Radio-photoluminescence dosimeter glass of low energy dependence and method of manufacturing same

Claim 2

A radio-photoluminescence dosimeter glass of low dependence on energy, consisting essentially of an inorganic silver compound and at least one metal fluoride selected from the group consisting of an alkali metal, alkaline earth metal, lanthanum, and aluminum.

Claim 3

A radio-photoluminescence dosimeter glass of low dependence on energy, consisting essentially of an inorganic silver compound and at least one inorganic complex metal fluoride.

Claim 4

A radio-photoluminescence dosimeter glass of low dependence on energy, consisting essentially of an inorganic silver compound and at least one inorganic complex metal fluoride.

Claim 5

The glass of claim 1, additionally containing at least one metal oxide selected from the group consisting of an alkali metal, alkaline earth metal, and aluminum, and phosphorus pentoxide.

Claim 6

The glass of Claim 1, additionally containing nitrogen pentoxide.

Claim 7

The glass of claim 3, additionally containing nitrogen pentoxide.

Claim 8

The glass of claim 1, consisting of 0.0001 to 15.0 %, by weight, of silver oxide Ag 2 O and a corresponding weight equivalent amount of phosphorus pentoxide P 2 O 5 calculated for the compound silver metaphosphate AgPO 3 and an amount of at least one metal fluoride so as to make 100 %, by weight.

Claim 9

The glass of claim 1, consisting of 0.001 to 10.0 %, by weight, of silver oxide Ag 2 O and a corresponding weight equivalent amount of phosphorus pentoxide P 2 O 5 calculated for the compound silver metaphosphate AgPO 3 and an amount of at least one metal fluoride so as to make 100 %, by weight.

Claim 10

The glass of claim 1, consisting of 0.01 % to 2.0 %, by weight, of silver oxide Ag 2 O and a corresponding weight equivalent amount of phosphorus pentoxide P 2 O 5 calculated for the compound silver metaphosphate AgPO 3 and an amount of at least one metal fluoride so as to make 100 %, by weight.

Claim 11

The glass according to claim 5, in which the metal oxide content is between 2.0 and 25.0 %, by weight, and the phosphorus pentoxide content is between 15.0 and 80.0 %, by weight.

Claim 12

The glass according to claim 1, additionally containing 0.5 to 5.0 %, by weight, of nitrogen pentoxide N 2 O 5 .

Claim 13

The glass of claim 6, additionally containing 2 to 25 %, by weight, of a metal oxide selected from the group consisting of an alkali metal, alkaline earth metal, and aluminum, 15 to 80 %, by weight, of phosphorus pentoxide, and 0.5 to 5.0 %, by weight, of nitrogen pentoxide.

Claim 14

The glass of claim 1, consisting of 0.02 to 1.7 %, by weight, of silver oxide Ag 2 O, 0.01 to 1.0 %, by weight of phosphorus pentoxide P 2 O 5 , and 5.0 to 99.5 %, by weight, of at least one of the metal fluorides of claim 1.

Claim 15

The glass of claim 12, additionally containing 5.0 % to 25.0 %, by weight, of a metal oxide selected from the group consisting of an alkali metal, alkaline earth metal, and aluminum and up to 77.0 %, by weight, of phosphorus pentoxide P 2 O 5 .

Claim 16

The glass of claim 13, additionally containing 1.0 to 2.0 %, by weight, of nitrogen pentoxide N 2 O 5 .

Claim 17

The glass according to claim 12, additionally containing at least one of the following metal oxides in the amounts given: up to 10.0 %, by weight, of an alkali metal oxide, up to 22.0 %, by weight, of an alkaline earth metal oxide, and up to 10.0 %, by weight, of aluminum oxide.

Claim 18

The glass of claim 15, containing at least one of the following alkali metal oxides in the amounts given: up to 1.0 %, by weight, of sodium oxide Na 2 O and up to 9.0 %, by weight, of lithium oxide Li 2 O.

Claim 19

The glass of claim 15, containing at least one of the following alkaline earth metal oxides in the amounts given: up to 3.0 %, by weight, of magnesium oxide MgO and up to 4.0 %, by weight, of calcium oxide CaO.

Claim 20

The glass of claim 15, containing at least one of the following alkaline earth metal oxides in the amounts given: up to 3.0 %, by weight, of magnesium oxide MgO and up to 22.0 %, by weight, of barium oxide BaO.

