Catalyst for conversion of hydrocarbons and method of preparing same
Assignee: Individual
•
Filing: 1974-04-18
•
Granted: 1976-01-06
•
Expires: 1994-04-18
Abstract
Abstract According to the invention, the catalyst contains oxides of nickel (25 per cent by weight), of aluminium (50 per cent by weight), of magnesium (14 per cent by weight), of calcium (10 per cent by weight) and of barium (1 per cent by weight), and the method of preparing it consists in that nickel carbonate, oxide or hydroxide of aluminium, and magnesium oxide pre-calcined at a temperature of 1300°±50°C, are mixed with an aqueous solution of nickel nitrate and of barium oxide; the obtained mixture is dried and calcined, and to the obtained mixture of the metal oxides are added a binding agent (calcium aluminate), a lubricating agent (potassium stearate), and a wetting agent (water or an aqueous solution of sulphosalicylic acid or of triethanolamine); the prepared mixture is pressed into tablets and the latter are hardened hydraulically, dried and calcined. The invention can be used in petrochemical synthesis.
Inventors
- 👤 Evgeny Vasilievich Kazakov
- 👤 Igor Fedorovich Balitsky
- 👤 Viktor Stanislavovich Sobolevsky
- 👤 Vladimir Petrovich Semenov
- 👤 Galina Nikiforovna Kashirina
- 👤 Natalya Alexandrovna Kruglikova
- 👤 Viktor Ivanovich Yagodkin
- 👤 Mikhail Arkadievich Shpolyansky
- 👤 Sergei Ivanovich Ruzinsky
- 👤 Igor Dmitrievich Gorbachevich
- 👤 Ivan Emanuilovich Gergert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:18
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/70; B01J23/76; B01J23/78; C; C01; C01B; C01B3/00; C01B3/02; C01B3/32; C01B3/34; C01B3/38; C01B3/40; C01B2203/00; C01B2203/10; C01B2203/1041; C01B2203/1047; C01B2203/1052; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/52
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
11 words
A catalyst for conversion of hydrocarbons consisting of a mixture of
Claim 2
Dependent Claim
11 words
A catalyst for conversion of hydrocarbons consisting of a mixture of
Claim 3
Dependent Claim
30 words
A catalyst for conversion of hydrocarbons according to claim 1, having the following composition, in per cent by weight: NiO 25
Al.sub.2 O.sub.3 50
MgO 14
CaO 10
BaO 1
Claim 4
Independent Claim
150 words
A method of preparing a catalyst for conversion of hydrocarbons, containing oxides of nickel, aluminium, magnesium, calcium, and of barium, consisting in that 21.5 parts by weight of basic nickel carbonate, an aluminium compound, selected from the group, consisting of aluminium oxide and aluminium hydroxide, and 15 parts by weight of magnesium oxide, pre-calcined at a temperature of 1300°±50°C, are mixed with an aqueous solution containing 56 parts by weight of nickel nitrate and an aqueous solution, containing 1 part by weight of barium oxide; the prepared mixture is dried, and calcined at a temperature of 380°C; to the obtained mixture of the metal oxides are added a binding agent, a lubricating agent and a wetting agent, selected from the group, consisting of water, an aqueous solution of sulphosalicylic acid and an aqueous solution of triethanolamine; the prepared catalyst mixture is compacted, granulated, and tabletted; the obtained tablets are hardened
Claim 5
Independent Claim
150 words
A method of preparing a catalyst for conversion of hydrocarbons, containing oxides of nickel, aluminium, magnesium, calcium, and of barium, consisting in that 21.5 parts by weight of basic nickel carbonate, an aluminium compound, selected from the group, consisting of aluminium oxide and aluminium hydroxide, and 15 parts by weight of magnesium oxide, pre-calcined at a temperature of 1300°±50°C, are mixed with an aqueous solution containing 56 parts by weight of nickel nitrate and an aqueous solution, containing 1 part by weight of barium oxide; the prepared mixture is dried, and calcined at a temperature of 380°C; to the obtained mixture of the metal oxides are added a binding agent, a lubricating agent and a wetting agent, selected from the group, consisting of water, an aqueous solution of sulphosalicylic acid and an aqueous solution of triethanolamine; the prepared catalyst mixture is compacted, granulated, and tabletted; the obtained tablets are hardened
