Method for beneficiation of magnesite ore
Assignee: Financial Mining - Industrial and Shipping Corp
•
Filing: 1974-12-10
•
Granted: 1976-02-03
•
Expires: 1994-12-10
Abstract
Abstract A method for beneficiation of magnesite ore wherein the ore is subjected to calcination to decrease the bulk density of the magnesite relative to the gangue. Accordingly, after such calcination, conventional gravimetric separations can be conducted with greatly increased efficiency. When the calcination is conducted in a reducing atmosphere, initially non-magnetic gangue material is converted to a magnetic form and conventional magnetic separation procedures are conducted with enhanced efficiency.
Inventors
- 👤 Anthony Z. Frangiskos
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 09:01
CPC Classifications
B; B03; B03B; B03B9/00
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
152 words
A process for recovering magnesite from its ores as a caustic-calcined magnesite comprising the steps of: calcining a particulate magnesite ore having a particle size between about 2 and about 17mm by gradually heating the ore at a temperature of from about 500°C to about 1000°C so as to gradually raise the temperature of the ore for the desired calcination thereby converting the ore into a mixture of caustic-calcined magnesite having a bulk density in range of from about 1.4 to about 1.6 g/cm 3 and calcined gangue having a bulk density in the range of from about 2.2 to about 2.4 g/cm 3 ; subsequently separating said caustic-calcined magnesite from said calcined gangue by a physical separation process by utilizing the difference between said bulk density of the caustic-calcined magnesite and said bulk density of the calcined gangue; and effecting said separation on said mixture without size reduction of the latter.
Claim 2
Dependent Claim
152 words
A process for recovering magnesite from its ores as a caustic-calcined magnesite comprising the steps of: calcining a particulate magnesite ore having a particle size between about 2 and about 17mm by gradually heating the ore at a temperature of from about 500°C to about 1000°C so as to gradually raise the temperature of the ore for the desired calcination thereby converting the ore into a mixture of caustic-calcined magnesite having a bulk density in range of from about 1.4 to about 1.6 g/cm 3 and calcined gangue having a bulk density in the range of from about 2.2 to about 2.4 g/cm 3 ; subsequently separating said caustic-calcined magnesite from said calcined gangue by a physical separation process by utilizing the difference between said bulk density of the caustic-calcined magnesite and said bulk density of the calcined gangue; and effecting said separation on said mixture without size reduction of the latter.
Claim 3
Dependent Claim
21 words
A process as set forth in claim 1 wherein the ore is subjected to a preconcentration step prior to said calcining.
Claim 4
Dependent Claim
22 words
A process for recovering magnesite from its ores as set forth in claim 1 wherein said physical separation is carried out pneumatically.
Claim 5
Dependent Claim
51 words
A process for recovering magnesite from its ores as set forth in claim 3 wherein said calcining is conducted in a reducing atmosphere to transform the gangue into a material having magnetic properties, and said process further including the step of separating calcined magnesite from the reduced gangue by magnetic separation.
Claim 6
Dependent Claim
47 words
A process as set forth in claim 1 further comprising the step of screening the mixture of material subsequent to said step of calcining and prior to said step of physical separation so as to separate the particles of the mixture into separate groups according to size.
Claim 7
Dependent Claim
25 words
A process for recovering magnesite from its ores as set forth in claim 1 wherein said physical separation process is a wet gravimetric separation process.
Claim 8
Dependent Claim
25 words
A process for recovering magnesite from its ores as set forth in claim 1 wherein said physical separation process is a dry gravimetric separation process.
Claim 9
Dependent Claim
49 words
A process for recovering magnesite from its ores as set forth in claim 1 wherein said calcining is conducted in a reducing atmosphere to transform the gangue into a material having magnetic properties, said process including the step of separating calcined magnesite from the reduced gangue by magnetic separation.
Claim 10
Dependent Claim
22 words
A process as set forth in claim 8 wherein the ore is subjected to a mechanical preparation step prior to said calcining.
Claim 11
Dependent Claim
21 words
A process as set forth in claim 4 wherein the ore is subjected to a preconcentration step prior to said calcining.
Claim 12
Dependent Claim
21 words
A process as set forth in claim 8 wherein the ore is subjected to a preconcentration step prior to said calcining.
Claim 13
Dependent Claim
22 words
A process as set forth in claim 1 wherein the ore is subjected to a mechanical preparation step prior to said calcining.
Claim 14
Dependent Claim
22 words
A process as set forth in claim 12 where in the ore is subjected to a preconcentration step prior to said calcining.
References Cited (Backward Citations)
GB190801110A
Cited
US1248880A
Cited
US1266730A
Cited
US1269170A
Cited
US1546854A
Cited
GB274889A
Cited
US1901102A
Cited
US2349556A
Cited
US2586545A
Cited
US2881048A
Cited
FR1322140A
Cited
US3482938A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-02 | 1979-08-04 | 1980-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-02 | 1983-08-04 | 1984-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-02 | 1987-08-04 | 1988-02-03 | $7700.00 | Window Closed / Lapsed |