Bonded gold article composition for bonding gold to a ceramic substrate utilizing copper oxide and cadium oxide
Assignee: Electro Oxide Corp
•
Filing: 1974-03-22
•
Granted: 1976-01-27
•
Expires: 1994-03-22
Abstract
Abstract A composition for, as well as a method of bonding gold to a ceramic substrate and a bonded gold article which includes a composition of gold, copper oxide, and cadmium oxide for bonding a gold layer to a ceramic substrate. Gold powder, copper oxide particles and cadmium oxide particles define a solid composition mixture where the copper oxide has a weight percentage in the preferred region between 0.25 and 3.0% and the cadmium oxide has a weight percentage in the preferred region between 1.0 and 5.0%. Organic binder is added to a predetermined amount of the copper oxide and cadmium particles and then blended. The gold powder is incorporated into the copper oxide, cadmium oxide, and organic binder to form a total composition mixture. The organic binder has a weight percentage of the total composition mixture within the ranges of 10 to 95%. The total composition mixture is blended and applied to a ceramic substrate. The coated ceramic article is fired within the preferred temperature range 950° to 100°C. Copper oxide crystals impregnate the ceramic substrate and form a high strength bond between the gold layer and the ceramic substrate.
Inventors
- 👤 Baynard R. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:57
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/45; C04B41/50; C04B41/51; C04B41/5116; C04B41/80; C04B41/81; C04B41/85; C04B41/88; C23; C23C; C23C24/00; C23C24/08; H; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/256
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
195 words
A method of bonding a gold layer to a ceramic substrate including the steps of: a. mixing on a weight basis: (A) about 0.1 to 7.0% of at least one copper oxide powder from the group consisting of cuprous oxide and cupric oxide; (B) about 0.01 to 15.0% of cadmium oxide powder; (C) 78.0 to 99.89% of gold powder having a particle size within the approximate range of 2.0 to 5.0 microns, said copper oxide powder and said cadmium oxide and said gold powder defining in combination a solid composition mixture, said weight percentages of said copper oxide, said cadmium oxide and said gold powder pertaining to said solid composition mixture; and, (D) about 10.0 to 95.0% of an organic binder devoid of glass frits, said organic binder in combination with waid copper powder, said cadmium oxide powder and said gold powder defining a total composition mixture, said weight percentages of said organic binder pertaining to said total composition mixture; b. applying said total composition mixture to a ceramic substrate to form a coated ceramic substrate; and c. firing said coated ceramic substrate at a predetermined temperature within the approximate temperature range of 850°to 1063°C.
Claim 2
Independent Claim
195 words
A method of bonding a gold layer to a ceramic substrate including the steps of: a. mixing on a weight basis: (A) about 0.1 to 7.0% of at least one copper oxide powder from the group consisting of cuprous oxide and cupric oxide; (B) about 0.01 to 15.0% of cadmium oxide powder; (C) 78.0 to 99.89% of gold powder having a particle size within the approximate range of 2.0 to 5.0 microns, said copper oxide powder and said cadmium oxide and said gold powder defining in combination a solid composition mixture, said weight percentages of said copper oxide, said cadmium oxide and said gold powder pertaining to said solid composition mixture; and, (D) about 10.0 to 95.0% of an organic binder devoid of glass frits, said organic binder in combination with waid copper powder, said cadmium oxide powder and said gold powder defining a total composition mixture, said weight percentages of said organic binder pertaining to said total composition mixture; b. applying said total composition mixture to a ceramic substrate to form a coated ceramic substrate; and c. firing said coated ceramic substrate at a predetermined temperature within the approximate temperature range of 850°to 1063°C.
Claim 3
Dependent Claim
59 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 1 wherein the step of mixing includes the steps of: a. incorporating said copper oxide powder and said cadmium oxide powder into said organic binder; and, b. blending said copper oxide powder and cadmium oxide powder and said organic binder with said gold powder.
Claim 4
Dependent Claim
47 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 2 wherein the step of blending includes the step of dispersing said copper oxide powder and cadmium oxide powder throughout said total composition mixture to form a substantially homogeneous total composition mixture.
