Process for de-inking printed waste cellulosic fibrous material

Claim 2

A process for de-inking waste, printed cellulosic fibrous material which comprises the following steps: a. Adding waste, printed, cellulosic fibrous material to a de-inking solution comprising (1) water, (2) a de-inking agent which is biodegradable and non-toxic to aquatic life and is selected from the group consisting of ethoxylated aliphatic di-ols having from 14 to 30 carbon atoms in the aliphatic chain and from 8 to 24 ethyleneoxy units per mole of di-ols and wherein the hydroxy groups in the di-ols are present on adjacent non-terminal carbon atoms in the aliphatic chain; and (3) a material present in sufficient quantity to maintain an alkaline pH of the de-inking solution between about 7.0 and 11.5; b. Contacting said printed material with the de-inking solution until the ink separates from the fibers; and c. Washing the de-inked cellulosic fibrous material.

Claim 3

A process as defined in claim 1 wherein said di-ol has from 15 to 17 carbon atoms in the aliphatic chain and from 9 to 11 ethyleneoxy units per mole of said di-ol.

Claim 4

A process as defined in claim 1 wherein the printed cellulosic material is present in an amount below about 10% by weight of the aqueous solution, and the de-inking agent is present in an amount between about 0.3 and 3% based upon the weight of the cellulosic material.

Claim 5

A process as defined in claim 3 wherein said di-ol has an average of from 15 to 17 carbon atoms in the aliphatic chain and from about 9 to 11 ethyleneoxy units per mole of said di-ol.

Claim 6

A process as defined in claim 3 wherein the process is carried out at a temperature between about 40°F to about 200°F, said alkaline material is selected from alkali metal hydroxides and silicates and wherein after the washing step the pH of the cellulosic material is reduced to between about 4.0 and 6.5.

Claim 7

A process as defined in claim 1 wherein the pH of the cellulosic material is reduced to between about 4.0 and 6.5 following washing.

Claim 8

A process as defined in claim 1 wherein said process is carried out at a temperature between about 40°F to about 200°F.

Claim 9

A process as defined in claim 1 wherein said material for maintaining alkaline pH is selected from the group consisting of alkali metal or alkaline earth metal hydroxides and salts.

Claim 10

A process for de-inking waste, printed cellulosic fibrous material to produce a pulp for use in making newsprint, which comprises the following steps: a. Adding waste, printed, cellulosic fibrous material to a de-inking solution comprising (1) water, (2) a de-inking agent which is biodegradable and non-toxic to aquatic life and is selected from the group consisting of ethoxylated aliphatic mono-ols having about 14 to 15 carbon atoms in the aliphatic chain and about 8 to 12 ethyleneoxy units per mole of said mono-ol; and (3) a material present in sufficient quantity to maintain an alkaline pH of the de-inking solution between about 7.0 and 11.5; b. Contacting said prinited cellulosic material with the de-inking solution until the ink separates from the fibers; c. Diluting the cellulosic material in the solution by adding water in sufficient amount to reduce the solids content to between about 0.5 to 1.5 percent based upon the solution weight; and d. Washing the de-inked diluted cellulosic material.

Claim 11

A process for de-inking waste, printed cellulosic fibrous material to produce a pulp for use in making newsprint, which comprises the following steps: a. Adding waste, printed, cellulosic fibrous material to a de-inking solution comprising (1) water, (2) a de-inking agent which is biodegradable and non-toxic to aquatic life and is selected from the group consisting of ethoxylated aliphatic mono-ols having about 14 to 15 carbon atoms in the aliphatic chain and about 8 to 12 ethyleneoxy units per mole of said mono-ol; and (3) a material present in sufficient quantity to maintain an alkaline pH of the de-inking solution between about 7.0 and 11.5; b. Contacting said prinited cellulosic material with the de-inking solution until the ink separates from the fibers; c. Diluting the cellulosic material in the solution by adding water in sufficient amount to reduce the solids content to between about 0.5 to 1.5 percent based upon the solution weight; and d. Washing the de-inked diluted cellulosic material.

Claim 12

A process as defined in claim 9 wherein said process is carried out at a temperature between about 40°F to about 200°F.

Claim 13

A process as defined in claim 9 wherein said material for maintaining alkaline pH is selected from the group consisting of alkali metal or alkaline earth metal hydroxides and alkali metal silicates.

Claim 14

A process as defined in claim 9 wherein the printed cellulosic material is present in an amount below about 10% by weight of the aqueous solution, and the de-inking agent is present in an amount between about 0.3 and 3% based upon the weight of the cellulosic material.

Claim 15

A process as defined in claim 12 wherein the amount of printed cellulosic fibrous material added to the de-inking solution is between about 4.0 and 6.0 percent by weight of the solution.

Claim 16

A process as defined in claim 9 wherein the pH of the cellulosic material is reduced to between about 4.0 and 6.5 following washing.

Claim 17

A process as defined in claim 9 wherein said de-inking agent is an ethoxylated aliphatic primary mono-ol.

Claim 18

A process as defined in claim 15 wherein said mono-ol is an ethoxylated aliphatic primary mono-ol having an average of from 14 to 15 carbon atoms in the aliphatic chain and an average of from 9 to 11 ethyleneoxy units per mole of said mono-ol.

Claim 19

A process as defined in Claim 15 wherein the printed cellulosic material is present in an amount below about 10% by weight of the aqueous solution, the de-inking agent is present in an amout between about 0.3 and 3% based upon the weight of the cellulosic material, said material for maintaining alkaline pH is selected from the group consisting of alkali metal or alkaline earth metal hydroxides and alkali metal silicates and wherein said process is carried out at a temperature between about 40°F to about 200°F.

