Assignee: Raytheon Co
•
Filing: 1974-02-27
•
Granted: 1976-01-27
•
Expires: 1994-02-27
Abstract
Abstract An invention directed to the preparation of laser windows from halide crystals purified by congruent growth from the melt by a reactive atmospheric processing method is disclosed. Single crystal refractory metal halides, and rare earth halides prepared by this invention can be used to produce laser windows of excellent mechanical, thermal, and optical properties.
Inventors
- 👤 Ricardo C. Pastor
- 👤 Kaneto Arita
- 👤 Morton Robinson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 17:16
CPC Classifications
H; H01; H01S; H01S3/00; H01S3/02; H01S3/03; H01S3/034; C; C01; C01F; C01F11/00; C01F11/20; C01F11/22; C30; C30B; C30B11/00; C30B15/00; C30B29/00; C30B29/10; C30B29/12; Y; Y10; Y10S; Y10S117/00; Y10S117/906
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
176 words
A method of preparing alkaline earth metal halide crystals for laser windows by a reactive atmosphere process comprising the steps of a. placing an alkaline earth metal halide crystal in a crystal growth crucible within a furnace; b. purging said furnace with an inert gas; c. causing the atmosphere within said purged furnace to become reactive with respect to anion and cation impurities by the application of low dewpoint HF gas at an input rate which maintains a positive pressure at a P H .sbsb.2O /P HF ratio less than 10 - 5 ; d. causing said halide crystal to melt by gradually increasing the temperature of said furnace to a point slightly above the melting point of said crystal; e. allowing said melt to soak in said reactive atmosphere from 8-15 hours; f. initiating a programmed crystal growth process with said crucible at a rate not to exceed a few millimeters per hour whereby a recrystallized crystal is formed; and g. allowing said crystal to slowly cool in the presence of the HF reactive atmosphere.
Claim 2
Independent Claim
176 words
A method of preparing alkaline earth metal halide crystals for laser windows by a reactive atmosphere process comprising the steps of a. placing an alkaline earth metal halide crystal in a crystal growth crucible within a furnace; b. purging said furnace with an inert gas; c. causing the atmosphere within said purged furnace to become reactive with respect to anion and cation impurities by the application of low dewpoint HF gas at an input rate which maintains a positive pressure at a P H .sbsb.2O /P HF ratio less than 10 - 5 ; d. causing said halide crystal to melt by gradually increasing the temperature of said furnace to a point slightly above the melting point of said crystal; e. allowing said melt to soak in said reactive atmosphere from 8-15 hours; f. initiating a programmed crystal growth process with said crucible at a rate not to exceed a few millimeters per hour whereby a recrystallized crystal is formed; and g. allowing said crystal to slowly cool in the presence of the HF reactive atmosphere.
Claim 3
Dependent Claim
15 words
The product of claim 1 wherein the alkaline earth halide crystal is CaF 2 .
Claim 4
Dependent Claim
15 words
The product of claim 1 wherein the alkaline earth halide crystal is BaF 2 .
Claim 5
Dependent Claim
15 words
The product of claim 1 wherein the alkaline earth halide crystal is SrF 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-26 | 1979-07-28 | 1980-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-26 | 1983-07-28 | 1984-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-26 | 1987-07-28 | 1988-01-27 | $7700.00 | Window Closed / Lapsed |