Manufacture of silicon nitride powder
Assignee: ZF International UK Ltd
•
Filing: 1972-03-14
•
Granted: 1976-02-10
•
Expires: 1992-03-14
Abstract
Abstract A method of manufacturing a silicon nitride powder comprises heating a bed of silicon powder in a furnace having an atmosphere containing nitrogen so that the silicon reacts with the nitrogen to produce silicon nitride. The exothermic reaction between the silicon and the nitrogen is monitored, either by comparing the temperature in the reaction bed with the temperature at another point in the furnace, or by allowing the nitrogen containing atmosphere to flow through the furnace and measuring the rates of flow of the atmosphere into and out of the furnace. The partial pressure of the nitrogen in the furnace atmosphere is then controlled in accordance with the exothermic reaction so as to ensure that the temperature in the bed does not exceed a predetermined value above which β-phase silicon nitride is formed, the partial pressure of the nitrogen in the furnace being controlled by effecting at least one of the steps of: A. diluting the nitrogen in the furnace atmosphere and, B. evacuating the furnace.
Inventors
- 👤 Roland John Lumby
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:39
CPC Classifications
C; C01; C01B; C01B21/00; C01B21/06; C01B21/068; C01B21/0682; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2004/62; C01P2006/00; C01P2006/10
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
122 words
A method of manufacturing a silicon nitride powder comprising heating a bed containing silicon powder in a furnace having an atmosphere including nitrogen, sensing the temperature in the bed and comparing said temperature with a further temperature at another point in the furnace outside said bed, and controlling the partial pressure of the nitrogen in the furnace atmosphere in accordance with the difference between said temperatures so as to ensure that the temperature in the bed does not exceed a predetermined value above which β-phase silicon nitride is formed, the partial pressure of the nitrogen in the furnace being controlled by effecting at least one of the steps of: a. diluting the nitrogen in the furnace atmosphere and, b. evacuating the furnace.
Claim 2
Independent Claim
122 words
A method of manufacturing a silicon nitride powder comprising heating a bed containing silicon powder in a furnace having an atmosphere including nitrogen, sensing the temperature in the bed and comparing said temperature with a further temperature at another point in the furnace outside said bed, and controlling the partial pressure of the nitrogen in the furnace atmosphere in accordance with the difference between said temperatures so as to ensure that the temperature in the bed does not exceed a predetermined value above which β-phase silicon nitride is formed, the partial pressure of the nitrogen in the furnace being controlled by effecting at least one of the steps of: a. diluting the nitrogen in the furnace atmosphere and, b. evacuating the furnace.
Claim 3
Dependent Claim
21 words
A method as claimed in claim 1, wherein the bed comprises a mixture of silicon powder and α-phase silicon nitride powder.
Claim 4
Dependent Claim
36 words
A method as claimed in claim 2 wherein the mixture of silicon powder and α-phase silicon nitride powder in the bed is arranged to have a tap density of the order of 0.7 grams per c.c.
Claim 5
Dependent Claim
22 words
A method as claimed in claim 2 wherein more than 5% by weight of α-phase silicon nitride is present in the mixture.
Claim 6
Dependent Claim
35 words
A method as claimed in claim 1 wherein the temperature of the silicon bed and the temperature at the point in the furnace spaced from the bed are sensed by a pair of thermocouples respectively.
Claim 7
Independent Claim
108 words
A method of manufacturing a silicon nitride powder comprising heating a bed containing silicon powder in a furnace having an atmosphere including nitrogen, sensing the temperature in the bed and comparing said temperature with a further temperature at another point in the furnace outside said bed, and controlling the partial pressure of the nitrogen in the furnace atmosphere in accordance with the difference between said temperatures so as to ensure that the temperature in the bed does not exceed a predetermined value above which β-phase silicon nitride is formed, the partial pressure of the nitrogen in the furnace being controlled by diluting the nitrogen in the furnace atmosphere.
Claim 8
Independent Claim
108 words
A method of manufacturing a silicon nitride powder comprising heating a bed containing silicon powder in a furnace having an atmosphere including nitrogen, sensing the temperature in the bed and comparing said temperature with a further temperature at another point in the furnace outside said bed, and controlling the partial pressure of the nitrogen in the furnace atmosphere in accordance with the difference between said temperatures so as to ensure that the temperature in the bed does not exceed a predetermined value above which β-phase silicon nitride is formed, the partial pressure of the nitrogen in the furnace being controlled by diluting the nitrogen in the furnace atmosphere.
References Cited (Backward Citations)
US2330767A
Cited
US2519481A
Cited
GB717555A
Cited
US2788264A
Cited
US3222438A
Cited
US3591337A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-09 | 1979-08-11 | 1980-02-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-09 | 1983-08-11 | 1984-02-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-09 | 1987-08-11 | 1988-02-10 | $7700.00 | Window Closed / Lapsed |