Resin laminate and method of making
Assignee: Individual
•
Filing: 1971-04-26
•
Granted: 1976-01-20
•
Expires: 1991-04-26
Abstract
Abstract A resin product is produced as an extrudate made up of two or more layers of different resin materials that retain desirable characteristics of each type of material. The layers are molecularly bonded or fully adhered in a face-to-face relation without an adverse modification of the characteristics of the individual materials. The extrudate is produced in the form of a longitudinal strip or sheet by simultaneously separately forcing or co-extending two or more different resin materials in a liquid or molten condition through separate die passageways while forming or shaping each material into a desired shape and applying the shaped materials as laminates in a face-to-face relation upon each other, while advancing them and thereafter solidifying them as adhering layers or plys of a unitized strip or sheet length.
Inventors
- 👤 Bernard W. Brooks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 14:37
CPC Classifications
B; B29; B29C; B29C48/00; B29C48/03; B29C48/07; B29C48/08; B29C48/16; B29C48/18; B29C48/21; B29C48/25; B29C48/30; B29C48/305; B29C48/307; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B32B27/30; B32B27/308; B32B27/36; B32B27/365; B32B2250/00; B32B2250/24; B32B2307/00; B32B2307/40; B32B2307/412
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
333 words
A process of the character shown and described for forming an improved extrudate resin laminate for glazing utilizations that is relatively unbreakable, that has the property of toughness and visual clearness and of light transmission without adverse reaction to ultraviolet light, and that is capable of being shaped, formed and used without danger of separating its layers with respect to each other which comprises, pressure-energizing and advancing a continuous flowing stream of acrylic resin in a molten condition as a strip-like section within and along an extrusion flow path within a die, simultaneously pressure-energizing and advancing a continuous flowing stream of a polycarbonate resin in a fully molten condition as a strip-like section of greater thickness than the acrylic strip-like section within and along a second extrusion flow path within the die; as the resins issue from the first and second-mentioned flow paths and without exposing them to the atmosphere, applying the acrylic resin as a strip-like flat face layer of lesser thickness upon the polycarbonate resin as a strip-like flat base layer of greater thickness within a final extrusion flow path within the die, pressure-energizing and advancing the two molten resin streams in wide face abutment with respect to each other within and along the final extrusion flow path to outwardly exit from the die as an extruded layered flow stream, and substantially immediately adjacent the exit of the layered stream from the die subjecting it to cooling and solidification and forming a molecularly bonded-together composite strip-like member; in furtherance of the process, advancing the polycarbonate resin material as a centrally disposed streamlike base layer; advancing the acrylic resin material in the form of two streamlike layers of strip-like section, each of lesser thickness than the polycarbonate strip-like section within the die and applying them in an aligned abutting relation to opposite faces of the base layer; and forming a composite resin member length having a base layer of the polycarbonate resin material and opposed facing layers of the acrylic resin material.
Claim 2
Dependent Claim
333 words
A process of the character shown and described for forming an improved extrudate resin laminate for glazing utilizations that is relatively unbreakable, that has the property of toughness and visual clearness and of light transmission without adverse reaction to ultraviolet light, and that is capable of being shaped, formed and used without danger of separating its layers with respect to each other which comprises, pressure-energizing and advancing a continuous flowing stream of acrylic resin in a molten condition as a strip-like section within and along an extrusion flow path within a die, simultaneously pressure-energizing and advancing a continuous flowing stream of a polycarbonate resin in a fully molten condition as a strip-like section of greater thickness than the acrylic strip-like section within and along a second extrusion flow path within the die; as the resins issue from the first and second-mentioned flow paths and without exposing them to the atmosphere, applying the acrylic resin as a strip-like flat face layer of lesser thickness upon the polycarbonate resin as a strip-like flat base layer of greater thickness within a final extrusion flow path within the die, pressure-energizing and advancing the two molten resin streams in wide face abutment with respect to each other within and along the final extrusion flow path to outwardly exit from the die as an extruded layered flow stream, and substantially immediately adjacent the exit of the layered stream from the die subjecting it to cooling and solidification and forming a molecularly bonded-together composite strip-like member; in furtherance of the process, advancing the polycarbonate resin material as a centrally disposed streamlike base layer; advancing the acrylic resin material in the form of two streamlike layers of strip-like section, each of lesser thickness than the polycarbonate strip-like section within the die and applying them in an aligned abutting relation to opposite faces of the base layer; and forming a composite resin member length having a base layer of the polycarbonate resin material and opposed facing layers of the acrylic resin material.
Claim 3
Dependent Claim
45 words
In a process as defined in claim 1, employing a pair of positively forwardly driven pinch rolls for advancing the composite member outwardly from the exit, and effecting the cooling and solidification-forming of the composite strip-like member before subjecting the member to the pinch rolls.
Claim 4
Dependent Claim
43 words
In a process as defined in claim 1, forming the polycarbonate as a base layer having a thickness of about 0.240 of an inch, and forming the acrylic layer as a surface facing layer having a thickness of about 0.005 of an inch.
Claim 5
Dependent Claim
49 words
In a process as defined in claim 3, advancing the polycarbonate base layer a molten temperature of about 450° to 500° F. and the acrylic layer at a temperature of about 400° F. into and in wide face abutment with respect to each other within and along the die.
Claim 6
Dependent Claim
54 words
In a process as defined in claim 1, applying each acrylic face layer of a thickness of about 0.005 of an inch and at a temperature of about 400° F to the polycarbonate base layer of a thickness of about 0.240 of an inch and at a temperature of about 450° to 500° F.
References Cited (Backward Citations)
US3276943A
Cited
US3170013A
Cited
US3443277A
Cited
US3420679A
Cited
US3476627A
Cited
US3556635A
Cited
US3639573A
Cited
US3668288A
Cited
US3565985A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-19 | 1979-07-21 | 1980-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-19 | 1983-07-21 | 1984-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-19 | 1987-07-21 | 1988-01-20 | $7700.00 | Window Closed / Lapsed |