Fire retardant fabrics
Assignee: United Merchants and Manuf Inc
•
Filing: 1974-01-21
•
Granted: 1976-02-03
•
Expires: 1994-01-21
Abstract
Abstract A process for rendering cellulose and cellulose containing fabrics fire resistant by first impregnating the fibers with an aminoplast resin and polymerizing the resin while the fibers are wet and swollen. Thereafter, the fabric is impregnated with tetrakis (hydroxymethyl) phosphonium hydroxide, cured, washed and dried. The fabric obtained from this process possesses high fire-retardency values, soft hand, and tensile values similar to that of the untreated fabric.
Inventors
- 👤 Marshall W. Duke
- 👤 Razmic S. Gregorian
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 14:58
CPC Classifications
D; D06; D06M; D06M15/00; D06M15/19; D06M15/37; D06M15/39; D06M15/423; D06M15/43; D06M15/431; C; C08; C08K; C08K5/00; C08K5/49; C08K5/51; C08K5/53; C08L; C08L1/00; C08L61/00; C08L61/20; C08L61/26; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T442/00; Y10T442/20; Y10T442/2041; Y10T442/2098; Y10T442/2631; Y10T442/2672; Y10T442/2689
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
181 words
A process for rendering a cellulose containing fabric fire retardant comprising: a. impregnating the fibers of the cellulose-based fabric with an aqueous aminoplast resin composition, such that the fibers become wet and swollen, in an amount sufficient to produce a resin content in the final fabric in the range from about 2% to 25% by weight based on the total weight of the fabric; b. polymerizing the resin in the impregnated fabric while the fibers are in a wet and swollen state; c. adjusting the pH of the fabric to a value greater than about 7.0; d. impregnating the fabric with a solution of tetrakis (hydroxymethyl) phosphonium hydroxide in an amount sufficient to produce a phosphorus content in the final fabric in the range from about 1% to 3% by weight based on the total weight of the fabric; e. subjecting the impregnated fabric to curing conditions consisting essentially of heating the fabric at a temperature in the range from about 300°F to 400°F for a time period from about 2 to 20 minutes; and f. washing and drying the fabric.
Claim 2
Dependent Claim
181 words
A process for rendering a cellulose containing fabric fire retardant comprising: a. impregnating the fibers of the cellulose-based fabric with an aqueous aminoplast resin composition, such that the fibers become wet and swollen, in an amount sufficient to produce a resin content in the final fabric in the range from about 2% to 25% by weight based on the total weight of the fabric; b. polymerizing the resin in the impregnated fabric while the fibers are in a wet and swollen state; c. adjusting the pH of the fabric to a value greater than about 7.0; d. impregnating the fabric with a solution of tetrakis (hydroxymethyl) phosphonium hydroxide in an amount sufficient to produce a phosphorus content in the final fabric in the range from about 1% to 3% by weight based on the total weight of the fabric; e. subjecting the impregnated fabric to curing conditions consisting essentially of heating the fabric at a temperature in the range from about 300°F to 400°F for a time period from about 2 to 20 minutes; and f. washing and drying the fabric.
Claim 3
Dependent Claim
19 words
The process of claim 1 wherein the fabric has a minimum cellulose content of about 65 percent by weight.
Claim 4
Dependent Claim
23 words
The process of claim 1 wherein in adjustment step (c) the pH is adjusted to a value in the range of about 8.5-9.6.
Claim 5
Dependent Claim
131 words
The process of claim 1, wherein in impregnation step (a), the fabric is impregnated with a mixture of an aminoplast resin and an organic halogenated phosphorus containing ester selected from the group consisting of compounds having the general formula ##EQU2## wherein R,R', and R" can be the same or different and may be a halogenated lower alkyl group having from 2 to 8 carbon atoms, and containing from 1 to 7 halogen atoms, a nucleus selected from the phenyl series which is substituted with 1 to 7 halogen atoms, a lower alkyl phenyl group wherein the alkyl group contains from 1 to 5 carbon atoms, and n is zero or 1, the concentration of said ester being from about 5 to 25% by weight based on the weight of the mixture.
Claim 6
Dependent Claim
52 words
The process of claim 4 wherein the halogenated phosphorus containing ester is selected from the group consisting of tris (2,3-dibromopropyl) phosphate, tris 2-(1,3 dibromopropyl) phosphate, tris (chloroethyl) phosphate, tris (2-bromo-3-chloropropyl) phosphate, tris 2-(1,3-dichloropropyl) phosphate, bis (2,3-dibromopropyl)-2,3-dibromopropyl phosphonate, tris-(2,6-dichlorophenyl) phosphate, tris-(p-bromophenyl) phosphate, tris-(2,3,4-tribromobuyl) phosphate, tris-2-(1,6-dibromonaphthyl) phosphate, bis (chloroethyl) phenyl phosphonate and tris-(2-bromo-4methylphenyl) phosphate.
Claim 7
Dependent Claim
26 words
The process of claim 4 wherein the fabric consists essentially of at least about 20 percent by weight cellulose, the remainder of the fabric being polyester.
Claim 8
Dependent Claim
67 words
The process of claim 1 wherein in impregnation step (a), the fabric is impregnated with a mixture of an aminoplast resin and an organic halogenated phosphorus containing ester selected from the group consisting of tris (dibromopropyl) phosphate, tris (dichloropropyl) phosphate, tris (chlorobromopropyl) phosphate, and di (chloroethyl) chloroethyl phosphonate the concentration of the ester being in the range from about 5 to 25% by weight of the mixture.
Claim 9
Dependent Claim
22 words
The process of claim 1 wherein subsequent to the adjustment step (c) and prior to impregnation step (d), the fabric is dried.
Claim 10
Dependent Claim
59 words
The process of claim 1 wherein in impregnation step (d), the fabric is impregnated with a solution comprising an aqueous mixture of about 10 to 35% by weight tetrakis (hydroxymethyl) phosphonium hydroxide and about 1 to 20% by weight of a nitrogenous compound selected from the group consisting of urea, ethylene urea, propylene urea, guanidine, dicyandiamide, oxamide, and thiourea.
Claim 11
Dependent Claim
23 words
The process of claim 1 wherein subsequent to curing step (e), and prior to washing step (f), the fabric is treated with peroxide.
Claim 12
Dependent Claim
13 words
A fire retardant cellulose containing fabric obtained from the process of claim 1.
Claim 13
Dependent Claim
13 words
A fire retardant cellulose containing fabric obtained from the process of claim 6.
References Cited (Backward Citations)
US2809941A
Cited
US2911326A
Cited
US2992138A
Cited
US3096201A
Cited
US3067062A
Cited
US3632297A
Cited
US3698854A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-02 | 1979-08-04 | 1980-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-02 | 1983-08-04 | 1984-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-02 | 1987-08-04 | 1988-02-03 | $7700.00 | Window Closed / Lapsed |