Abstract
Abstract A method for producing a phenolic molding is disclosed. The method includes the steps of mixing phenol, formaldehyde and a hydraulic cement, forming the resulting composition to a predetermined shape and maintaining the composition in the predetermined shape until an insoluble, infusible article is formed by condensation. At least 10 percent of the hydraulic cement must be Portland cement. The mole ratio of formaldehyde to phenol must be at least 1:1, and the amount of hydraulic cement must be sufficient for reaction with from 1 to 9 times the sum of the water of condensation of the phenol with the formaldehyde and the water charged to the mix. The use of reinforcing glass fibers in producing phenolic moldings is also disclosed, as well as the use of urea and resorcinol in addition to the phenol, formaldehyde and hydraulic cement.
Inventors
- 👤 Kevin M. Foley
- 👤 Frank Paul McCombs
- 👤 Reuben H. Bell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:31
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02; C04B24/00; C04B24/24; C04B24/28; C04B24/30; C04B24/307; C04B24/40; C04B24/42; C08; C08K; C08K3/00; C08K3/01; C08K3/013
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
105 words
A method for producing a phenolic molding which includes the steps of mixing phenol, formaldehyde and a hydraulic cement at least 10 percent of which is Portland cement in such proportions that the mole ratio of formaldehyde to phenol is at least 1:1 and the weight of the hydraulic cement is from one to nine times the sum of the weight of the water charged to the mix and three-fifths of the weight of the formaldehyde charged to the mix, forming the resulting composition to a predetermined shape and maintaining the composition in the predetermined shape until an insoluble, infusible article is formed by condensation.
Claim 2
Independent Claim
105 words
A method for producing a phenolic molding which includes the steps of mixing phenol, formaldehyde and a hydraulic cement at least 10 percent of which is Portland cement in such proportions that the mole ratio of formaldehyde to phenol is at least 1:1 and the weight of the hydraulic cement is from one to nine times the sum of the weight of the water charged to the mix and three-fifths of the weight of the formaldehyde charged to the mix, forming the resulting composition to a predetermined shape and maintaining the composition in the predetermined shape until an insoluble, infusible article is formed by condensation.
Claim 3
Dependent Claim
28 words
A method as claimed in claim 1 in which the composition is subjected to a temperature above ambient and to super-atmospheric pressure while maintained in the predetermined shape.
Claim 4
Dependent Claim
27 words
A method as claimed in claim 2 wherein the composition additionally contains from 10 percent to 150 percent of urea, based upon the weight of the phenol.
Claim 5
Dependent Claim
27 words
A method as claimed in claim 1 wherein the composition additionally contains from 1 percent to 70 percent of resorcinol, based upon the weight of the phenol.
Claim 6
Dependent Claim
108 words
A method as claimed in claim 3 wherein the mole ratio of formaldehyde to phenol is from about 1.5:1 to about 4.5:1, the weight of hydraulic cement is from about 11/2 to about 5 times the sum of the weight of the water charged to the mix and three-fifths of the weight of the formaldehyde charged to the mix, and wherein the initial mix is maintained at a temperature not higher than about 125°F. until partial condensation occurs, the partial condensate and glass fibers are collected on a carrier sheet, and the condensate is formed to an insoluble, infusible article with the glass fibers in reinforcing relationship therein.
Claim 7
Dependent Claim
121 words
A method as claimed in claim 5 wherein the phenol, formaldehyde, urea and a portion of the Portland cement ranging from about two one-hundredths to two-tenths of the sum of the weight of the water charged to the mix and three-fifths of the weight of the formaldehyde charged to the mix are maintained at a temperature not higher than about 125°F. for from 10 to 24 hours, and wherein the remainder of the Portland cement and of the Gypsum cement, if any, are then added to the reaction mixture while the temperature thereof is maintained not higher than about 125°F., and wherein it is the resulting partial condensate that is collected with glass fibers and formed into an insoluble, infusible article.
Claim 8
Dependent Claim
10 words
A phenolic molding produced by the method of claim 1.
References Cited (Backward Citations)
US2152670A
Cited
US3240736A
Cited
US3216966A
Cited
US3415774A
Cited
US3502610A
Cited
US3663720A
Cited
US3666703A
Cited
US3785839A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-16 | 1979-09-15 | 1980-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-16 | 1983-09-15 | 1984-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-16 | 1987-09-15 | 1988-03-16 | $7700.00 | Window Closed / Lapsed |