Water absorbing starch-acrylonitrile graft copolymers fumed silica or alumina modified to improve rate of absorption for physiological fluids
Assignee: Kimberly Clark Corp
•
Filing: 1975-03-07
•
Granted: 1976-01-13
•
Expires: 1995-03-07
Abstract
Abstract An improvement in the composition of particulate, water-insoluble alkali metal carboxylate salts of starch-acrylonitrile graft copolymers of the type which are produced by saponifying starch-acrylonitrile graft copolymers with an alkali metal base in an aqueous alcoholic medium and which particulate copolymer in its unimproved form is capable of absorbing in excess of 50 parts of aqueous fluids per part of copolymer when saturated. The improvement comprises the intermixture with the particulate copolymer of fumed silica or fumed alumina particles in an amount sufficient to increase markedly the rate at which the mixture absorbs physiological fluid as compared to the rate of absorption for such fluids exhibited by the copolymer before the fumed material is added. The mixture also minimizes the undesirable dusting tendency which is a characteristic of the particulate copolymer in the absence of the fumed silica or alumina.
Inventors
- 👤 David V. Duchane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 06:13
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; A; A61; A61L; A61L15/00; A61L15/16; A61L15/18; A61L15/42; A61L15/60; C08K3/34; C08K3/36
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
168 words
An improvement in the composition of particulate, water-insoluble alkali metal carboxylate salts of starch-acrylonitrile graft copolymers of the type which are produced by saponifying a starch-acrylonitrile graft copolymer with an alkali metal base in an aqueous alcoholic medium and which particulate copolymer in its unimproved form is capable of absorbing in excess of 50 parts by weight of aqueous fluids per part of copolymer, and in which the molar ratio of the acrylonitrile to the starch in the graft copolymers is in the range of 2:1 to 30:1; said improvement comprising modifying said particulate copolymer by mixing therewith a minor quantity of a fumed oxide selected from the group consisting of fumed silica or fumed alumina in an amount sufficient to increase the rate at which said modified copolymer absorbs saline physiological fluids as compared to the rate at which said unimproved copolymer absorbs said fluids without reducing significantly the total absorbent capacity otherwise exhibited by said unimproved copolymer while minimizing the tendency of said copolymer to dust.
Claim 2
Dependent Claim
168 words
An improvement in the composition of particulate, water-insoluble alkali metal carboxylate salts of starch-acrylonitrile graft copolymers of the type which are produced by saponifying a starch-acrylonitrile graft copolymer with an alkali metal base in an aqueous alcoholic medium and which particulate copolymer in its unimproved form is capable of absorbing in excess of 50 parts by weight of aqueous fluids per part of copolymer, and in which the molar ratio of the acrylonitrile to the starch in the graft copolymers is in the range of 2:1 to 30:1; said improvement comprising modifying said particulate copolymer by mixing therewith a minor quantity of a fumed oxide selected from the group consisting of fumed silica or fumed alumina in an amount sufficient to increase the rate at which said modified copolymer absorbs saline physiological fluids as compared to the rate at which said unimproved copolymer absorbs said fluids without reducing significantly the total absorbent capacity otherwise exhibited by said unimproved copolymer while minimizing the tendency of said copolymer to dust.
Claim 3
Dependent Claim
202 words
An improvement in a water-insoluble, particulate form, alkali metal carboxylate salt of a starch-polyacrylonitrile graft copolymer or a starch-polymethacrylonitrile graft copolymer which copolymer in particulate form is capable of absorbing in excess of 50 parts by weight of aqueous fluids per part of copolymer while maintaining insolubility and which copolymer has been produced by saponifying a starch-polyacrylonitrile or starch-polymethacrylonitrile graft copolymer with an aqueous methanolic or ethanolic solution of an alkali base selected from the group consisting of sodium hydroxide, lithium hydroxide or potassium hydroxide, and in which the molar ratio of the acrylonitrile or methacrylonitrile to the starch in the graft copolymer is in the range of 2:1 to 30:1; said improvement comprising modifying said particulate copolymer by combining and mixing therewith a minor quantity of a fumed oxide selected from the group consisting of fumed silica or fumed alumina, said quantity being in an amount sufficient to markedly increase the rate at which said modified copolymer absorbs saline physiological fluids as compared to the rate at which said particulate copolymer in its unimproved state absorbs said fluids while minimizing the tendency of said copolymer to dust and without reducing significantly the total absorbent capacity otherwise exhibited by said unimproved copolymer.
Claim 4
Dependent Claim
202 words
An improvement in a water-insoluble, particulate form, alkali metal carboxylate salt of a starch-polyacrylonitrile graft copolymer or a starch-polymethacrylonitrile graft copolymer which copolymer in particulate form is capable of absorbing in excess of 50 parts by weight of aqueous fluids per part of copolymer while maintaining insolubility and which copolymer has been produced by saponifying a starch-polyacrylonitrile or starch-polymethacrylonitrile graft copolymer with an aqueous methanolic or ethanolic solution of an alkali base selected from the group consisting of sodium hydroxide, lithium hydroxide or potassium hydroxide, and in which the molar ratio of the acrylonitrile or methacrylonitrile to the starch in the graft copolymer is in the range of 2:1 to 30:1; said improvement comprising modifying said particulate copolymer by combining and mixing therewith a minor quantity of a fumed oxide selected from the group consisting of fumed silica or fumed alumina, said quantity being in an amount sufficient to markedly increase the rate at which said modified copolymer absorbs saline physiological fluids as compared to the rate at which said particulate copolymer in its unimproved state absorbs said fluids while minimizing the tendency of said copolymer to dust and without reducing significantly the total absorbent capacity otherwise exhibited by said unimproved copolymer.
Claim 5
Dependent Claim
29 words
The improved copolymer composition of claim 2 wherein said fumed oxide is added in the amount of in the range of about 1 percent to 10 percent by weight.
Claim 6
Dependent Claim
22 words
The improved copolymer composition of claim 2 wherein said fumed oxide is added in the amount of about 2 percent by weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-12 | 1979-07-14 | 1980-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-12 | 1983-07-14 | 1984-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-12 | 1987-07-14 | 1988-01-13 | $7700.00 | Window Closed / Lapsed |