Coating and combined sizing and coating composition for glass fibers
Assignee: PPG Industries Inc
•
Filing: 1974-05-06
•
Granted: 1976-02-24
•
Expires: 1994-05-06
Abstract
Abstract Individual glass fibers are coated with a combined sizing and coating composition that includes a zinc salt having a solubility constant (K s ) of not less than 1 × 10 - 3 complexed with ammonia as a substitute for all or part of the resorcinol-formaldehyde resin. The preferred combined sizing and coating composition includes as the latex constituent, a styrene-butadiene vinylpyridine terpolymer, as the resin constituent, resorcinol-formaldehyde and zinc sulphate complexed with ammonia and as the coupling agent, a silane selected from amino, amido, chloropropyl, epoxy, ureido-functional silanes. An aqueous solution of the combined sizing and coating composition is prepared and the individual glass fibers are coated shortly after attenuation with this combined sizing and coating composition. The coated individual glass fibers are thereafter gathered into strands and the strands are dried while spaced from each other. The dried strands are thereafter, collected on a forming tube. The coated strands are used as a glass fiber reinforcement for elastomeric products. The zinc salts complexed with ammonia, may also be used in a coating composition for use with glass fibers that have been previously coated with a separate sizing composition that includes a coupling agent.
Inventors
- 👤 Dennis M. Fahey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:25
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/04; C08J5/06; C08J5/08; B; B60; B60B; B60B5/00; B60B5/02; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/26; C03C25/27; C08J2321/00; Y; Y10; Y10S; Y10S524/00; Y10S524/925; Y10S524/926; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938; Y10T428/294; Y10T428/2958; Y10T428/2962; Y10T428/2964
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
103 words
In a glass fiber coating composition useful in preparing glass fibers for reinforcing elastomers comprising an aqueous dispersion of an elastomeric latex selected from the group consisting of natural and synthetic rubber latices and a rubber adhesive, the improvement comprising, as said adhesive, a zinc salt in an amount from 0.01 to 5 percent by weight based on the total weight of the coating composition, said zinc salt being capable of being complexed with ammonia and having a solubility constant of not less than 1 × 10.sup. -3 ; and having present in the dispersion sufficient ammonia for complexing the zinc salt present.
Claim 2
Dependent Claim
103 words
In a glass fiber coating composition useful in preparing glass fibers for reinforcing elastomers comprising an aqueous dispersion of an elastomeric latex selected from the group consisting of natural and synthetic rubber latices and a rubber adhesive, the improvement comprising, as said adhesive, a zinc salt in an amount from 0.01 to 5 percent by weight based on the total weight of the coating composition, said zinc salt being capable of being complexed with ammonia and having a solubility constant of not less than 1 × 10.sup. -3 ; and having present in the dispersion sufficient ammonia for complexing the zinc salt present.
Claim 3
Dependent Claim
13 words
The composition of claim 1 wherein said dispersion also contains a resorcinol-formaldehyde resin.
Claim 4
Dependent Claim
25 words
The composition of claim 1 wherein said zinc salt is selected from the group consisting of zinc sulphate, zinc phosphate, zinc nitrate and zinc chloride.
Claim 5
Dependent Claim
13 words
The composition of claim 4 wherein said aminofunctional silane coupling agent is gamma-aminopropyltriethoxysilane.
Claim 6
Dependent Claim
13 words
The composition of claim 4 wherein said elastomeric latex is a styrene-butadiene-vinylpyridine terpolymer.
Claim 7
Dependent Claim
106 words
In a coating composition for coating glass fibers, said glass fibers useful in reinforcing elastomeric materials, comprising an aqueous dispersion containing an elastomeric latex selected from the group consisting of natural and synthetic rubber latices and a rubber adhesive having furfuryl alcohol therein, the improvement comprising, as said adhesive, in an amount of 0.01 to 5 percent by weight based on the total weight of the coating composition, said zinc salt being capable of being complexed with ammonia and having a solubility constant of not less than 1 × 10.sup. -3 ; and having present in the dispersion sufficient ammonia for complexing the zinc salt present.
Claim 8
Dependent Claim
106 words
In a coating composition for coating glass fibers, said glass fibers useful in reinforcing elastomeric materials, comprising an aqueous dispersion containing an elastomeric latex selected from the group consisting of natural and synthetic rubber latices and a rubber adhesive having furfuryl alcohol therein, the improvement comprising, as said adhesive, in an amount of 0.01 to 5 percent by weight based on the total weight of the coating composition, said zinc salt being capable of being complexed with ammonia and having a solubility constant of not less than 1 × 10.sup. -3 ; and having present in the dispersion sufficient ammonia for complexing the zinc salt present.