Claim 5
Dependent Claim
34 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 2 wherein said organic binder has a predetermined weight percentage between 15% and 50% of said total composition mixture.
Claim 6
Dependent Claim
35 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 2 wherein said cadmium oxide powder has a predetermined weight percentage between 0.01% and 15.0% of said solid composition mixture.
Claim 7
Dependent Claim
36 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 5 wherein said predetermined weight percentage of said cadmium oxide powder is between 1.0 and 5.0% of said solid composition mixture.
Claim 8
Dependent Claim
49 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 2 wherein the step of incorporating is preceded by the step of dimensionally shaping said copper oxide powder and said cadmium oxide powder to a predetermined size less than approximately 1.0 micron in length.
Claim 9
Dependent Claim
81 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 7 wherein the step of dimensionally shaping said copper oxide and cadmium oxide includes the steps of: a. mixing said copper oxide powder and cadmium oxide powder with a wetting agent and, b. grinding said combination of copper oxide powder, said cadmium oxide powder and said wetting agent until a substantial quantity of copper oxide and cadmium oxide particles have been reduced to said predetermined size.
Claim 10
Dependent Claim
51 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 8 wherein the step of milling includes the step of reducing a substantial number of individual particles of said copper oxide powder and said cadmium oxide powder to a length less than one micron in dimension.
Claim 11
Dependent Claim
41 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 8 wherein the step of grinding is followed by the step of drying said wetting agent from said copper oxide powder and said cadmium oxide powder.
Claim 12
Dependent Claim
52 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 10 wherein the step of drying includes the step of heating said combination of said wetting agent and said copper oxide powder and said cadmium oxide powder until said wetting agent is substantially removed from said combination.
Claim 13
Dependent Claim
42 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 11 wherein the step of heating includes the step of inserting said combination into an oven maintained at a predetermined temperature sufficient to dry said wetting agent.
Claim 14
Dependent Claim
27 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 12 wherein said oven is maintained at an internal temperature approximating 100°C.
Claim 15
Dependent Claim
22 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 13 wherein said wetting agent is toluol.
Claim 16
Dependent Claim
22 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 13 wherein said wetting agent is benzene.
Claim 17
Dependent Claim
41 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 2 wherein the step of applying said total composition mixture includes the step of coating said ceramic substrate with a layer of said total composition mixture.
Claim 18
Dependent Claim
41 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 16 wherein the step of coating said ceramic substrate includes the step of silk screening said total composition mixture onto a surface of said ceramic substrate.
Claim 19
Dependent Claim
35 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 17 wherein said silk screened coating has a fired predetermined thickness between 50 millionths and 300 millionths of an inch.
Claim 20
Dependent Claim
36 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 17 wherein said silk screened coating has a fired predetermined thickness substantially between 75 millionths and 100 millionths of an inch.
Claim 21
Dependent Claim
38 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 16 wherein the step of coating includes the step of dipping said ceramic substrate into said total composition mixture for forming said layer.
Claim 22
Dependent Claim
33 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 17 wherein said dipped coating has a fired thickness between 50 millionths and 300 millionths of an inch.
Claim 23
Dependent Claim
35 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 17 wherein said dipped coating has a fired predetermined thickness substantially between 75 millionths and 100 millionths of an inch.
Claim 24
Dependent Claim
40 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 16 wherein the step of coating said ceramic substrate includes the step of printing said total composition mixture onto a surface of said ceramic substrate.
Claim 25
Dependent Claim
33 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 23 wherein said printed coating has a fired thickness between 50 millionths and 300 millionths of an inch.
Claim 26
Dependent Claim
35 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 23 wherein said printed coating has a fired predetermined thickness substantially between 75 millionths and 100 millionths of an inch.
Claim 27
Dependent Claim
40 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 2 wherein the step of firing said ceramic substrate includes the step of inserting said coated ceramic substrate into an oven having an oxidizing atmosphere.
