US3939849A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Filter elements
Assignee: Monsanto Chemicals Ltd
•
Filing: 1974-07-08
•
Granted: 1976-02-24
•
Expires: 1994-07-08
Abstract
Abstract A polyolefin filter for tobacco products and the like was prepared. The extruded element is an open-cell foamed polyethylene or polypropylene having a TPM filtration efficiency greater than 20 percent. The filter rod can be made by extruding polyethylene containing less than 0.2 moles of a volatile blowing agent per 100 grams of resin at a melt temperature between 130 DEG C. and 150 DEG C., the temperature of the die being between 120 DEG C. and 136 DEG C. Higher melt temperature and die temperature are required for polypropylenes.
Inventors
- 👤 Samuel Baxter
- 👤 Pushpkumar Dewanmal Changani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:18
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; A; A24; A24D; A24D3/00; A24D3/06; A24D3/08; C08J2323/00; C08J2323/02; Y; Y10; Y10S; Y10S264/00; Y10S264/05
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
228 words
A rod shaped cigarette filter comprised of a polypropylene foam or a foam of high density polyethylene, said foam having a substantially opencell structure wherein more than half of the cells present contain cell walls which are perforated, and wherein the microstructure of said foam is characterized by the presence of numerous fine fibre-like elements having thicknesses within the range of from about 0.1 to 2 microns which bridge across said perforations in the cell walls, said fibre-like elements being interconnected with each other or with the part of the cell wall that forms the boundary of the perforation and thereby being substantially free of loose ends; said cigarette filter having a TPM filtration efficiency of from 20 to 60 percent, a ΔP 10 of from about 0.5 to 15 centimeters water gauge, and a hardness of from about 50 to 100 percent, said percent hardness being determined by subjecting a 120 millimeter length sample of said cigarette filter rod of predetermined initial diameter to compression under a 300 gram load for 15 seconds and thereafter measuring the rod diameter to determine the decrease in initial diameter, the percent hardness is then calculated from the equation: Percent hardness = [(D - A)/D] × 100 wherein D represents the initial diameter of the rod and A represents the decrease in said initial diameter following 15 seconds under said load.
Claim 2
Dependent Claim
228 words
A rod shaped cigarette filter comprised of a polypropylene foam or a foam of high density polyethylene, said foam having a substantially opencell structure wherein more than half of the cells present contain cell walls which are perforated, and wherein the microstructure of said foam is characterized by the presence of numerous fine fibre-like elements having thicknesses within the range of from about 0.1 to 2 microns which bridge across said perforations in the cell walls, said fibre-like elements being interconnected with each other or with the part of the cell wall that forms the boundary of the perforation and thereby being substantially free of loose ends; said cigarette filter having a TPM filtration efficiency of from 20 to 60 percent, a ΔP 10 of from about 0.5 to 15 centimeters water gauge, and a hardness of from about 50 to 100 percent, said percent hardness being determined by subjecting a 120 millimeter length sample of said cigarette filter rod of predetermined initial diameter to compression under a 300 gram load for 15 seconds and thereafter measuring the rod diameter to determine the decrease in initial diameter, the percent hardness is then calculated from the equation: Percent hardness = [(D - A)/D] × 100 wherein D represents the initial diameter of the rod and A represents the decrease in said initial diameter following 15 seconds under said load.
Claim 3
Dependent Claim
19 words
An extruded rod of substantially open-cell foam as defined in claim 1 which can be cut up into filters.
Claim 4
Dependent Claim
10 words
A cigarette having a filter as defined in claim 1.
Claim 5
Dependent Claim
53 words
A cigarette filter in accordance with claim 1 in which said foam is comprised of a high density polyethylene, wherein said high density polyethylene has a density in the range of from about 0.950 and 0.970 grams per cubic centimeter and a melt index from about 1 to 8 grams per 10 minutes.
Claim 6
Dependent Claim
56 words
A cigarette filter in accordance with claim 1 wherein more than half of the cell walls of said foam each contain a perforation that takes up from about 70 to 95 percent of the total area of the cell wall, giving a reticular structure formed by the boundaries between the remaining parts of said cell wall.
Claim 7
Dependent Claim
42 words
A cigarette filter in accordance with claim 1 wherein the filter has a hardness of from 80 to 100 percent, a ΔP 10 of from 0.5 to 10 centimeters water gauge, and a TPM filtration efficiency of from 30 to 60 percent.
Claim 8
Dependent Claim
20 words
A cigarette filter in accordance with claim 1 in which there are at least 100 fibre-like elements bridging each perforation.
