Fireproof inorganic protective coating and the method of its production
Assignee: Silesian University of Technology
•
Filing: 1974-04-19
•
Granted: 1976-02-24
•
Expires: 1994-04-19
Abstract
Abstract An inorganic fireproof protective coating composition consisting of 5 to 15 percent by weight of a powdered silicate-oxide sinter or alloy, 15 to 35 percent by weight of an anhydrous powdered alumosilicate substance, and 50 to 80 percent of the acid phosphates of aluminum, chromium, magnesium or calcium, or mixtures thereof. All three ingredients of the coating form a suspensoid upon mixing and thereafter they are subjected to self-hardening at room temperature. The hardening process may be accelerated by heating up to 150 DEG C. The coating is designed for protection of products made of readily inflammable materials, particularly of wood and of wood-like materials, against destruction by fire or glow.
Inventors
- 👤 Adam Gierek
- 👤 Stanislaw Pawlowski
- 👤 Boleslaw Formanek
- 👤 Eugeniusz Piesiur
- 👤 Grzegorz Pucka
- 👤 Bogdan Blachnicki
- 👤 Jerzy Rychlewski
- 👤 Janusz Gajda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 03:28
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/18; C09D1/00; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
247 words
A fireproof inorganic protective air hardenable coating mixture comprising (A) 5 to 15 percent by weight of a silicate oxide sinter or alloy comprising 50 to 65 percent by weight of Fe 2 O 3 plus FeO in any weight proportion, 3 to 8 percent of CuO plus CuO 2 in any weight proportion, 2 to 7 percent by weight of CaO, 20 to 30 percent by weight of SiO 2 , and 0 to 10 percent of other oxides selected from the group consisting of Al 2 O 3 , TiO 2 , NiO, CoO, MgO, Na 2 O and K 2 O in any weight proportion; (B) 15 to 35 percent by weight of an anhydrous aluminosilicate substance either in the natural state or sintered at a temperature above 1,000°C, said substance comprising 40 to 75 percent by weight of SiO 2 , 10 to 45 percent by weight of Al 2 O 3 , 0 to 15 percent by weight of Fe 2 O 3 plus FeO in any weight proportion, and 0 to 10 percent by weight of other oxides selected from the group consisting of TiO 2 , CaO, MgO, Na 2 O and K 2 O in any weight proportions, and (C) 50 to 80 percent by weight of an acid solution of mono- or dibasic phosphates of aluminum, chromium, magnesium or calcium, or of their mixtures in any weight proportion, said acid solution having a density of 1.3 to 1.6g/cc.
Claim 2
Dependent Claim
247 words
A fireproof inorganic protective air hardenable coating mixture comprising (A) 5 to 15 percent by weight of a silicate oxide sinter or alloy comprising 50 to 65 percent by weight of Fe 2 O 3 plus FeO in any weight proportion, 3 to 8 percent of CuO plus CuO 2 in any weight proportion, 2 to 7 percent by weight of CaO, 20 to 30 percent by weight of SiO 2 , and 0 to 10 percent of other oxides selected from the group consisting of Al 2 O 3 , TiO 2 , NiO, CoO, MgO, Na 2 O and K 2 O in any weight proportion; (B) 15 to 35 percent by weight of an anhydrous aluminosilicate substance either in the natural state or sintered at a temperature above 1,000°C, said substance comprising 40 to 75 percent by weight of SiO 2 , 10 to 45 percent by weight of Al 2 O 3 , 0 to 15 percent by weight of Fe 2 O 3 plus FeO in any weight proportion, and 0 to 10 percent by weight of other oxides selected from the group consisting of TiO 2 , CaO, MgO, Na 2 O and K 2 O in any weight proportions, and (C) 50 to 80 percent by weight of an acid solution of mono- or dibasic phosphates of aluminum, chromium, magnesium or calcium, or of their mixtures in any weight proportion, said acid solution having a density of 1.3 to 1.6g/cc.
Claim 3
Independent Claim
295 words
A method of producing a coated substrate comprising grinding to a grain size smaller than 0.5 mm (A) 5 to 15 percent by weight of a silicate oxide sinter or alloy comprising 50 to 65 percent by weight of Fe 2 O 3 plus FeO in any weight proportion, 3 to 8 percent of CuO plus CuO 2 in any weight proportion, 2 to 7 percent by weight of CaO, 20 to 30 percent by weight of SiO 2 , and 0 to 10 percent of other oxides selected from the group consisting of Al 2 O 3 , TiO, NiO, CoO, MgO, Na 2 O and K 2 O in any weight proportion and (B) 15 to 35 percent by weight of an anhydrous aluminosilicate substance in the natural state or which has been sintered at a temperature above 1,000°C, and said substance comprising 40 to 75 percent by weight of SiO 2 , 10 to 45 percent by weight of Al 2 O 3 , 0 to 15 percent by weight of Fe 2 O 3 plus FeO in any weight proportion, and 0 to 10 percent by weight of other oxides selected from the group consisting of TiO 2 , CaO, MgO, Na 2 O and K 2 O in any weight proportion; mixing the ground material in a water solution of mono- or dibasic acid phosphates of aluminum, chromium, magnesium, or calcium or a mixture of said acid phosphates, the solution of acid phosphate having a density of 1.3 to 1.6 g/cc, and forming a suspensoid of said ground material in the solution; applying a coating of the suspensoid to the surface of a substrate and hardening the coating in air at a temperature from room temperature up to about 150°C.
Claim 4
Independent Claim
295 words
A method of producing a coated substrate comprising grinding to a grain size smaller than 0.5 mm (A) 5 to 15 percent by weight of a silicate oxide sinter or alloy comprising 50 to 65 percent by weight of Fe 2 O 3 plus FeO in any weight proportion, 3 to 8 percent of CuO plus CuO 2 in any weight proportion, 2 to 7 percent by weight of CaO, 20 to 30 percent by weight of SiO 2 , and 0 to 10 percent of other oxides selected from the group consisting of Al 2 O 3 , TiO, NiO, CoO, MgO, Na 2 O and K 2 O in any weight proportion and (B) 15 to 35 percent by weight of an anhydrous aluminosilicate substance in the natural state or which has been sintered at a temperature above 1,000°C, and said substance comprising 40 to 75 percent by weight of SiO 2 , 10 to 45 percent by weight of Al 2 O 3 , 0 to 15 percent by weight of Fe 2 O 3 plus FeO in any weight proportion, and 0 to 10 percent by weight of other oxides selected from the group consisting of TiO 2 , CaO, MgO, Na 2 O and K 2 O in any weight proportion; mixing the ground material in a water solution of mono- or dibasic acid phosphates of aluminum, chromium, magnesium, or calcium or a mixture of said acid phosphates, the solution of acid phosphate having a density of 1.3 to 1.6 g/cc, and forming a suspensoid of said ground material in the solution; applying a coating of the suspensoid to the surface of a substrate and hardening the coating in air at a temperature from room temperature up to about 150°C.
Claim 5
Dependent Claim
18 words
The method according to claim 2 comprising grinding (A) and (B) to a grain size smaller than 0.1mm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-23 | 1979-08-25 | 1980-02-24 | $2000.00 | Window Closed / Lapsed |