 20% by weight, the temperature during seed formation is about 20° to 40°C, and pigment formation is carried out at a temperature of about 70° to 90°C.
Claim 8
Dependent Claim
243 words
In the production of a precipitated red iron (III) oxide pigment of hematite structure wherein an aqueous iron (II) salt solution is mixed with an aqueous alkali solution in substantially equivalent quantities to produce an aqueous suspension of iron (II) hydroxide or carbonate, the suspension is oxidized by passing oxygencontaining gases through it with stirring under atmospheric pressure at a temperature of about 0° to 50°C to form a suspension of iron (III) seed, and the resulting iron (III) seed suspension is allowed to grow into precipitated red iron (III) oxide pigment by further oxidation with an oxygen-containing gas at a temperature of about 50° to 100°C in the presence of more iron (II) salt and alkali solution or in the presence of iron (II) salt and metallic iron at a pH-value kept in the acid range, the improvement which comprises producing the iron (III) seed suspension by oxidation with the oxygen-containing gases for about 4 to 30 minutes and in the presence of at least one foreign modifying substance selected from the group consisting of a trihydric or polyhydric alcohol, aliphatic monocarboxylic acid, dicarboxylic acid with more than one alcohol group in the molecule, aliphatic tricarboxylic acid with at least one alcohol group in the molecule, and monosaccharide, disaccharide or polysaccharide hydroxyaldehyde or hydroxyketone, so that lattice-distorted chemically reactive finely divided delta--FeOOH seeds are formed, whereby the resulting red iron (III) oxide pigment contains less than about 15% by weight of α--FeOOH.
Claim 9
Dependent Claim
243 words
In the production of a precipitated red iron (III) oxide pigment of hematite structure wherein an aqueous iron (II) salt solution is mixed with an aqueous alkali solution in substantially equivalent quantities to produce an aqueous suspension of iron (II) hydroxide or carbonate, the suspension is oxidized by passing oxygencontaining gases through it with stirring under atmospheric pressure at a temperature of about 0° to 50°C to form a suspension of iron (III) seed, and the resulting iron (III) seed suspension is allowed to grow into precipitated red iron (III) oxide pigment by further oxidation with an oxygen-containing gas at a temperature of about 50° to 100°C in the presence of more iron (II) salt and alkali solution or in the presence of iron (II) salt and metallic iron at a pH-value kept in the acid range, the improvement which comprises producing the iron (III) seed suspension by oxidation with the oxygen-containing gases for about 4 to 30 minutes and in the presence of at least one foreign modifying substance selected from the group consisting of a trihydric or polyhydric alcohol, aliphatic monocarboxylic acid, dicarboxylic acid with more than one alcohol group in the molecule, aliphatic tricarboxylic acid with at least one alcohol group in the molecule, and monosaccharide, disaccharide or polysaccharide hydroxyaldehyde or hydroxyketone, so that lattice-distorted chemically reactive finely divided delta--FeOOH seeds are formed, whereby the resulting red iron (III) oxide pigment contains less than about 15% by weight of α--FeOOH.
Claim 10
Dependent Claim
29 words
A process as claimed in claim 7, wherein the seed-modifying foreign substance is used in about 1 to 30% by weight based on the iron present during seed formation.
Claim 11
Dependent Claim
35 words
A process as claimed in claim 7, wherein the seed formation is effected in the presence of about 0.8 to 2.0 equivalents of aqueous alkali solution, based on the quantity of iron (II) salt present.
Claim 12
Dependent Claim
45 words
A process as claimed in claim 7, wherein the newly formed seed prior to said further oxidation is subjected to a thermal treatment at a temperature above about 50°C and up to 100°C under normal pressure and above 100°C under excess pressure in an autoclave.
Claim 13
Dependent Claim
45 words
A process as claimed in claim 7, wherein the seed-modifying foreign substance is used in about 4 to 20% by weight, the temperature during seed formation is about 20 to 40°C, and pigment formation is carried out at a temperature of about 70° to 90°C.
Claim 14
Dependent Claim
43 words
A process as claimed in claim 7, wherein the seed-modifying foreign substance is at least one member selected from the group consisting of erythritol, mannitol, glyceric acid, K,Na-tartrate, Na-citrate, ribose, glucose, fructose, tannin, and NH 4 --, Ca--, Al--, Fe-- and Mg--lignin sulfonate.
References Cited (Backward Citations)
US2620261A
Cited
US2558303A
Cited
US2618532A
Cited
US2618571A
Cited
US2696426A
Cited
US3009821A
Cited
US3382174A
Cited
US3627554A
Cited
US3755554A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-23 | 1979-09-22 | 1980-03-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-23 | 1983-09-22 | 1984-03-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-23 | 1987-09-22 | 1988-03-23 | $7700.00 | Window Closed / Lapsed |