Assignee: Hoechst AG
•
Filing: 1973-06-18
•
Granted: 1976-03-09
•
Expires: 1993-06-18
Abstract
Abstract The invention provides condensed aluminum phosphates which contain P 2 O 5 and Al 2 O 3 in a molar ratio equal to or greater than 1.5:1, are X-ray amorphous and have an apparent density between 50 and 200 grams/liter. They are made by spray-drying an aluminum orthophosphate solution or suspension containing P 2 O 5 and Al 2 O 3 in the molar ratio desired in the final product, in a spray tower at temperatures higher thana 250°C to effect direct transformation into condensed aluminum phosphates.
Inventors
- 👤 Horst-Dieter Wasel-Nielen
- 👤 Gero Heymer
- 👤 Peter Wirtz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 19:57
CPC Classifications
C; C01; C01B; C01B25/00; C01B25/16; C01B25/26; C01B25/38; C04; C04B; C04B22/00; C04B22/08; C04B22/16
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
115 words
A process for spray-drying solutions or suspensions of aluminium orthophosphates containing P 2 O 5 and Al 2 O 3 in a molar ratio equal to or greater than 1.5:1 in a spraying tower at elevated temperatures which comprises spraying the said solutions or suspensions through a flame zone, the temperatures within the said spraying tower being between 300° and 600°C and off-gases escaping from the said tower having temperatures between 100° and 500°C with the resultant formation of condensed aluminium phosphates containing P 2 O 5 and Al 2 O 3 in a molar ratio equal to or greater than 1.5:1, being X-ray amorphous and having an apparent density between 50 and 200 grams/liter.
Claim 2
Dependent Claim
115 words
A process for spray-drying solutions or suspensions of aluminium orthophosphates containing P 2 O 5 and Al 2 O 3 in a molar ratio equal to or greater than 1.5:1 in a spraying tower at elevated temperatures which comprises spraying the said solutions or suspensions through a flame zone, the temperatures within the said spraying tower being between 300° and 600°C and off-gases escaping from the said tower having temperatures between 100° and 500°C with the resultant formation of condensed aluminium phosphates containing P 2 O 5 and Al 2 O 3 in a molar ratio equal to or greater than 1.5:1, being X-ray amorphous and having an apparent density between 50 and 200 grams/liter.
Claim 3
Dependent Claim
31 words
The process as claimed in claim 1, which comprises producing quick-setting condensed aluminium phosphate hardeners for water-glass cements by spray-drying the said solutions or suspensions at temperatures between 300° and 400°C.
Claim 4
Dependent Claim
31 words
The process as claimed in claim 1, which comprises producing slow-setting condensed aluminium phosphate hardeners for water-glass cements by spray-drying the said solutions for suspensions at temperatures between 400° and 600°C.
Claim 5
Dependent Claim
105 words
The process as claimed in claim 1, which comprises producing condensed aluminium phosphate hardeners for water-glass cements, which cause setting of the cements within a period of 10 to 50 minutes, by spray-drying the said solutions or suspensions at temperatures between 300° and 400°C and annealing the resulting spray-dried product for a period between 10 and 60 minutes at temperatures between 400° and 600°C, the annealing temperature being the higher within the limits specified the longer the setting time targeted within the limits specified, and the annealing time being the shorter within the limits specified the shorter the setting time targeted within the limits specified.
References Cited (Backward Citations)
CA504832A
Cited
US2898189A
Cited
GB995096A
Cited
DE1467061A1
Cited
US3445257A
Cited
US3607019A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-09 | 1979-09-08 | 1980-03-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-09 | 1983-09-08 | 1984-03-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-09 | 1987-09-08 | 1988-03-09 | $7700.00 | Window Closed / Lapsed |