Claim 20

A process for de-inking waste, printed cellulosic fibrous material to produce a pulp for use in making newsprint which comprises the following steps: a. Adding waste, printed, cellulosic fibrous material to a de-inking solution comprising (1) water, (2) a de-inking agent which is biodegradable and non-toxic to aquatic life and is selected from the group consisting of ethoxylated aliphatic mono-ols having about 14 to 15 carbon atoms in the aliphatic chain and about 8 to 12 ethyleneoxy units per mole of said mono-ol, and (3) a material present in sufficient quantity to maintain an alkaline pH of the de-inking solution between about 7.0 and 11.5; b. Contacting said printed material with the de-inking solution until the ink separates from the fibers; c. Washing the de-inked cellulosic material with water; and d. Acidifying said washed de-inked cellulosic material by reducing its pH to between about 4.0 and 6.5.

Claim 21

A process for de-inking waste, printed cellulosic fibrous material to produce a pulp for use in making newsprint which comprises the following steps: a. Adding waste, printed, cellulosic fibrous material to a de-inking solution comprising (1) water, (2) a de-inking agent which is biodegradable and non-toxic to aquatic life and is selected from the group consisting of ethoxylated aliphatic mono-ols having about 14 to 15 carbon atoms in the aliphatic chain and about 8 to 12 ethyleneoxy units per mole of said mono-ol, and (3) a material present in sufficient quantity to maintain an alkaline pH of the de-inking solution between about 7.0 and 11.5; b. Contacting said printed material with the de-inking solution until the ink separates from the fibers; c. Washing the de-inked cellulosic material with water; and d. Acidifying said washed de-inked cellulosic material by reducing its pH to between about 4.0 and 6.5.

Claim 22

A process as defined in claim 18 wherein said process is carried out at a temperature between about 40°F to about 200°F.

Claim 23

A process as defined in claim 18 wherein said material for maintaining alkaline pH is selected from the group consisting of alkali metal or alkaline earth metal hydroxides and salts.

Claim 24

A process as defined in claim 18 wherein the printed cellulosic material is present in an amount below about 10% by weight of the aqueous solution, and the de-inking agent is present in an amount between about 0.3 and 3% based upon the weight of the cellulosic material.

Claim 25

A process as defined in claim 18 wherein said de-inking agent is an ethoxylated aliphatic primary mono-ol.

Claim 26

A process as defined in claim 22 wherein said mono-ol is an ethoxylated aliphatic primary mono-ol having from 14 to 15 carbon atoms in the aliphatic chain and from 9 to 11 ethyleneoxy units per mole of said mono-ol.

Claim 27

A process as defined in claim 22 wherein the printed cellulosic material is present in an amount below about 10% by weight of the aqueous solution, the de-inking agent is present in an amount between about 0.3 and 3% based upon the weight of the cellulosic material, said material for maintaining alkaline pH is selected from the group consisting of alkali metal or alkaline earth metal hydroxides and alkali metal silicates and wherein said process is carried out at a temperature between about 40°F to about 200°F.

Claim 28

A process as defined in claim 18 wherein after contacting and before washing, the cellulosic material is diluted by the addition of water to the solution in sufficient amount to reduce the solids content to between about 0.5 to 1.5 percent based upon the solution weight.

Claim 29

A process for de-inking waste, printed paper to produce a pulp for use in making newsprint, which comprises the following steps: a. Adding waste, printed paper to a de-inking solution consisting essentially of (1) water, (2) a de-inking agent which is biodegradable and non-toxic to aquatic life and is selected from the group consisting of ethoxylated aliphatic mono-ols having about 14 to 15 carbon atoms in the aliphatic chain and from about 8 to 12 ethyleneoxy units per mole of said mono-ols; and (3) an alkaline material selected from the group consisting of alkali metal and alkaline earth metal hydroxides and alkali metal silicates present in sufficient quantity to maintain the alkaline pH of the de-inking solution between about 7.0 and 11.5; b. Contacting said waste paper with the de-inking solution until the ink separates from the waste paper fibers; c. Diluting the waste paper fibers in the solution by adding water in sufficient amount to reduce the solids content to between about 0.5 to 1.5 percent based upon the solution weight; and d. Washing the diluted paper fibers.

Claim 30

A process for de-inking waste, printed paper to produce a pulp for use in making newsprint, which comprises the following steps: a. Adding waste, printed paper to a de-inking solution consisting essentially of (1) water, (2) a de-inking agent which is biodegradable and non-toxic to aquatic life and is selected from the group consisting of ethoxylated aliphatic mono-ols having about 14 to 15 carbon atoms in the aliphatic chain and from about 8 to 12 ethyleneoxy units per mole of said mono-ols; and (3) an alkaline material selected from the group consisting of alkali metal and alkaline earth metal hydroxides and alkali metal silicates present in sufficient quantity to maintain the alkaline pH of the de-inking solution between about 7.0 and 11.5; b. Contacting said waste paper with the de-inking solution until the ink separates from the waste paper fibers; c. Diluting the waste paper fibers in the solution by adding water in sufficient amount to reduce the solids content to between about 0.5 to 1.5 percent based upon the solution weight; and d. Washing the diluted paper fibers.

Claim 31

A process as defined in claim 26 wherein the de-inking agent is an ethoxylated aliphatic primary mono-ol.

Claim 32

A process as defined in claim 26 wherein the printed paper is present in an amount below about 10% by weight of the aqueous solution, the de-inking agent is present in an amount between about 0.3 and 3% based upon the weight of the paper, and wherein said process is carried out at a temperature between about 40°F to about 200°F.

Claim 33

A process as defined in claim 28 wherein the pH of the paper fibers is reduced to between about 4.0 and 6.5 following washing.