Assignee: Xerox Corp
•
Filing: 1974-04-26
•
Granted: 1976-01-06
•
Expires: 1994-04-26
Abstract
Abstract A highly reversion resistant polyisoprene elastomer composition vulcanized with a low sulfur content is described and used in paper feed belts. The polyisoprene rubber compositions are particularly useful in the paper feed belts used to feed and transport paper in xerographic machines and paper sorting machines. The low-sulfur vulcanizate of isoprene provides high resistance to physical degradation due to dynamic mechanical stress under operating conditions.
Inventors
- 👤 Paul C. Amatangelo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:50
CPC Classifications
C; C08; C08L; C08L9/00; C08K; C08K5/00; C08K5/0008; C08K5/0025; C08K5/36; C08K5/39; C08K5/40; C08K5/43; C08K5/44; C08L81/00; C08L81/04
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
196 words
A composition for manufacture of belts used to feed or transport substrate material, said belts being characterized by resistance to overcure reversion, by a high coefficient of friction for said substrate material and by a high resistance to physical degradation due to dynamic mechanical stress, comprising, synthetic polyisoprene; about 6.0 to about 15.0 parts by weight metallic oxide per 100 parts of polyisoprene; about 1.0 to about 5.0 parts by weight fatty acid per 100 parts of polyisoprene; 0.0 to about 2.0 parts by weight antioxidant per 100 parts polyisoprene and sulfur-containing cure ingredients and accelerators comprising about 0.5 to about 1.5 parts by weight of at least one organic polysulfide chosen from the group consisting of the dimorpholine polysulfides and the liquid aliphatic polysulfides per 100 parts of polyisoprene, about 0.5 to about 1.5 parts by weight of at least one sulfenamide accelerator per 100 parts of polyisoprene, about 0.5 to about 1.0 part by weight of at least one thiuram sulfide of the type having at least two sulfide groups or mercaptobenzothiazyl disulfide, accelerator per 100 parts of polyisoprene, and about 0.1 to about 1.3 parts by weight sulfur per 100 parts of polyisoprene.
Claim 2
Dependent Claim
196 words
A composition for manufacture of belts used to feed or transport substrate material, said belts being characterized by resistance to overcure reversion, by a high coefficient of friction for said substrate material and by a high resistance to physical degradation due to dynamic mechanical stress, comprising, synthetic polyisoprene; about 6.0 to about 15.0 parts by weight metallic oxide per 100 parts of polyisoprene; about 1.0 to about 5.0 parts by weight fatty acid per 100 parts of polyisoprene; 0.0 to about 2.0 parts by weight antioxidant per 100 parts polyisoprene and sulfur-containing cure ingredients and accelerators comprising about 0.5 to about 1.5 parts by weight of at least one organic polysulfide chosen from the group consisting of the dimorpholine polysulfides and the liquid aliphatic polysulfides per 100 parts of polyisoprene, about 0.5 to about 1.5 parts by weight of at least one sulfenamide accelerator per 100 parts of polyisoprene, about 0.5 to about 1.0 part by weight of at least one thiuram sulfide of the type having at least two sulfide groups or mercaptobenzothiazyl disulfide, accelerator per 100 parts of polyisoprene, and about 0.1 to about 1.3 parts by weight sulfur per 100 parts of polyisoprene.
Claim 3
Dependent Claim
12 words
The composition of claim 1 wherein said fatty acid is stearic acid.
Claim 4
Dependent Claim
31 words
The composition of Claim 1 wherein said anti-oxidant is selected from the group consisting of 2,2'-bis(4-methyl-6-tertiary-butyl phenol; 2,2'-methylene bis (4-ethyl-6-tertiary-butyl phenol; hydroquinone; and a mixture of di-para-methoxydiphenylamine, diphenyl-para-phenylene diamine, and phenyl-beta-naphthyl-amine.
Claim 5
Dependent Claim
21 words
The composition of claim 1 wherein the sulfenamide accelerator is selected from the group consisting of N-cyclohexyl-2-benzothiazole sulfenamide and N-tertiary-butyl-2-benzothiazole sulfenamide.
Claim 6
Dependent Claim
23 words
The composition of claim 1 wherein the thiuram sulfide accelerator is selected form the group consisting of tetramethyl thiuram disulfide and mercaptobenzothiazyl disulfide.
Claim 7
Dependent Claim
12 words
The composition of claim 1 wherein the metallic oxide is zinc oxide.
