Process for producing caprolactam
Assignee: Hillyard Chemical Co
•
Filing: 1974-08-09
•
Granted: 1976-02-17
•
Expires: 1994-08-09
Abstract
Abstract A non-catalytic method is provided for depolymerizing nylon-6 to produce e-caprolactam. The nylon, as a melt is continuously fed to a reaction zone together with superheated steam and undecomposed polymer melt is continuously withdrawn from the reaction zone together with steam and polymer decomposition products. Caprolactam is recovered from the polymer decomposition products.
Inventors
- 👤 Frank C. Fowler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:50
CPC Classifications
C; C07; C07D; C07D201/00; C07D201/02; C07D201/12; C08; C08J; C08J11/00; C08J11/04; C08J11/10; C08J11/14; C08J2377/00; C08J2377/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
77 words
A process for producing e-caprolactam from a polymer thereof which comprises continuously introducing into a reaction zone a melt of said polymer, continuously introducing high temperature steam into said reaction zone as the sole depolymerizing agent therein, continuously withdrawing from said reaction zone, steam, polymer degradation products and undecomposed polymer melt, maintaining said reaction zone at a temperature of at least about 600°F. and recovering e-caprolactam from said polymer degradation products as a product of said process.
Claim 2
Dependent Claim
77 words
A process for producing e-caprolactam from a polymer thereof which comprises continuously introducing into a reaction zone a melt of said polymer, continuously introducing high temperature steam into said reaction zone as the sole depolymerizing agent therein, continuously withdrawing from said reaction zone, steam, polymer degradation products and undecomposed polymer melt, maintaining said reaction zone at a temperature of at least about 600°F. and recovering e-caprolactam from said polymer degradation products as a product of said process.
Claim 3
Dependent Claim
56 words
The process of claim 1 wherein said polymer melt is introduced into said reaction zone at a temperature between about 450° and about 600°F. and steam is introduced into said reaction zone at a temperature between about 750° and about 1300°F. and said reaction zone is at an average temperature between about 650° and about 1250°F.
Claim 4
Dependent Claim
32 words
The process of claim 1 wherein said steam is supplied to said reaction zone in an amount between about 2 and about 10 times the weight of the polymer melt supplied thereto.
Claim 5
Dependent Claim
34 words
The process of claim 3 wherein said polymer melt is injected into a stream of said steam and wherein said steam and polymer melt are introduced into said reaction zone as a combined stream.
Claim 6
Dependent Claim
27 words
The process of claim 1 wherein the average residence time of said polymer melt in said reaction zone is from about 1/2 minute to about 10 minutes.
Claim 7
Dependent Claim
21 words
The process of claim 1 wherein at least a portion of said undecomposed polymer melt is recycled to said reaction zone.
Claim 8
Dependent Claim
32 words
The process of claim 6 wherein at least a portion of said polymer degradation products is recycled to said reaction zone after removal of at least a portion of the 3-caprolactam therein.
Claim 9
Dependent Claim
182 words
A process for producing e-caprolactam from a polymer thereof which comprises maintaining a melt of said polymer at a temperature between about 400° and about 600°F., continuously injecting a portion of said melt into a stream of steam heated to between about 750° and about 1000°F. in a weight ratio between about 1/10 to about 1/2 pounds of melt to one pound of steam to produce a combined stream of polymer melt and steam, continuously introducing said combined stream into an elongated reaction zone, said steam being the sole depolymerizing agent in said zone, maintaining said reaction zone at an average temperature between about 650° and about 1250°F., maintaining said polymer melt in said reaction zone for an average residence time between about 1/2 minute and about 10 minutes, continuously withdrawing from said reaction zone, steam, polymer degradation products and undecomposed polymer melt, recovering e-caprolactam from said polymer degradation products and recycling to said reaction zone at least a portion of said undecomposed polymer melt and at least a portion of said polymer degradation products from which said e-caprolactam has been removed.
Claim 10
Dependent Claim
182 words
A process for producing e-caprolactam from a polymer thereof which comprises maintaining a melt of said polymer at a temperature between about 400° and about 600°F., continuously injecting a portion of said melt into a stream of steam heated to between about 750° and about 1000°F. in a weight ratio between about 1/10 to about 1/2 pounds of melt to one pound of steam to produce a combined stream of polymer melt and steam, continuously introducing said combined stream into an elongated reaction zone, said steam being the sole depolymerizing agent in said zone, maintaining said reaction zone at an average temperature between about 650° and about 1250°F., maintaining said polymer melt in said reaction zone for an average residence time between about 1/2 minute and about 10 minutes, continuously withdrawing from said reaction zone, steam, polymer degradation products and undecomposed polymer melt, recovering e-caprolactam from said polymer degradation products and recycling to said reaction zone at least a portion of said undecomposed polymer melt and at least a portion of said polymer degradation products from which said e-caprolactam has been removed.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-16 | 1979-08-18 | 1980-02-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-16 | 1983-08-18 | 1984-02-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-16 | 1987-08-18 | 1988-02-17 | $7700.00 | Window Closed / Lapsed |