Plugging subterranean regions with acrylic-epoxy resin-forming emulsions
Assignee: Shell USA Inc
•
Filing: 1974-10-15
•
Granted: 1976-01-20
•
Expires: 1994-10-15
Abstract
Abstract A subterranean region is plugged by flowing into it an aqueous emulsion containing an epoxy-resin-forming polyepoxy polymer, an acrylic-resin-forming polycarboxy polymer, and a material for controlling the rate of the interaction of said polymers, with the proportions of said materials arranged to cause the emulsion to become a resinous plug after being emplaced.
Inventors
- 👤 Randolph H. Knapp
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 17:31
CPC Classifications
C; C09; C09K; C09K8/00; C09K8/50; C09K8/502; C09K8/56; C09K8/57; C09K8/575; C09K8/5751; C09K8/5755; E; E21; E21B; E21B33/00; E21B33/10; E21B33/13; E21B33/138
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
98 words
In a well treating process in which a subterranean region is plugged by flowing into it a pumpable fluid that subsequently becomes relatively immobile, the improvement which comprises: compounding an aqueous emulsion that contains an epoxy-resin-forming polyepoxy polymer, an acrylic-resin-forming polycarboxy polymer, and a material for controlling the rate of the polymerization of said polymers; and correlating the proportions of said polymers and polymerization rate-controlling material with the temperature and flow properties of the subterranean region to be plugged so that, after being flowed into said region, the emulsion becomes a resinous plug having a significant compressive strength.
Claim 2
Dependent Claim
98 words
In a well treating process in which a subterranean region is plugged by flowing into it a pumpable fluid that subsequently becomes relatively immobile, the improvement which comprises: compounding an aqueous emulsion that contains an epoxy-resin-forming polyepoxy polymer, an acrylic-resin-forming polycarboxy polymer, and a material for controlling the rate of the polymerization of said polymers; and correlating the proportions of said polymers and polymerization rate-controlling material with the temperature and flow properties of the subterranean region to be plugged so that, after being flowed into said region, the emulsion becomes a resinous plug having a significant compressive strength.
Claim 3
Dependent Claim
43 words
The process of claim 1 in which the proportions of the ingredients are adjusted so that, in an unconsolidated reservoir sand, the emulsion is capable of forming a plugged mass having a compressive strength of at least about 100 pounds per square inch.
Claim 4
Dependent Claim
23 words
The process of claim 1 in which said emulsion contains an organic silane that is capable of reacting with epoxy or carboxy groups.
Claim 5
Dependent Claim
30 words
The process of claim 1 in which said emulsion contains a proportion of asphalt that is significant but is less than that of the total proportion of the resin-forming polymers.
Claim 6
Dependent Claim
24 words
The process of claim 1 in which the material for controlling the rate of interaction between the polymers includes a water-soluble alkali metal halide.
Claim 7
Dependent Claim
14 words
The process of claim 5 in which the alkali metal halide is sodium chloride.
Claim 8
Dependent Claim
75 words
The process of claim 1 in which: the proportions of the polymers and polymerization rate-controlling ingredients are adjusted to provide an emulsion that is slowly reactive at the temperature of the subterranean region; and a slug of the emulsion is flowed into the region and kept static long enough for gelation to occur in any portions that have become mixed with aqueous alkali metal halide solution which is encountered within any portion of the region.
Claim 9
Dependent Claim
99 words
The process of claim 1 in which: the proportion of said polymers and polymerization ratecontrolling ingredients are adjusted to provide an emulsion that is slowly reactive at the temperature of said subterranean region; and said emulsion is injected relatively slowly so that, when a first arriving portion of the emulsion flows into a relatively permeable portion of the subterranean region that contains an aqueous solution of an alkali metal halides, that portion of the emulsion is gelled and tends to cause later arriving portions of the emulsion to be diverted into the less permeable portions of the subterranean region.
References Cited (Backward Citations)
US2859820A
Cited
US3181612A
Cited
US3282338A
Cited
US3176769A
Cited
US3335796A
Cited
US3634237A
Cited
US3401747A
Cited
US3587742A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-19 | 1979-07-21 | 1980-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-19 | 1983-07-21 | 1984-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-19 | 1987-07-21 | 1988-01-20 | $7700.00 | Window Closed / Lapsed |