Claim 8
Dependent Claim
11 words
The composition of claim 1 wherein the organic polysulfide is 4,4'-dithiodimorpholine.
Claim 9
Dependent Claim
187 words
A belt material for the manufacture of flexible paper feed belts in sheet feeders, transporters or separators in xerographic machines made by the process of: a. adding to synthetic isoprene rubber gum about 6.0 to about 15.0 parts by weight zinc oxide per 100 parts of said gum; about 1.0 to about 5.0 parts by weight fatty acid per 100 parts of said gum; 0.0 to about 2.0 parts by weight anti-oxidant per 100 parts of said gum; and sulfur-containing cure and accelerator ingredients consisting essentially of about 0.5 to about 1.5 parts by weight 4,4'-dithiodimorpholine per 100 parts of said gum; about 0.5 to about 1.5 parts by weight of a sulfenamide accelerator per 100 parts of said gum, about 0.5 to about 1.5 parts by weight of thiuram sulfide of the type having at least two sulfide groups or mercaptobenzothiazyl disulfide, accelerator per 100 parts of said gum; and 0.0 to about 1.3 parts by weight sulfur per 100 parts of said gum; and b. working the ingredients of (a) into said gum to form a blend of the ingredients and the isoprene rubber gum.
Claim 10
Dependent Claim
187 words
A belt material for the manufacture of flexible paper feed belts in sheet feeders, transporters or separators in xerographic machines made by the process of: a. adding to synthetic isoprene rubber gum about 6.0 to about 15.0 parts by weight zinc oxide per 100 parts of said gum; about 1.0 to about 5.0 parts by weight fatty acid per 100 parts of said gum; 0.0 to about 2.0 parts by weight anti-oxidant per 100 parts of said gum; and sulfur-containing cure and accelerator ingredients consisting essentially of about 0.5 to about 1.5 parts by weight 4,4'-dithiodimorpholine per 100 parts of said gum; about 0.5 to about 1.5 parts by weight of a sulfenamide accelerator per 100 parts of said gum, about 0.5 to about 1.5 parts by weight of thiuram sulfide of the type having at least two sulfide groups or mercaptobenzothiazyl disulfide, accelerator per 100 parts of said gum; and 0.0 to about 1.3 parts by weight sulfur per 100 parts of said gum; and b. working the ingredients of (a) into said gum to form a blend of the ingredients and the isoprene rubber gum.
Claim 11
Dependent Claim
31 words
The belt material made by the process of claim 8 further comprising forming the uniformly dispersed blend into a shape suitable for flexible belts and curing said blend at elevated temperatures.
Claim 12
Dependent Claim
27 words
The belt material made by the process of claim 9 wherein the blend is cured by exposing said blend to heat at about 300°F., to about 340°F.
Claim 13
Dependent Claim
23 words
The belt material made by the process of claim 8 wherein the ingredients of step (b) are pre-mixed and added to said gum.
Claim 14
Dependent Claim
27 words
The belt material made by the process of claim 8 wherein the sulfur-containing cure and accelerator ingredients of step (b) are pre-mixed and added to said gum.
Claim 15
Dependent Claim
17 words
The belt material made by the process of claim 8 wherein the fatty acid is stearic acid.
Claim 16
Dependent Claim
32 words
The belt material made by the process of claim 8 wherein the anti-oxidant is selected from the group consisting of diarylamines, hydroquinones, aldehyde-amines, substituted phenols, bis phenols and mixtures of aromatic amines.
Claim 17
Dependent Claim
26 words
The belt material made by the process of claim 8 wherein the sulfenamide accelerator is selected from the group consisting of N-cyclohexyl-2-benzothiazole sulfenamide and N-tertiary-butyl-2-benzothiazole sulfenamide.
Claim 18
Dependent Claim
28 words
The belt material made by the process of claim 8 wherein the thiuram sulfide accelerator is selected from the group consisting of tetramethyl thiuram disulfide and mercaptobenzothiazyl disulfide.
Claim 19
Dependent Claim
46 words
The belt material made by the process of claim 8 further comprising adding up to 15.0 parts by weight reinforcing fillers or plasticizer or both per 100 parts of said gum, said fillers or plasticizers comprising ingredients having no effect on the curing of the gum.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-05 | 1979-07-07 | 1980-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-05 | 1983-07-07 | 1984-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-05 | 1987-07-07 | 1988-01-06 | $7700.00 | Window Closed / Lapsed |