US3930876A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Inorganic coating composition
Assignee: Kansai Paint Co Ltd
•
Filing: 1974-06-17
•
Granted: 1976-01-06
•
Expires: 1994-06-17
Abstract
Abstract An improved silicate-phosphate type inorganic coating composition having a long pot life or shelf life is provided which comprises a water soluble silicate or modified silicate and an inorganic phosphate pretreated with such silicate.
Inventors
- 👤 Jun Nakajima
- 👤 Hiroshi Iwai
- 👤 Iwao Momiyama
- 👤 Tatsuo Fukushima
- 👤 Rentaro Takeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 16:15
CPC Classifications
C; C09; C09D; C09D1/00; C09D1/02; C01; C01B; C01B25/00; C01B25/16; C01B25/26; C01B25/45
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
285 words
A method of preparing an aqueous coating composition which comprises mixing (A) a water soluble silicate selected from the group consisting of (1) silicates of the formula: M.sub.2 O.xSiO.sub.2 (I) wherein M represents a member selected from the group consisting of alkali metals, --N(CH 2 OH) 4 , --N(C 2 H 4 OH) 4 and --C(NH 2 ) 2 NH, and x is a number of from 0.5 to 5 inclusive, (2) silicates of the formula (I) modified with at least one of fluorides of silicofluorides of a metal selected from the group consisting of Ca, Al, Mg, Zn and Zr and (3) silicates of the formula (I) modified with at least one of oxides or hydroxides of a metal selected from the group consisting of Al, Ca, Mg, Zr, V, Zn and Cs, (B) a phosphate type hardener selected from the group consisting of condensed phosphates prepared by heating a mixture of the phosphate of the formula (II): M.sub.i O.sub.j.mP.sub.2 O.sub.5 (II) wherein M represents a metal selected from the group consisting of Al, Mg, Ca, Mn, Zn, Fe and Cu, i is 1 or 2 and j is 1 or 3 depending upon the valency (2 or 3) of the metal M and m is a number of from 0.25 to 4 inclusive with at least one double oxides of (i) at least one metal selected from Zn, Mg and Ca and (ii) at least one metal selected from transition metals and metals belonging to Group IV of Periodic Table, the condensed phosphates having been pretreated with at least one of the said silicates (1) or modified silicates (2) and (3) before being mixed with the water soluble silicate (A) and (C) water.
Claim 2
Independent Claim
285 words
A method of preparing an aqueous coating composition which comprises mixing (A) a water soluble silicate selected from the group consisting of (1) silicates of the formula: M.sub.2 O.xSiO.sub.2 (I) wherein M represents a member selected from the group consisting of alkali metals, --N(CH 2 OH) 4 , --N(C 2 H 4 OH) 4 and --C(NH 2 ) 2 NH, and x is a number of from 0.5 to 5 inclusive, (2) silicates of the formula (I) modified with at least one of fluorides of silicofluorides of a metal selected from the group consisting of Ca, Al, Mg, Zn and Zr and (3) silicates of the formula (I) modified with at least one of oxides or hydroxides of a metal selected from the group consisting of Al, Ca, Mg, Zr, V, Zn and Cs, (B) a phosphate type hardener selected from the group consisting of condensed phosphates prepared by heating a mixture of the phosphate of the formula (II): M.sub.i O.sub.j.mP.sub.2 O.sub.5 (II) wherein M represents a metal selected from the group consisting of Al, Mg, Ca, Mn, Zn, Fe and Cu, i is 1 or 2 and j is 1 or 3 depending upon the valency (2 or 3) of the metal M and m is a number of from 0.25 to 4 inclusive with at least one double oxides of (i) at least one metal selected from Zn, Mg and Ca and (ii) at least one metal selected from transition metals and metals belonging to Group IV of Periodic Table, the condensed phosphates having been pretreated with at least one of the said silicates (1) or modified silicates (2) and (3) before being mixed with the water soluble silicate (A) and (C) water.
Claim 3
Dependent Claim
61 words
A method as claimed in claim 1 wherein the modified silicate (2) is prepared by mixing an aqueous solution of the silicate of the formula (I) with the fluoride or silico-fluoride and heating the mixture, the amount of the fluoride or silicofluoride being 0.5 - 10 parts by weight based on 100 parts by weight (as dry solid) of the silicate.
Claim 4
Dependent Claim
61 words
A method as claimed in claim 1 wherein the modified silicate (3) is prepared by mixing an aqueous solution of the silicate of the formula (I) with the oxide or hydroxide and heating the mixture, the amount of the oxide or hydroxide being 0.5 - 30 parts by weight based on 100 parts by weight (as dry solid) of the silicate.
