US3936441A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the production of water adsorbing but water-insoluble cellulose ethers
Assignee: Hoechst AG
•
Filing: 1974-11-11
•
Granted: 1976-02-03
•
Expires: 1994-11-11
Abstract
Abstract This invention relates to an improvement in the process for the production of water-adsorbing, but largely water-insoluble, cellulose ethers, in which cellulose is alkalized in the presence of alkali hydroxide and isopropanol as a reaction medium and is so reacted with an etherification agent that by etherification only a water-soluble cellulose ether is produced, and in which process the cellulose is reacted with a cross-linking agent which is polyfunctional towards cellulose in an alkaline reaction medium before, during, or after the etherification of the cellulose, the improvement comprising effecting the etherification of cellulose to carboxymethyl cellulose, carboxymethyl hydroxyethyl cellulose, hydroxyethyl cellulose, or methylhydroxyethyl cellulose, reacting the cellulose with the polyfunctional cross-linking agent in the presence of 0.8 to 7.5 parts by weight of isopropanol, based upon the cellulose weight, and employing as the cross-linking agent acrylamido methylene chloroacetamide, dichloroacetic acid or phosphorus oxychloride or a compound in which at least two groups functional towards cellulose are THE ACRYLIC AMINO GROUP CH2=CH-C-N- PARALLEL ¦ O the chlorine azomethine group -N=C- ¦ Cl OR THE ALLYLOXY AZOMETHINE GROUP -N=C-O-CH2-CH=CH2 . ¦
Inventors
- 👤 Arno Holst
- 👤 Michael Kostrzewa
- 👤 Helmut Lask
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:52
CPC Classifications
C; C08; C08B; C08B15/00; C08B15/10; A; A61; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/28; C08B11/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
167 words
In the process for the production of water-adsorbing, but largely waterinsoluble, cellulose ethers, in which cellulose is alkalized in the presence of alkali hydroxide and isopropanol as a reaction medium and is so reacted with an etherification agent that by etherification only a water-soluble cellulose ether is produced, and in which process the cellulose is reacted with a cross-linking agent which is polyfunctional towards cellulose in an alkaline reaction medium before, during, or after the etherification of the cellulose, the improvement which comprises effecting the etherification of cellulose to carboxymethyl cellulose, carboxymethyl hydroxyethyl cellulose, hydroxyethyl cellulose, or methylhydroxyethyl cellulose, reacting the cellulose with the polyfunctional cross-linking agent in the presence of 0.8 to 7.5 parts by weight of isopropanol, based upon the cellulose weight, and employing as the cross-linking agent acrylamido methylene chloroacetamide, dichloroacetic acid or phosphorus oxychloride or a compound in which at least two groups functional towards cellulose are the acrylic amino group ##EQU7## the chlorine azomethine group ##EQU8## or the allyloxy azomethine group ##EQU9##
Claim 2
Dependent Claim
167 words
In the process for the production of water-adsorbing, but largely waterinsoluble, cellulose ethers, in which cellulose is alkalized in the presence of alkali hydroxide and isopropanol as a reaction medium and is so reacted with an etherification agent that by etherification only a water-soluble cellulose ether is produced, and in which process the cellulose is reacted with a cross-linking agent which is polyfunctional towards cellulose in an alkaline reaction medium before, during, or after the etherification of the cellulose, the improvement which comprises effecting the etherification of cellulose to carboxymethyl cellulose, carboxymethyl hydroxyethyl cellulose, hydroxyethyl cellulose, or methylhydroxyethyl cellulose, reacting the cellulose with the polyfunctional cross-linking agent in the presence of 0.8 to 7.5 parts by weight of isopropanol, based upon the cellulose weight, and employing as the cross-linking agent acrylamido methylene chloroacetamide, dichloroacetic acid or phosphorus oxychloride or a compound in which at least two groups functional towards cellulose are the acrylic amino group ##EQU7## the chlorine azomethine group ##EQU8## or the allyloxy azomethine group ##EQU9##
Claim 3
Dependent Claim
15 words
A process according to claim 1 in which the cros-linking agent is dimethylol methylene bisacrylamide.
Claim 4
Dependent Claim
14 words
A process according to claim 1 in which the cross-linking agent is methylene bisacrylamide.
Claim 5
Dependent Claim
13 words
A process according to claim 1 in which the cross-linking agent is 2,4,6-trichloropyrimidine.
Claim 6
Dependent Claim
13 words
A process according to claim 1 in which the cross-linking agent is 2,4,5,6-tetrachloropyrimidine.
Claim 7
Dependent Claim
14 words
A process according to claim 1 in which the cross-linking agent is cyanuric chloride.
Claim 8
Dependent Claim
14 words
A process according to claim 1 in which the cross-linking agent is acrylamidomethylene chloroacetamide.
Claim 9
Dependent Claim
14 words
A process according to claim 1 in which the cross-linking agent is trisacrylol hexahydrotriazine.
Claim 10
Dependent Claim
14 words
A process according to claim 1 in which the cross-linking agent is triallyl cyanurate.
Claim 11
Dependent Claim
14 words
A process according to claim 1 in which the cross-linking agent is phosphorus oxychloride.
Claim 12
Dependent Claim
125 words
A process for the production of water-adsorbing, but largely water-insoluble cellulose ethers which comprises alkalizing cellulose in the presence of alkali hydroxide and 0.8 to 7.5 parts by weight of isopropanol as a reaction medium, based upon the cellulose weight, reacting the alkalized cellulose with an etherification agent so that by etherification only a water-soluble carboxymethyl cellulose, carboxymethyl hydroxyethyl cellulose, hydroxyethyl cellulose, or methylhydroxyethyl cellulose is produced, and reacting said cellulose, before, during, or after the etherification thereof with a cross-linking agent selected from the group consisting of methylene bisacrylamide, N-N'-dimethylol methylene bisacrylamide, trisacrylol hexahydro triazine, acrylamido methylene chloroacetamide, 2,4,6-trichloropyrimidine, cyanuric chloride, triallyl cyanurate, dichloroacetic acid, and phosphorus oxychloride, whereby a cross-linked cellulose ether is obtained which is more than 50 percent by weight water-insoluble.
Claim 13
Dependent Claim
125 words
A process for the production of water-adsorbing, but largely water-insoluble cellulose ethers which comprises alkalizing cellulose in the presence of alkali hydroxide and 0.8 to 7.5 parts by weight of isopropanol as a reaction medium, based upon the cellulose weight, reacting the alkalized cellulose with an etherification agent so that by etherification only a water-soluble carboxymethyl cellulose, carboxymethyl hydroxyethyl cellulose, hydroxyethyl cellulose, or methylhydroxyethyl cellulose is produced, and reacting said cellulose, before, during, or after the etherification thereof with a cross-linking agent selected from the group consisting of methylene bisacrylamide, N-N'-dimethylol methylene bisacrylamide, trisacrylol hexahydro triazine, acrylamido methylene chloroacetamide, 2,4,6-trichloropyrimidine, cyanuric chloride, triallyl cyanurate, dichloroacetic acid, and phosphorus oxychloride, whereby a cross-linked cellulose ether is obtained which is more than 50 percent by weight water-insoluble.
References Cited (Backward Citations)
US2517577A
Cited
US2886474A
Cited
US3029232A
Cited
US3102773A
Cited
US3125406A
Cited
US3298979A
Cited
US3423163A
Cited
GB1099239A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-02 | 1979-08-04 | 1980-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-02 | 1983-08-04 | 1984-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-02 | 1987-08-04 | 1988-02-03 | $7700.00 | Window Closed / Lapsed |