Claim 6
Independent Claim
226 words
A method of preparing the catalyst for conversion of hydrocarbons, containing oxides of nickel, aluminium, magnesium, calcium, and of barium, consisting in that 21.5 parts by weight of basic nickel carbonate, an aluminium compound, selected from the group, consisting of aluminium oxide taken in the quantity of 25 parts by weight and aluminium hydroxide taken in the quantity of 38 parts by weight, 15 parts by weight of magnesium oxide, pre-calcined at a temperature of 1300°±50°C, a binding agent of calcium dialuminate, taken in the quantity of 50 per cent with respect to the total quantity of the binding agent in the catalyst, are mixed with an aqueous solution, containing 56 parts by weight of nickel nitrate and an aqueous solution, containing 1 part by weight of barium oxide; the prepared mixture is dried and calcined at a temperature of 380°C; to the obtained mixture of the metal oxides are added the other 50 per cent of the binding agent, selected from the group, consisting of calcium monoaluminate and calcium dialuminate, so that the total quantity of the binding agent is 40 parts by weight, a lubricating agent of potassium stearate, and a wetting agent selected from the group, consisting of water, aqueous solution of sulphosalicylic acid, and aqueous solution of triethanolamine; the prepared catalyst mixture is compacted, granulated, and tabletted; the obtained tablets are hardened
Claim 7
Independent Claim
226 words
A method of preparing the catalyst for conversion of hydrocarbons, containing oxides of nickel, aluminium, magnesium, calcium, and of barium, consisting in that 21.5 parts by weight of basic nickel carbonate, an aluminium compound, selected from the group, consisting of aluminium oxide taken in the quantity of 25 parts by weight and aluminium hydroxide taken in the quantity of 38 parts by weight, 15 parts by weight of magnesium oxide, pre-calcined at a temperature of 1300°±50°C, a binding agent of calcium dialuminate, taken in the quantity of 50 per cent with respect to the total quantity of the binding agent in the catalyst, are mixed with an aqueous solution, containing 56 parts by weight of nickel nitrate and an aqueous solution, containing 1 part by weight of barium oxide; the prepared mixture is dried and calcined at a temperature of 380°C; to the obtained mixture of the metal oxides are added the other 50 per cent of the binding agent, selected from the group, consisting of calcium monoaluminate and calcium dialuminate, so that the total quantity of the binding agent is 40 parts by weight, a lubricating agent of potassium stearate, and a wetting agent selected from the group, consisting of water, aqueous solution of sulphosalicylic acid, and aqueous solution of triethanolamine; the prepared catalyst mixture is compacted, granulated, and tabletted; the obtained tablets are hardened
Claim 8
Dependent Claim
26 words
A method according to claim 3, in which potassium stearate is taken in the quantity of 0.5-2.0 per cent of dry weight of the catalyst mixture.
Claim 9
Dependent Claim
26 words
A method according to claim 4, in which potassium stearate is taken in the quantity of 0.5-2.0 per cent of dry weight of the catalyst mixture.
Claim 10
Dependent Claim
26 words
A method according to claim 3, in which sulphosalicylic acid is taken in the quantity of 0.06-0.75 per cent of dry weight of the catalyst mixture.
Claim 11
Dependent Claim
26 words
A method according to claim 4, in which sulphosalicylic acid is taken in the quantity of 0.06-0.75 per cent of dry weight of the catalyst mixture.
Claim 12
Dependent Claim
13 words
A method according to claim 3, in which triethanolamine is taken in the
Claim 13
Dependent Claim
25 words
A method according to claim 4, in which triethanolamine is taken in the quantity of 0.03-0.45 per cent of dry weight of the catalyst mixture.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-05 | 1979-07-07 | 1980-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-05 | 1983-07-07 | 1984-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-05 | 1987-07-07 | 1988-01-06 | $7700.00 | Window Closed / Lapsed |