Process for preparing a sulfite modified melamine resin solution
Assignee: Evonik Operations GmbH
•
Filing: 1974-04-17
•
Granted: 1976-03-02
•
Expires: 1994-04-17
Abstract
Abstract The aqueous melamine resin solutions prepared according to the process of U.S. Pat. No. 2,730,516 by sequential condensation of a sulfite bearing, aqueous solution of melamine and formaldehyde at alkaline and acid pH and subsequent neutralization is stabilized by preliminary condensation of the melamine and formaldehyde prior to addition of the sulfite and by refluxing the ultimate condensation mixture at pH 8.5 for 1 hour or more. Concrete mixtures prepared with the stabilized resin solutions cure more rapidly.
Inventors
- 👤 Alois Aignesberger
- 👤 Paul Bornmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 15:07
CPC Classifications
C; C04; C04B; C04B24/00; C04B24/16; C04B24/20; C04B24/22; C08; C08G; C08G12/00; C08G12/02; C08G12/40
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
109 words
In a process for preparing a solution of sulfite modified melamine resin, wherein melamine is dissolved in aqueous formaldehyde solution at elevated temperature, the clear solution so formed is cooled, an alkali metal sulfite is dissolved in the cooled solution, the resulting sulfite bearing solution is adjusted to a pH value above 7, heated, again cooled, acidified, and heated to cause formation of said resin by condensation, and the condensation mixture obtained is adjusted to a pH value above 7, the improvement which comprises heating said condensation mixture at pH 8 to 11 for 1 to 3 hours at a temperature at which said mixture refluxes at atmospheric pressure.
Claim 2
Dependent Claim
109 words
In a process for preparing a solution of sulfite modified melamine resin, wherein melamine is dissolved in aqueous formaldehyde solution at elevated temperature, the clear solution so formed is cooled, an alkali metal sulfite is dissolved in the cooled solution, the resulting sulfite bearing solution is adjusted to a pH value above 7, heated, again cooled, acidified, and heated to cause formation of said resin by condensation, and the condensation mixture obtained is adjusted to a pH value above 7, the improvement which comprises heating said condensation mixture at pH 8 to 11 for 1 to 3 hours at a temperature at which said mixture refluxes at atmospheric pressure.
Claim 3
Dependent Claim
34 words
In a process as set forth in claim 1, said clear solution being held at a pH of 3.5 to 5 for 20 to 100 minutes at 75° to 85°C prior to said cooling.
Claim 4
Dependent Claim
39 words
In a process as set forth in claim 2, said clear solution being held at a pH of 4.5 for said 20 to 100 minutes, and the pH of said condensation mixture during said heating thereof being approximately 8.5.
Claim 5
Dependent Claim
46 words
In a process as set forth in claim 1, the respective amounts of said melamine, said formaldehyde, and said alkali metal sulfite being such that said sulfite bearing solution contains 2.5 to 3 gram-moles formaldehyde and 0.8 to 1.2 gram-atom sulfur as sulfite per gram-mole melamine.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-02 | 1979-09-01 | 1980-03-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-02 | 1983-09-01 | 1984-03-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-02 | 1987-09-01 | 1988-03-02 | $7700.00 | Window Closed / Lapsed |