Claim 9
Dependent Claim
118 words
In a coating composition for coating glass fibers comprising an aqueous dispersion containing an elastomeric latex selected from the group consisting of natural and synthetic rubber latices, a silane coupling agent selected from the group consisting of amino, amido, epoxy, chloropropyl and ureido-functional silanes and a rubber adhesive containing furfuryl alcohol, the improvement comprising, as the rubber adhesive, a zinc salt in an amount of 0.01 to 5 percent by weight based on the total weight of the coating composition, said zinc salt being capable of being complexed with ammonia and having a solubility constant of not less than 1 × 10.sup. -3 ; and having present in the dispersion sufficient ammonia to complex the zinc salt present.
Claim 10
Dependent Claim
118 words
In a coating composition for coating glass fibers comprising an aqueous dispersion containing an elastomeric latex selected from the group consisting of natural and synthetic rubber latices, a silane coupling agent selected from the group consisting of amino, amido, epoxy, chloropropyl and ureido-functional silanes and a rubber adhesive containing furfuryl alcohol, the improvement comprising, as the rubber adhesive, a zinc salt in an amount of 0.01 to 5 percent by weight based on the total weight of the coating composition, said zinc salt being capable of being complexed with ammonia and having a solubility constant of not less than 1 × 10.sup. -3 ; and having present in the dispersion sufficient ammonia to complex the zinc salt present.
Claim 11
Dependent Claim
69 words
In a glass fiber composition suitable for use in reinforcing elastomeric materials comprising glass fibers having a coating thereon comprising a natural or synthetic rubber the improvement comprising said coating containing a zinc salt, said salt being present in an amount of 0.014 to 20 percent by weight based on the weight of the coating and having a solubility constant of not less than 1 × 10.sup. -3 .
Claim 12
Dependent Claim
69 words
In a glass fiber composition suitable for use in reinforcing elastomeric materials comprising glass fibers having a coating thereon comprising a natural or synthetic rubber the improvement comprising said coating containing a zinc salt, said salt being present in an amount of 0.014 to 20 percent by weight based on the weight of the coating and having a solubility constant of not less than 1 × 10.sup. -3 .
Claim 13
Dependent Claim
23 words
The composition of claim 8 wherein the glass fiber composition is present in a strand containing a plurality of said coated glass fibers.
Claim 14
Dependent Claim
71 words
In a glass fiber composition suitable for use in reinforcing elastomeric materials, comprising: glass fibers having a coating thereon comprising a natural or synthetic rubber and a silane coupling agent, the improvement comprising said composition containing a zinc salt, said zinc salt being present in an amount of 0.01 to 5 percent by weight of the coating and having a solubility constant of not less than 1 × 10.sup. -3 .
Claim 15
Dependent Claim
71 words
In a glass fiber composition suitable for use in reinforcing elastomeric materials, comprising: glass fibers having a coating thereon comprising a natural or synthetic rubber and a silane coupling agent, the improvement comprising said composition containing a zinc salt, said zinc salt being present in an amount of 0.01 to 5 percent by weight of the coating and having a solubility constant of not less than 1 × 10.sup. -3 .
Claim 16
Dependent Claim
23 words
The composition of claim 10 wherein the glass fiber composition is present in a strand containing a plurality of said coated glass fibers.
Claim 17
Dependent Claim
114 words
In a coating composition for coating glass fibers comprising an aqueous dispersion containing an elastomeric latex selected from the group consisting of natural and synthetic rubber latices, a silane coupling agent selected from the group consisting of amino, amido, epoxy, chloropropyl, and ureido-functional silanes and a rubber adhesive, the improvement comprising, as said adhesive, a zinc salt in an amount of 0.01 to 5 percent by weight based on the total weight of the coating composition, and being capable of being complexed with ammonia, said zinc salt having a solubility constant of not less than 1 × 10.sup. -3 ; and having present in the dispersion sufficient ammonia for complexing the zinc salt present.
Claim 18
Dependent Claim
114 words
In a coating composition for coating glass fibers comprising an aqueous dispersion containing an elastomeric latex selected from the group consisting of natural and synthetic rubber latices, a silane coupling agent selected from the group consisting of amino, amido, epoxy, chloropropyl, and ureido-functional silanes and a rubber adhesive, the improvement comprising, as said adhesive, a zinc salt in an amount of 0.01 to 5 percent by weight based on the total weight of the coating composition, and being capable of being complexed with ammonia, said zinc salt having a solubility constant of not less than 1 × 10.sup. -3 ; and having present in the dispersion sufficient ammonia for complexing the zinc salt present.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-23 | 1979-08-25 | 1980-02-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-23 | 1983-08-25 | 1984-02-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-23 | 1987-08-25 | 1988-02-24 | $7700.00 | Window Closed / Lapsed |