US3931380A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making nestable foamed plastic cups
Assignee: Georgia Pacific Consumer Products LP
•
Filing: 1973-12-26
•
Granted: 1976-01-06
•
Expires: 1993-12-26
Abstract
Abstract Cups having a sidewall made from foam sheet plastic with a fusion sealed, lapped seam, wherein the lapped seam and the sidewall immediately adjacent the lapped seam are of identical thickness, are provided with additional rigidity per unit wall thickness by compressing the foam sheet either in-line with the foam extrusion operation or up to several months after extrusion. The cup is characterized by a substantial skin on only the outer surface of the sidewall.
Inventors
- 👤 Ilie Mila Belivakici
- 👤 Clifford Clayton Goehring
- 👤 James Alan Wachtel
- 👤 William Joseph Lahm
- 👤 Carl Richard Storms
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 02:29
CPC Classifications
B; B29; B29C; B29C66/00; B29C66/01; B29C66/03; B29C66/032; B29C66/0324; B29C66/03241; B29C44/00; B29C44/34; B29C44/56; B29C44/5627; B29C44/5636; B29C65/00; B29C65/02; B29C66/05; B29C66/10; B29C66/12; B29C66/128; B29C66/1282; B29C66/1284; B29C66/12841; B29C66/40; B29C66/41; B29C66/43; B29C66/432; B29C66/4322; B29C66/50; B29C66/51; B29C66/54; B29C66/542; B29C66/545; B29C66/70; B29C66/72; B29C66/727; B65; B65D; B65D11/00; B65D11/02; B29C66/11; B29C66/112; B29C66/1122; B29C66/71; B29K; B29K2105/00; B29K2105/04; B29K2105/25; B29K2105/253; B29K2105/256; B29L; B29L2031/00; B29L2031/712; B29L2031/7132
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
275 words
A method of making from foamed plastic sheet material a molded, lapped seam, fused cup having wall portions thinner than the initial sheet material, leakproof seals between the bottom and sidewalls and wherein the seam and the sidewall are of identical thickness comprising the steps of: 1. providing an extruded, foamed plastic sheet material having a density of about 16 to 17 lbs./ft. 3 and a substantial skin on its outer surface only, a density gradient wherein the cell size of said sheet increases inwardly from said outer surface and a thickness greater than the final sidewall thickness; 2. comprising said extruded sheet to a thickness less than that of the final sidewall thereby decreasing the cell size variation; 3. forming a blank from said compressed sheet of suitable shape and size to form the sidewall of said cup; 4. providing mold means comprising female and male mold members; 5. positioning said sidewall blank in said female mold member; 6. positioning a blank of suitable shape and size to form the bottom wall of said cup on said male mold member; 7. joining said mold members sufficiently to form a mold cavity wherein the mold members are spaced an amount greater than the thickness of said compressed sidewall blank and equal to the thickness of the final sidewall of said cup; and 8. fusing said sidewall and bottom wall blanks thus positioned in said mold cavity in the presence of steam to expand said compressed sheet into the space between said mold members to form a cup having a sidewall increased in thickness and decreased in cell size variation from that of the compressed sheet.
Claim 2
Independent Claim
275 words
A method of making from foamed plastic sheet material a molded, lapped seam, fused cup having wall portions thinner than the initial sheet material, leakproof seals between the bottom and sidewalls and wherein the seam and the sidewall are of identical thickness comprising the steps of: 1. providing an extruded, foamed plastic sheet material having a density of about 16 to 17 lbs./ft. 3 and a substantial skin on its outer surface only, a density gradient wherein the cell size of said sheet increases inwardly from said outer surface and a thickness greater than the final sidewall thickness; 2. comprising said extruded sheet to a thickness less than that of the final sidewall thereby decreasing the cell size variation; 3. forming a blank from said compressed sheet of suitable shape and size to form the sidewall of said cup; 4. providing mold means comprising female and male mold members; 5. positioning said sidewall blank in said female mold member; 6. positioning a blank of suitable shape and size to form the bottom wall of said cup on said male mold member; 7. joining said mold members sufficiently to form a mold cavity wherein the mold members are spaced an amount greater than the thickness of said compressed sidewall blank and equal to the thickness of the final sidewall of said cup; and 8. fusing said sidewall and bottom wall blanks thus positioned in said mold cavity in the presence of steam to expand said compressed sheet into the space between said mold members to form a cup having a sidewall increased in thickness and decreased in cell size variation from that of the compressed sheet.
Claim 3
Dependent Claim
50 words
The method of claim 1 wherein said plastic foam sheet material having a substantial skin on its outer surface and density gradient provided in step (1) is obtained by extruding foam plastic through an orifice and impinging cooling air on the outer surface of said sheet as it is extruded.
Claim 4
Dependent Claim
33 words
The method of claim 1 wherein the thickness of said sheet material is about 35 to 40 mils as extruded, about 23 to 26 mils as compressed and about 30 mils after molding.
Claim 5
Dependent Claim
10 words
The method of claim 1 wherein the plastic is polystyrene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-05 | 1979-07-07 | 1980-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-05 | 1983-07-07 | 1984-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-05 | 1987-07-07 | 1988-01-06 | $7700.00 | Window Closed / Lapsed |