Water-soluble coating composition and method for making same
Assignee: Individual
•
Filing: 1974-02-27
•
Granted: 1976-03-09
•
Expires: 1994-02-27
Abstract
Abstract A method is described for preparation of an adduct product for use as a binder medium for paints to be applied by electrodeposition. This product is the adduct resulting from the solution of a solid polycycloalkadiene polymer having a molecular weight of 700-800 in a liquid polyalkadiene polymer of 500-5000 molecular weight after the initiation of the adduct formation reaction by the addition of an unsaturated polycarboxylic acid or its anhydride. The adduct is formed by adding the acid or anhydride to the solution of the solid polymer in the liquid. The resulting adduct product is suitable for use as a paint binder for electrodeposited paints when diluted with water. The paint composition may be formed by mixing of pigments into the binder and then suspending the mixture in water.
Inventors
- 👤 Charles Schein
- 👤 Jean-Jacques Le Minez
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:10
CPC Classifications
C; C08; C08C; C08C19/00; C08C19/28; C09; C09D; C09D5/00; C09D5/44; C09D5/4403; Y; Y10; Y10S; Y10S524/00; Y10S524/901
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
101 words
A method for the preparation of an addition product binder suitable for a water-soluble coating composition capable of being applied by electrodeposition, wherein at least one solid polycycloalkadiene having a ball and ring melting point of from 70° to 100°C and a molecular weight of from 700 to 800 is dissolved in at least one liquid polyalkadiene conjugated polymer of molecular weight from 500 to 5000 by mixing; this mixture is maintained at a substantially constant temperature and an adduct formation reaction is initiated by the addition of at least one unsaturated polycarboxylic acid or its anhydride to the dissolved mixture.
Claim 2
Independent Claim
101 words
A method for the preparation of an addition product binder suitable for a water-soluble coating composition capable of being applied by electrodeposition, wherein at least one solid polycycloalkadiene having a ball and ring melting point of from 70° to 100°C and a molecular weight of from 700 to 800 is dissolved in at least one liquid polyalkadiene conjugated polymer of molecular weight from 500 to 5000 by mixing; this mixture is maintained at a substantially constant temperature and an adduct formation reaction is initiated by the addition of at least one unsaturated polycarboxylic acid or its anhydride to the dissolved mixture.
Claim 3
Dependent Claim
27 words
The method according to claim 1, wherein the polycarboxylic acid or the anhydride is added to the polycycloalkadiene-polyalkadiene mixture at a temperature of from 170° to 200°C.
Claim 4
Dependent Claim
22 words
The method according to claim 1, wherein the polycarboxylic acid or anhydride is added to the polycycloalkadiene-polyalkadiene mixture with exclusion of air.
Claim 5
Dependent Claim
32 words
The method according to claim 1, wherein to 75 to 90% by weight of the polycycloalkadiene-polyalkadiene mixture are added to from 25 to 10% by weight of unsaturated polycarboxylic acid or anhydride.
Claim 6
Dependent Claim
39 words
A method according to claim 1, characterized by the fact that, after the polycarboxylic acid or anhydride has been added, cooling is carried out, and then the resulting addition product is dissolved in at least one water miscible solvent.
Claim 7
Dependent Claim
27 words
The method according to claim 5, wherein after the addition product has been dissolved, the solution is neutralized by the use of at least one nitrogenized base.
Claim 8
Dependent Claim
24 words
The method according to claim 1, wherein the solid polycycloalkadiene is dissolved in at least one liquid polyalkadiene without carboxyl and hydroxyl terminal radicals.
Claim 9
Dependent Claim
26 words
The method according to claim 7, wherein the polyalkadiene without carboxyl and hydroxyl terminal radicals in a 1-3 polybutadiene of molecular weight from 1000 to 1500.
Claim 10
Dependent Claim
26 words
The method according to claim 7, wherein the polyalkadiene without carboxyl and hydroxyl terminal radicals is a 1-3 polypentadiene of molecular weight of 500 to 2000.
Claim 11
Dependent Claim
28 words
The method according to claim 1, wherein the solid polycycloalkadiene is dissolved in at least one liquid polyalkadiene comprising at least one polyalkadiene having a hydroxyl terminal radical.