Claim 28
Dependent Claim
45 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 26 wherein the step of firing said coated ceramic substrate includes the step of heating said coated ceramic substrate to a predetermined temperature within the range substantially between 900°to 1042°C.
Claim 29
Dependent Claim
45 words
The method of bonding a gold layer to a ceramic substrate as recited in claim 26 wherein the step of firing said coated ceramic substrate includes the step of heating said coated ceramic substrate to a predetermined temperature within the range substantially between 950°to 1000°C.
Claim 30
Dependent Claim
93 words
A ceramic article having thereon a fired coating of a solid composition mixture on a weight basis of: (A) about 0.1% to 7.0% of at least one copper oxide powder from the group consisting of cuprous oxide and cupric oxide; (B) about 0.01 to 15.0% of cadmium oxide powder; and (C) about 78.0 to 99.89% of gold powder having a particle size within the approximate range of 2.0 to 5.0 microns, said solid composition mixture being fired onto a ceramic substrate at a predetermined temperature within the approximate temperature range of 850°to 1063°C.
Claim 31
Dependent Claim
93 words
A ceramic article having thereon a fired coating of a solid composition mixture on a weight basis of: (A) about 0.1% to 7.0% of at least one copper oxide powder from the group consisting of cuprous oxide and cupric oxide; (B) about 0.01 to 15.0% of cadmium oxide powder; and (C) about 78.0 to 99.89% of gold powder having a particle size within the approximate range of 2.0 to 5.0 microns, said solid composition mixture being fired onto a ceramic substrate at a predetermined temperature within the approximate temperature range of 850°to 1063°C.
Claim 32
Dependent Claim
16 words
The ceramic article as recited in claim 29 wherein said copper oxide powder is cuprous oxide.
Claim 33
Dependent Claim
26 words
The ceramic article as recited in claim 30 wherein said weight percentage of said cadmium oxide is between 0.05 and 10.0% of said solid composition mixture.
Claim 34
Dependent Claim
27 words
The ceramic article as recited in claim 30 wherein said fired coating has a predetermined layered thickness substantially between 50 millionths and 300 millionths of an inch.
Claim 35
Dependent Claim
27 words
The ceramic article as recited in claim 30 wherein said fired coating has a predetermined layered thickness substantially between 75 millionths and 100 millionths of an inch.
Claim 36
Dependent Claim
23 words
The ceramic article as recited in claim 30 wherein said coating is fired at a predetermined temperature within the approximate range 900°to 1042°C.
Claim 37
Dependent Claim
24 words
The ceramic article as recited in claim 30 wherein said coating is fired at a predetermined temperature within the approximate range 950° to 1000°C.
Claim 38
Dependent Claim
16 words
The ceramic article as recited in claim 29 wherein said copper oxide powder is cupric oxide.
Claim 39
Dependent Claim
27 words
The ceramic article as recited in claim 36 wherein said weight percentage of said cadmium oxide is substantially between 0.05 and 10.0% of said solid composition mixture.
Claim 40
Dependent Claim
27 words
The ceramic article as recited in claim 36 wherein said fired coating has a predetermined layered thickness substantially between 50 millionths and 300 millionths of an inch.
Claim 41
Dependent Claim
27 words
The ceramic article as recited in claim 36 wherein said fired coating has a predetermined layered thickness substantially between 75 millionths and 100 millionths of an inch.
Claim 42
Dependent Claim
24 words
The ceramic article as recited in claim 36 wherein said coating is fired at a predetermined temperature within the approximate range 900° to 1042°C.
Claim 43
Dependent Claim
24 words
The ceramic article as recited in claim 36 wherein said coating is fired at a predetermined temperature within the approximate range 950° to 1000°C.
References Cited (Backward Citations)
US2733161A
Cited
US2247036A
Cited
US2837487A
Cited
GB855625A
Cited
US3557576A
Cited
US3407081A
Cited
US3440182A
Cited
US3622523A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-26 | 1979-07-28 | 1980-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-26 | 1983-07-28 | 1984-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-26 | 1987-07-28 | 1988-01-27 | $7700.00 | Window Closed / Lapsed |