Claim 9
Dependent Claim
45 words
A cigarette filter in accordance with claim 1 in which said foam is comprised of a polypropylene resin having a melt index of from 1 to 12 grams per 10 minutes as measured at a temperature of 190°C. and under a weight of 2.16 kilograms.
Claim 10
Dependent Claim
21 words
A cigarette filter in accordance with claim 1 wherein more than half of the cell walls of said foam are perforated.
Claim 11
Dependent Claim
21 words
A composite filter for a cigarette wherein a portion thereof consists of a rod shaped foam as defined in claim 1.
Claim 12
Dependent Claim
16 words
A composite filter in accordance with claim 10 wherein the rod shaped foam is highdensity polyethylene.
Claim 13
Dependent Claim
11 words
A cigarette having a composite filter as defined in claim 10.
Claim 14
Dependent Claim
203 words
A rod shaped cigarette filter comprised of a polypropylene foam or a foam of high density polyethylene, said foam having a substantially opencell structure wherein more than half of the cells present contain cell walls which are perforated, and wherein the microstructure of said foam is characterized by the presence of two-dimensional webs of interconnected fibre-like elements which extend across said perforations in the cell walls, said interconnected fibre-like elements having thicknesses within the range of from 0.1 to 2 microns; said cigarette filter having a TPM filtration efficiency of from 20 to 60 percent, aΔP 10 of from about 0.5 to 15 centimeters water gauge, and a hardness of from about 50 to 100 percent, said percent hardness being determined by subjecting a 120 millimeter length sample of said cigarette filter rod of predetermined initial diameter to compression for 15 seconds under a 300 gram load and thereafter measuring the rod diameter to determine the resulting decrease in said initial diameter, the percent hardness is then calculated from the equation: Percent hardness = [(D - A)/D] × 100 wherein D represents the initial diameter of the rod and A represents the decrease in said initial diameter following 15 seconds under said load.
Claim 15
Dependent Claim
203 words
A rod shaped cigarette filter comprised of a polypropylene foam or a foam of high density polyethylene, said foam having a substantially opencell structure wherein more than half of the cells present contain cell walls which are perforated, and wherein the microstructure of said foam is characterized by the presence of two-dimensional webs of interconnected fibre-like elements which extend across said perforations in the cell walls, said interconnected fibre-like elements having thicknesses within the range of from 0.1 to 2 microns; said cigarette filter having a TPM filtration efficiency of from 20 to 60 percent, aΔP 10 of from about 0.5 to 15 centimeters water gauge, and a hardness of from about 50 to 100 percent, said percent hardness being determined by subjecting a 120 millimeter length sample of said cigarette filter rod of predetermined initial diameter to compression for 15 seconds under a 300 gram load and thereafter measuring the rod diameter to determine the resulting decrease in said initial diameter, the percent hardness is then calculated from the equation: Percent hardness = [(D - A)/D] × 100 wherein D represents the initial diameter of the rod and A represents the decrease in said initial diameter following 15 seconds under said load.
Claim 16
Dependent Claim
53 words
A cigarette filter in accordance with claim 13 in which said foam is comprised of a high density polyethylene, wherein said high density polyethylene has a density in the range of from about 0.950 and 0.970 grams per cubic centimeter and a melt index from about 1 to 8 grams per 10 minutes.
Claim 17
Dependent Claim
56 words
A cigarette filter in accordance with claim 13 wherein more than half of the cell walls of said foam each contain a perforation that takes up from about 70 to 90 percent of the total area of the cell wall, giving a reticular structure formed by the boundaries between the remaining parts of said cell walls.
Claim 18
Dependent Claim
42 words
A cigarette filter in accordance with claim 13 wherein the filter has a hardness of from 80 to 100 percent, a Δp.sub. 10 of from 0.5 to 10 centimeters water gauge, and a TPM filtration efficiency of from 30 to 60 percent.
Claim 19
Dependent Claim
45 words
A cigarette filter in accordance with claim 13 in which said foam is comprised of a polypropylene resin having a melt index of from 1 to 12 grams per 10 minutes as measured at a temperature of 190°C. and under a weight of 2.16 kilograms.
Claim 20
Dependent Claim
21 words
A cigarette filter in accordance with claim 13 wherein more than half of the cell walls of said foam contain perforations.
References Cited (Backward Citations)
CA865462A
Cited
GB893958A
Cited
GB908185A
Cited
US3884030A
Cited
GB1122661A
Cited
GB1111928A
Cited
GB1279803A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-23 | 1979-08-25 | 1980-02-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-23 | 1983-08-25 | 1984-02-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-23 | 1987-08-25 | 1988-02-24 | $7700.00 | Window Closed / Lapsed |