Method of manufacturing acrylic fibers
Assignee: Kanegafuchi Chemical Industry Co Ltd
•
Filing: 1974-06-14
•
Granted: 1976-03-09
•
Expires: 1994-06-14
Abstract
Abstract A method of manufacturing acrylic fibers free from delustering in boiling water, comprises the steps of forming a spinning solution by dissolving in a solvent of Aceton et al, (a) a copolymer consisting of (1) 30 - 80% acrylonitril and (2) 70 - 20% vinyl chloride or vinylidenechloride, or (b) a tripolymer consisting of (1), (2) and (3) 3.0% or less by weight of ethylenically unsaturated monomer having hydrophilic radicals, and adding one or more compound selected from the group of (1) homopolymer or copolymer of glycidyl methacrylate and (2) specific organic tin compounds, and spinning said spinning solution into a first bath consisting of 60% or less said organic solvent-water and leading said yarn in a 2nd bath consisting of 61 - 85% said organic solvent-water and then in a 3rd and more bath consisting of less than 60% said organic solvent-water and drying, drawing out and annealing said yarn by ordinary methods.
Inventors
- 👤 Ko Kozuka
- 👤 Shunichiro Kurioka
- 👤 Taizo Yasumoto
- 👤 Shigeru Kobayashi
- 👤 Atsuo Kubota
- 👤 Nobumasa Otoshi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:53
CPC Classifications
C; C08; C08L; C08L33/00; C08L33/18; C08L33/20; C08K; C08K5/00; C08K5/56; C08K5/57; C08L33/04; C08L33/14; D; D01; D01F; D01F6/00; D01F6/44; D01F6/54
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
314 words
Method of manufacturing modacrylic fibers comprising the steps of A. dissolving in an organic solvent selected from the group consisting of acetone, acetonitrile, dimethylformamide and mixtures thereof a copolymer consisting essential of a. 30 to 80 weight percent acrylonitrile, b. 70 to 20 weight percent vinyl chloride or vinylidene chloride, and c. 0 to 3 weight percent ethylenically unsaturated monomers having a hydrophillic group and selected from the group consisting of sodium sulfopropyl methacrylate, sodium parastyrene sulfonate, sodium methacryloxybenzene sulfonate, sodium allyl sulfonate, sodium methallyl sulfonate, sodium acrylate, sodium itaconate and mixtures thereof, said copolymer being in a concentration of from 18 to 25%; B. adding 0.2 to 30.0 weight percent based on the weight of said copolymer of a homopolymer of glycidyl methacrylate or a copolymer consisting essentially of 30 weight percent or more of glycidyl methacrylate polymerized with one or more ethylenically unsaturated monomer selected from the group consisting of methyl acrylate, methyl methacrylate, acrylonitrile, vinyl acetate, vinyl chloride, vinylidene chloride, styrene, vinyl pyrrolidone and the like in an amount of 70 weight percent or less, wherein the specific viscosity of said homopolymer or copolymer of glycidyl methacrylate is from 0.01 to 0.50 as measured at 30°C in 2.0 to 4.0 g/l acetone solution; C. spinning the resulting spinning solution in at least first and second baths comprising one or more said solvents in concentrations of less than 60 weight percent and 61 to 85 weight percent respectively; D. leading the thus obtained coagulated filaments successively through one or more subsequent baths containing 60 weight percent or less of said solvent thereby to remove said solvent and to wash said filaments; E. drying said filaments at about 100° to 135°C; F. stretching said filaments 2 to 4 times its length at a temperature of about 100° to 135°C; and G. heat treating said filaments at a temperature of about 135° to 155°C.
Claim 2
Dependent Claim
314 words
Method of manufacturing modacrylic fibers comprising the steps of A. dissolving in an organic solvent selected from the group consisting of acetone, acetonitrile, dimethylformamide and mixtures thereof a copolymer consisting essential of a. 30 to 80 weight percent acrylonitrile, b. 70 to 20 weight percent vinyl chloride or vinylidene chloride, and c. 0 to 3 weight percent ethylenically unsaturated monomers having a hydrophillic group and selected from the group consisting of sodium sulfopropyl methacrylate, sodium parastyrene sulfonate, sodium methacryloxybenzene sulfonate, sodium allyl sulfonate, sodium methallyl sulfonate, sodium acrylate, sodium itaconate and mixtures thereof, said copolymer being in a concentration of from 18 to 25%; B. adding 0.2 to 30.0 weight percent based on the weight of said copolymer of a homopolymer of glycidyl methacrylate or a copolymer consisting essentially of 30 weight percent or more of glycidyl methacrylate polymerized with one or more ethylenically unsaturated monomer selected from the group consisting of methyl acrylate, methyl methacrylate, acrylonitrile, vinyl acetate, vinyl chloride, vinylidene chloride, styrene, vinyl pyrrolidone and the like in an amount of 70 weight percent or less, wherein the specific viscosity of said homopolymer or copolymer of glycidyl methacrylate is from 0.01 to 0.50 as measured at 30°C in 2.0 to 4.0 g/l acetone solution; C. spinning the resulting spinning solution in at least first and second baths comprising one or more said solvents in concentrations of less than 60 weight percent and 61 to 85 weight percent respectively; D. leading the thus obtained coagulated filaments successively through one or more subsequent baths containing 60 weight percent or less of said solvent thereby to remove said solvent and to wash said filaments; E. drying said filaments at about 100° to 135°C; F. stretching said filaments 2 to 4 times its length at a temperature of about 100° to 135°C; and G. heat treating said filaments at a temperature of about 135° to 155°C.
Claim 3
Dependent Claim
37 words
Method of claim 1, wherein said one or more subsequent baths comprise a third bath having a solvent concentration of about 60%, and one or more baths subsequent thereto having concentrations of solvents in successively lower amounts.
Claim 4
Dependent Claim
31 words
Method of claim 1, wherein said homopolymer or copolymer of glycidyl methacrylate is added in an amount of from 0.5 to 5.0 weight percent based on the weight of said copolymer.
Claim 5
Dependent Claim
39 words
Method of claim 1, wherein said filaments are dried at a temperature of between 110°C and 125°C, stretched at about 250 to 300 percent, and heat treated at a temperature of about 140°C to 150°C for about 5 minutes.
Claim 6
Dependent Claim
39 words
Method of claim 1, wherein the concentration of said solvent in said first bath is from 10 to 50 weight percent and wherein the concentration of said solvent in said second bath is from 63 to 85 weight percent.
Claim 7
Dependent Claim
42 words
Method of claim 5, wherein said third and a fourth bath are used, said third bath having said solvent concentration of from 20 to 55 weight percent and said fourth bath having said solvent concentration of from 10 to 30 weight percent.
Claim 8
Dependent Claim
35 words
Method of claim 1, wherein said copolymer of glycidyl methacrylate consists essentially of 50 weight percent or more of glycidyl methacrylate and 50 weight percent or less of said one or more ethylenically unsaturated monomer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-09 | 1979-09-08 | 1980-03-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-09 | 1983-09-08 | 1984-03-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-09 | 1987-09-08 | 1988-03-09 | $7700.00 | Window Closed / Lapsed |