Method and apparatus for producing high modulus bixial fabric
Assignee: BP Chemicals Hitco Inc
•
Filing: 1974-06-10
•
Granted: 1976-03-23
•
Expires: 1994-06-10
Abstract
Abstract The transverse properties of high modulus fabric such as graphite are significantly improved by continuously processing the material through a multiple roller unit under warp tension while restraining fill shrinkage by wrapping the material no less than 180° around each roll and by minimizing unrestrained inter-roll travel by controlling the inter-roll span. Graphite precursor fabrics such as polyacrylonitrile (PAN) can be stretched as high as 45% in the warp direction with as little as 1-2% shrinkage in the fill direction. The invention also relates to simultaneous stretching and preoxidation of the precursor fabric under tension and while minimizing fill shrinkage.
Inventors
- 👤 Richard J. Larsen
- 👤 Robert W. Mitchell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 09:27
CPC Classifications
D; D06; D06C; D06C3/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
143 words
A continuous and dynamic method for developing high biaxial modulus in a woven graphite precursor fabric comprising the steps of: 1. stretching the fabric while heating the fabric to a temperature of at least 175°F; 2. preoxidizing the fabric by heating the fabric to a temperature of at least 400°F and applying an oxidizing atmosphere to the fabric, steps (1) and (2) being conducted while simultaneously applying a warp tension of at least 5 pounds per inch up to the breaking strength of the fabric to the fabric; and passing the tensioned fabric around at least 180° of the alternate upper and lower surfaces of at least two closely spaced rolls, the tangential distance between said rolls being no more than 12 inches and stretching said fabric in the warp direction up to 50% while restraining fill shrinkage to no more than 2%.
Claim 2
Dependent Claim
143 words
A continuous and dynamic method for developing high biaxial modulus in a woven graphite precursor fabric comprising the steps of: 1. stretching the fabric while heating the fabric to a temperature of at least 175°F; 2. preoxidizing the fabric by heating the fabric to a temperature of at least 400°F and applying an oxidizing atmosphere to the fabric, steps (1) and (2) being conducted while simultaneously applying a warp tension of at least 5 pounds per inch up to the breaking strength of the fabric to the fabric; and passing the tensioned fabric around at least 180° of the alternate upper and lower surfaces of at least two closely spaced rolls, the tangential distance between said rolls being no more than 12 inches and stretching said fabric in the warp direction up to 50% while restraining fill shrinkage to no more than 2%.
Claim 3
Dependent Claim
20 words
A method according to claim 1 in which the fabric is wrapped around at least 270° of each roll surface.
Claim 4
Dependent Claim
20 words
A method according to claim 2 in which the tangential distance between adjacent rolls is from 1/2 to 3 inches.
Claim 5
Dependent Claim
19 words
A method according to claim 3 in which the warp tension is from 10 to 20 pounds per inch.
Claim 6
Dependent Claim
15 words
A method according to claim 1 in which the roll surfaces are arcuate, convexly shaped.
Claim 7
Independent Claim
103 words
An apparatus for continuously processing graphite precursor fabric; at least two rolls arranged to receive said fabric wrapped over at least 180° of the alternate upper and lower surfaces of adjacent rolls; roll support means disposed to support the adjacent rolls such that the tangential distance between adjacent rolls is no more than 12 inches; means to tension the wrapped fabric from at least 5 pounds per inch to below breaking strength to stretch the fabric in the warp direction up to 50% while restraining fill shrinkage to no more than 2%; means for applying an oxidizing atmosphere to the tensioned heated fabric.
Claim 8
Independent Claim
103 words
An apparatus for continuously processing graphite precursor fabric; at least two rolls arranged to receive said fabric wrapped over at least 180° of the alternate upper and lower surfaces of adjacent rolls; roll support means disposed to support the adjacent rolls such that the tangential distance between adjacent rolls is no more than 12 inches; means to tension the wrapped fabric from at least 5 pounds per inch to below breaking strength to stretch the fabric in the warp direction up to 50% while restraining fill shrinkage to no more than 2%; means for applying an oxidizing atmosphere to the tensioned heated fabric.
Claim 9
Dependent Claim
40 words
An apparatus according to claim 6 in which a plurality of alternate rolls are disposed on axial parallel planes, said rolls being separated by at least the radius of said rolls to provide an S-wrap of fabric through said apparatus.
Claim 10
Dependent Claim
24 words
An apparatus according to claim 6 further including independent driver means associated with each roll for driving each roll at a set, predetermined speed.
Claim 11
Dependent Claim
28 words
An apparatus according to claim 8 further including independent heating means for heating each roll to a predetermined temperature successively higher than the temperature of the preceding roll.
Claim 12
Dependent Claim
69 words
An apparatus according to claim 6 including a first stretching chamber containing at least two of said rolls and roll support means and including first heating means for heating the fabric up to 400°F and a second preoxidation chamber including a second set of said rolls and roll support means and including said applying means and second independent heating means for heating the fabric to a temperature above 400°F.
References Cited (Backward Citations)
US2824383A
Cited
US2884015A
Cited
US3243845A
Cited
US3474509A
Cited
US3517425A
Cited
US3803672A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-23 | 1979-09-22 | 1980-03-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-23 | 1983-09-22 | 1984-03-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-23 | 1987-09-22 | 1988-03-23 | $7700.00 | Window Closed / Lapsed |