Method for making ferrous metal having improved resistances to corrosion at elevated temperatures and to oxidization
Assignee: Mazda Motor Corp
•
Filing: 1974-06-06
•
Granted: 1976-03-02
•
Expires: 1994-06-06
Abstract
Abstract A method for making ferrous metal having highly improved resistances to corrosion and to oxidization, which comprises hot-dipping a metallic workpiece in a molten aluminum or aluminum alloy bath, primary heat-treatment of the metallic workpiece and secondary heat-treatment of the metallic workpiece. During the primary heat-treatment, an intermetallic compound layer is formed over the surface of the metallic workpiece, which is developed into an alloy layer during the secondary heat-treatment to make the alloy layer firmly secured to the base of the workpiece. The secondary heat-treatment may be omitted depending on the application of the ferrous metal processed by this method.This is a division of application Ser. No. 305,558, filed Nov. 10, 1972.
Inventors
- 👤 Takao Sasame
- 👤 Toshio Yagi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:39
CPC Classifications
C; C23; C23C; C23C2/00; C23C2/26; C23C2/04; C23C2/12; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/923; Y10S428/924; Y10S428/926; Y10S428/9335; Y10S428/939; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12736; Y10T428/1275; Y10T428/12757
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
125 words
A method for making ferrous metal having highly improved resistance to corrosion and oxidization, which comprises dipping a ferrous workpiece in a molten metal bath containing an aluminum alloy, which aluminum alloy contains chromium in an amount of 1 to 10 percent by weight based on the total weight of said aluminum alloy, and having a temperature of from 750° to 930° C, for from 30 to 300 seconds, and heating the resultant ferrous workpiece for at least 30 minutes at an elevated temperature of from 700° to 930° C, thereby forming an intermetallic compound layer uniformly over the surface of said ferrous workpiece, said intermetallic compound layer containing iron and aluminum as its principle components and having a surface portion containing an aluminum-chromium compound.
Claim 2
Independent Claim
125 words
A method for making ferrous metal having highly improved resistance to corrosion and oxidization, which comprises dipping a ferrous workpiece in a molten metal bath containing an aluminum alloy, which aluminum alloy contains chromium in an amount of 1 to 10 percent by weight based on the total weight of said aluminum alloy, and having a temperature of from 750° to 930° C, for from 30 to 300 seconds, and heating the resultant ferrous workpiece for at least 30 minutes at an elevated temperature of from 700° to 930° C, thereby forming an intermetallic compound layer uniformly over the surface of said ferrous workpiece, said intermetallic compound layer containing iron and aluminum as its principle components and having a surface portion containing an aluminum-chromium compound.
Claim 3
Dependent Claim
19 words
A method as claimed in claim 1, wherein said intermetallic compound layer is 50 to 200 microns in depth.
Claim 4
Dependent Claim
22 words
A method as claimed in claim 1, wherein said heating is effected for a period of time not more than 3 hours.
Claim 5
Dependent Claim
68 words
A ferrous workpiece prepared according to the method of claim 1, having a surface portion formed with an intermetallic compound layer having relatively high resistance to corrosion and oxidation, said intermetallic compound layer being 50 to 200 microns in depth and containing aluminum and iron as its principle components and having a surface portion containing an aluminum-chromium compound, said aluminum being uniformly distributed in said intermetallic compound layer.
References Cited (Backward Citations)
US1409017A
Cited
FR714928A
Cited
US2197622A
Cited
FR983726A
Cited
US2625495A
Cited
US2824020A
Cited
US2917818A
Cited
US2955958A
Cited
US3027269A
Cited
FR1391659A
Cited
US3467545A
Cited
US3287159A
Cited
US3567409A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-02 | 1979-09-01 | 1980-03-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-02 | 1983-09-01 | 1984-03-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-02 | 1987-09-01 | 1988-03-02 | $7700.00 | Window Closed / Lapsed |