Claim 12
Dependent Claim
60 words
The method according to claim 10, wherein the polyalkadiene having a hydroxyl terminal radical is a polybutadiene having a hydroxyl index less than 20, an iodine index of from 300 to 450 and comprising from 50 to 70% of the 1.4 trans form, from 20 to 60% of the 1.4 cis form, and from 5 to 25% of vinyl form.
Claim 13
Dependent Claim
27 words
A method according to claim 1, wherein the solid polycycloalkadiene is dissolved in at least one polyalkadiene comprising at least one polyalkadiene having a carboxyl terminal radical.
Claim 14
Dependent Claim
60 words
The method according to claim 12, wherein the polyalkadiene having a carboxyl terminal radical is a polybutadiene having a percentage of carboxyl of from 1 to 5, a molecular weight of from 1500 to 5000, and possessing 50 to 70% of 1,4 trans form, from 20 to 60% of 1,4 cis form, and from 5 to 25% of vinyl form.
Claim 15
Independent Claim
31 words
The method according to claims 1 wherein the mixture of polyalkadienes and polycycloalkadienes comprises from 60 to 95% by weight of polyalkadienes and from 40 to 5% by weight of polycycloalkadienes.
Claim 16
Dependent Claim
55 words
The method according to claim 1 wherein the mixture of polyalkadienes and polycycloalkadienes comprises 45 to 15% by weight of polyalkadiene having a carboxyl radical or of polyalkadiene having hydroxyl radical, from 50 to 70% by weight of polyalkadiene having no hydroxyl and carboxyl terminal radicals and from 40 to 5% by weight of polycycloalkadiene.
Claim 17
Dependent Claim
59 words
The method according to claim 1 wherein the mixture of polyalkadienes and polycycloalkadienes comprises 45 to 15% of polyakadiene having carboxyl terminal radical, from 45 to 15% by weight of polyalkadiene having a hydroxyl terminal radical, from 50 to 70% by weight of polyalkadiene without carboxyl and hydroxyl terminal radicals, and 40 to 5% by weight of solid polycycloalkadiene.
Claim 18
Dependent Claim
17 words
The method according to claim 1, wherein the unsaturated polycarboxylic acid is maleic acid or fumaric acid.
Claim 19
Dependent Claim
24 words
The method according to claim 1, wherein the liquid polyalkadiene and the solid polycycloalkadiene are mixed at a temperature of from 150° to 220°C.
Claim 20
Dependent Claim
49 words
The method according to claim 1 wherein the mixture of polyalkadienes and polycycloalkadienes comprises from 50 to 70% by weight of polyalkadiene having a carboxyl terminal radical, 45 to 15% by weight of polyalkadiene having a hydroxyl terminal radical, and 40 to 5% by weight of solid polycyclo alkadiene.
Claim 21
Dependent Claim
11 words
The coating composition prepared according to the method of claim 1.
Claim 22
Dependent Claim
53 words
An adduct product formed from the reaction initiated by the addition of an ethylenically unsaturated polycarboxylic acid or its anhydride to a solution of a solid polycycloalkadiene polymer of ball and ring melting point of 70°-100°C and molecular weight of 700 to 800, in a liquid polyalkadiene conjugated polymer of 500-5000 molecular weight.
Claim 23
Dependent Claim
53 words
An adduct product formed from the reaction initiated by the addition of an ethylenically unsaturated polycarboxylic acid or its anhydride to a solution of a solid polycycloalkadiene polymer of ball and ring melting point of 70°-100°C and molecular weight of 700 to 800, in a liquid polyalkadiene conjugated polymer of 500-5000 molecular weight.
Claim 24
Dependent Claim
17 words
A paint binder comprising the adduct of claim 21 at least partially neutralized by a nitrogenous base.
Claim 25
Dependent Claim
19 words
A paint for application by electrodeposition comprising the paint binder of claim 22, and including pigments and deionized water.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-09 | 1979-09-08 | 1980-03-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-09 | 1983-09-08 | 1984-03-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-09 | 1987-09-08 | 1988-03-09 | $7700.00 | Window Closed / Lapsed |