Oxidation resistant carbonaceous bodies and method of producing same
Assignee: Unifrax I LLC
•
Filing: 1973-01-29
•
Granted: 1976-02-03
•
Expires: 1993-01-29
Abstract
Abstract An oxidation inhibitant paint for coating the surfaces of carbon or graphite articles comprises a suspension of about 10 to about 35 percent finely divided elemental boron, dispersed in a thermosetting resin such as a solution of furfuryl alcohol prepolymer, furfural and maleic anhydride. Silica or boron nitride may be added to the paint mixture, a preferred paint composition having about 22 to 23 percent boron and 2 to 3 percent silica, dispersed in a resin solution of about 48 to 49 percent furfuryl alcohol prepolymer, about 48 to 49 percent furfural and about 2 to 4 percent maleic anhydride. The paint may be applied to the carbon article (e.g., by brushing, spraying, dipping or rolling) and then cured to give a firmly adherent coating of resin, silica and elemental boron. The coating is strongly resistant against thermal and mechanical stresses applied to the carbon article, protecting the carbon against oxidation at temperatures up to at least 900°C.
Inventors
- 👤 Glenn R. Marin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 03:45
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B35/00; C04B35/515; C04B35/52; C04B35/524; C04B41/45; C04B41/50; C04B41/80; C04B41/81; C04B41/85; C09; C09D; C09D5/00; Y; Y10; Y10T; Y10T428/00; Y10T428/30
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
130 words
A method for making a carbonaceous article comprising reinforced and laminated carbon oxidation resistant by forming a coating thereon, comprising the steps of: a. coating the surface of the article with a thin uniform layer of a suspension comprising about 10 to about 35% of elemental boron having an average particle diameter in the range of about 0.5 to about 2 microns, said elemental boron being dispersed in a thermosetting resin solution, said solution comprising about 40 to about 60% furfuryl alcohol prepolymer, about 40 to about 60% furfural and about 1 to 10% maleic anhydride; and b. heating the coated article in the temperature range of about 300° to about 400°F under an inert atmosphere, thereby curing the coated suspension for forming the oxidation resistant coating on the article.
Claim 2
Independent Claim
130 words
A method for making a carbonaceous article comprising reinforced and laminated carbon oxidation resistant by forming a coating thereon, comprising the steps of: a. coating the surface of the article with a thin uniform layer of a suspension comprising about 10 to about 35% of elemental boron having an average particle diameter in the range of about 0.5 to about 2 microns, said elemental boron being dispersed in a thermosetting resin solution, said solution comprising about 40 to about 60% furfuryl alcohol prepolymer, about 40 to about 60% furfural and about 1 to 10% maleic anhydride; and b. heating the coated article in the temperature range of about 300° to about 400°F under an inert atmosphere, thereby curing the coated suspension for forming the oxidation resistant coating on the article.
Claim 3
Dependent Claim
106 words
An oxidation resistant carbonaceous article comprising reinforced and laminated carbon having a surface coating of finely divided elemental boron, said elemental boron having average particle diameters in the range of about 0.5 to about 2 microns, said elemental boron suspended in a cured thermosetting resin, the elemental boron comprising about 10 to about 35% of said resin suspension, and said resin comprising about 40 to about 60% furfuryl alcohol prepolymer, about 40 to about 60% furfural, and about 1 to about 10% maleic anhydride, said coating having been deposited on the exterior of said carbonaceous article from the application of said elemental boron containing resin suspension.
Claim 4
Dependent Claim
106 words
An oxidation resistant carbonaceous article comprising reinforced and laminated carbon having a surface coating of finely divided elemental boron, said elemental boron having average particle diameters in the range of about 0.5 to about 2 microns, said elemental boron suspended in a cured thermosetting resin, the elemental boron comprising about 10 to about 35% of said resin suspension, and said resin comprising about 40 to about 60% furfuryl alcohol prepolymer, about 40 to about 60% furfural, and about 1 to about 10% maleic anhydride, said coating having been deposited on the exterior of said carbonaceous article from the application of said elemental boron containing resin suspension.
References Cited (Backward Citations)
US2992960A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-02 | 1979-08-04 | 1980-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-02 | 1983-08-04 | 1984-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-02 | 1987-08-04 | 1988-02-03 | $7700.00 | Window Closed / Lapsed |