Cobalt-base alloy

Claim 2

A composition of matter consisting essentially of the following elements in amounts expressed in weight percent: Chromium -- from about 25 to about 36 Nickel -- from about 3.5 to about 13 Wolfram -- from about 3 to about 10.5 Tantalum -- from about 1.4 to about 6.5 Zirconium -- from about 0.005 to about 0.02 Silicon -- from about 0.05 to about 2 Carbon -- from about 0.35 to about 0.95 Boron -- from about 0.001 to about 0.1 Iron -- from about 0.01 to about 12 Cobalt -- Balance the weight ratio of wolfram to tantalum being within the range of from about 1 to about 5.5 and the weight ratio of zirconium to boron being within the range of from about 0.05 to about 35.

Claim 3

The composition of claim 1 in which said elements are contained in the following approximate amounts, expressed in weight percent: Chromium -- from about 28.5 to about 33 Nickel -- from about 9.5 to about 11 Wolfram -- from about 5.5 to about 8 Tantalum -- from about 2.6 to about 4.4 Zirconium -- from about 0.009 to about 0.025 Silicon -- from about 0.25 to about 0.7 Carbon -- from about 0.5 to about 0.65 Boron -- from about 0.01 to about 0.035 Iron -- from about 0.25 to about 0.6 Cobalt -- Balance the weight ratio of wolfram to tantalum being within the range of from about 1.9 to about 3.5 and the weight ratio of zirconium to boron being within the range of from about 0.25 to about 0.9.

Claim 4

The composition of claim 1 in which said elements are contained in the following approximate amounts expressed in weight percent: Chromium -- about 31.2 Nickel -- about 10.4 Wolfram -- about 6.5 Tantalum -- about 2.8 Zirconium -- about 0.01 Silicon -- about 0.38 Carbon -- about 0.58 Boron -- about 0.03 Iron -- about 0.32 Cobalt -- balance the weight ratio of wolfram to tantalum being about 2.3 and the weight ratio of zirconium to boron being about 0.3.

Claim 5

The composition of claim 1 in which said composition contains up to about 0.1 weight percent aluminum, about 0.1 weight percent titanium, about 0.015 weight percent sulfur and about 0.015 weight percent phosphorous.

Claim 6

The composition of claim 1 which is air castable at a temperature within the range of from about 2,800°F to about 3,025°F.

Claim 7

The composition of claim 1 having a life of about 8,500 hours at stress-rupture conditions of about 1,500 psi. and 2,050°F.

Claim 8

The composition of claim 1 having an as cast hardness of 108 (Rockwell B Scale) and a heat treated hardness of 111 (Rockwell B Scale).

Claim 9

An article of manufacture produced by casting the composition of matter defined in claim 1.

Claim 10

An article of manufacture produced by casting and machining the composition of matter defined in claim 1.

Claim 11

A spinner comprised of the composition of claim 1, said spinner being comprised of foraminous walls and adapted for rotation.