Claim 5
Dependent Claim
56 words
A method as claimed in claim 1 wherein the condensed phosphate is prepared by mixing the phosphate of the formula (II) with the double oxide and heating the mixture at 100°- 400°C for 2 - 7 hours, the amount of the double oxide being 0.2 - 2.0 parts by weight per part of the phosphate (a).
Claim 6
Dependent Claim
55 words
A method as claimed in claim 1 wherein the pretreatment of the condensed phosphate is conducted by mixing the condensed phosphate with the silicate (1) or modified silicate (2) or (3) in an aqueous system in such a proportion that the resulting slurry would have a pH of 5 - 9.5, preferably 6 - 8.5.
Claim 7
Dependent Claim
37 words
A method as claimed in claim 1 wherein the pretreated condensed phosphate is used in an amount of 60 - 150 parts by weight per 100 parts of the silicate (1) or modified silicate (2) or (3).
Claim 8
Independent Claim
315 words
A method of forming an inorganic coating on a substrate which comprises applying to the surface of said substrate an aqueous coating composition prepared by mixing (A) a water soluble silicate selected from the group consisting of (1) silicates of the formula: M.sub.2 O.x SiO.sub.2 (I) wherein M represents a member selected from the group consisting of alkali metals, --N(CH 2 OH) 4 , --N(C 2 H 4 OH) 4 and --C(NH 2 ) 2 NH, and x is a number of from 0.5 to 5 inclusive, (2) silicates of the formula (I) modified with at least one of fluorides of silicofluorides of a metal selected from the group consisting of Ca, Al, Mg, Zn and Zr and (3) silicates of the formula (I) modified with at least one of oxides or hydroxides of a metal selected from the group consisting of Al, Ca, Mg, Zr, V, Zn, and Cs, (B) a phosphate type hardener selected from the group consisting of condensed phosphates prepared by heating a mixture of the phosphate of the formula (II): M.sub.i O.sub.j.mP.sub.2 O.sub.5 (II) wherein M represents a metal selected from the group consisting of Al, Mg, Ca, Mn, Zn, Fe and Cu, i is 1 or 2 and j is 1 or 3 depending upon the valency (2 or 3) of the metal M and m is a number of from 0.25 to 4 inclusive with at least one double oxides of (i) at least one metal selected from Zn, Mg and Ca and (ii) at least one metal selected from transition metals and metals belonging to Group IV of Periodic Table, the condensed phosphates having been pretreated with at least one of the said silicates (1) or modified silicates (2) and (3) before being mixed with the water soluble silicate (A) and (C) water; and baking the coated layer at a temperature of 150°-250°C until it is hardened.
Claim 9
Independent Claim
315 words
A method of forming an inorganic coating on a substrate which comprises applying to the surface of said substrate an aqueous coating composition prepared by mixing (A) a water soluble silicate selected from the group consisting of (1) silicates of the formula: M.sub.2 O.x SiO.sub.2 (I) wherein M represents a member selected from the group consisting of alkali metals, --N(CH 2 OH) 4 , --N(C 2 H 4 OH) 4 and --C(NH 2 ) 2 NH, and x is a number of from 0.5 to 5 inclusive, (2) silicates of the formula (I) modified with at least one of fluorides of silicofluorides of a metal selected from the group consisting of Ca, Al, Mg, Zn and Zr and (3) silicates of the formula (I) modified with at least one of oxides or hydroxides of a metal selected from the group consisting of Al, Ca, Mg, Zr, V, Zn, and Cs, (B) a phosphate type hardener selected from the group consisting of condensed phosphates prepared by heating a mixture of the phosphate of the formula (II): M.sub.i O.sub.j.mP.sub.2 O.sub.5 (II) wherein M represents a metal selected from the group consisting of Al, Mg, Ca, Mn, Zn, Fe and Cu, i is 1 or 2 and j is 1 or 3 depending upon the valency (2 or 3) of the metal M and m is a number of from 0.25 to 4 inclusive with at least one double oxides of (i) at least one metal selected from Zn, Mg and Ca and (ii) at least one metal selected from transition metals and metals belonging to Group IV of Periodic Table, the condensed phosphates having been pretreated with at least one of the said silicates (1) or modified silicates (2) and (3) before being mixed with the water soluble silicate (A) and (C) water; and baking the coated layer at a temperature of 150°-250°C until it is hardened.
References Cited (Backward Citations)
US3669699A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-05 | 1979-07-07 | 1980-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-05 | 1983-07-07 | 1984-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-05 | 1987-07-07 | 1988-01-06 | $7700.00 | Window Closed / Lapsed |