Claim 21

The glass of claim 15, containing aluminum oxide Al 2 O 3 in an amount not exceeding 10.0 %, by weight.

Claim 22

The glass of claim 12, in which the fluoride is present in an amount of at least 5 % and up to 50.0 %, by weight, of an alkali metal fluoride, up to 65.0 %, by weight, of an alkaline earth metal fluoride, and up to 35.0 %, by weight, of aluminum or lanthanum fluoride.

Claim 23

The glass of claim 12, in which the fluoride is present in an amount of at least 5 % and up to 50.0 %, by weight, of an alkali metal fluoride.

Claim 24

The glass of claim 12, in which the fluoride is present in an amount of at least 5 % and up to 65.0 %, by weight, of an alkaline earth metal fluoride.

Claim 25

The glass of claim 12, in which the fluoride is present in an amount of at least 5 % and up to 35.0 %, by weight, of aluminum or lanthanum fluoride.

Claim 26

The glass of claim 21, in which the alkali metal fluoride is present in an amount of at least 5 % and up to 49.0 %, by weight, of lithium flouride LiF and up to 5.0 %, by weight, of potassium fluoride KF.

Claim 27

The glass of claim 22, in which the alkaline earth metal fluoride is present in an amount of at least 5 % and up to 10.0 %, by weight, of beryllium fluoride BeF 2 , up to 10.0 %, by weight, of magnesium fluoride MgF 2 , up to 32.0 %, by weight, of calcium fluoride CaF 2 , up to 12.0 %, by weight, of strontium fluoride SrF 2 , and up to 15.0 %, by weight, of barium fluoride BaF 2 .

Claim 28

The glass of claim 23, in which at least one of the aluminum and lanthanum fluorides is present in an amount of at least 5 % and up to 6.0 %, by weight, of lanthanum fluoride LaF 3 and up to 31.0 %, by weight, of aluminum fluoride AlF 3 .

Claim 29

A radio-photoluminescence dosimeter glass of low dependence on energy, said glass essentially consisting of a silver compound selected from the group consisting of silver metaphosphate, silver nitrate, silver carbonate, and silver lithium metaphosphate, and a metal fluoride selected from the group consisting of an alkali metal fluoride, and alkaline earth metal fluoride, aluminum fluoride, lanthanum fluoride, the hydrogen fluorides of said metals, and the inorganic complex fluorides thereof, the fluoride content of said glass being at least about 5 %, by weight, and the silver oxide content of said glass being between about 0.0001 and about 15.0 %, by weight.

Claim 30

A radio-photoluminescence dosimeter glass of low dependence on energy, said glass essentially consisting of a silver compound selected from the group consisting of silver metaphosphate, silver nitrate, silver carbonate, and silver lithium metaphosphate, and a metal fluoride selected from the group consisting of an alkali metal fluoride, and alkaline earth metal fluoride, aluminum fluoride, lanthanum fluoride, the hydrogen fluorides of said metals, and the inorganic complex fluorides thereof, the fluoride content of said glass being at least about 5 %, by weight, and the silver oxide content of said glass being between about 0.0001 and about 15.0 %, by weight.

Claim 31

A radio-photoluminescence dosimeter glass of low dependence on energy, said glass essentially consisting of a silver compound selected from the group consisting of silver metaphosphate, silver nitrate, silver carbonate, and silver lithium metaphosphate, a metal fluoride selected from the group consisting of an alkali metal fluoride, an alkaline earth metal fluoride, aluminum fluoride, lanthanum fluoride, the hydrogen fluorides of said metals, and the inorganic complex fluorides thereof, and a metal metaphosphate selected from the group consisting of an alkali metal metaphosphate, an alkaline earth metal metaphosphate and aluminum metaphosphate, the fluoride content of said glass being at least about 5 %, by weight, the silver oxide content of said glass being between 0.0001 % and 15.0 %, by weight, and the metaphosphate content including the silver metaphosphate content of said glass being between 95.0 % and 0.5 %, by weight.

Claim 32

A radio-photoluminescence dosimeter glass of low dependence on energy, said glass essentially consisting of a silver compound selected from the group consisting of silver metaphosphate, silver nitrate, silver carbonate, and silver lithium metaphosphate, a metal fluoride selected from the group consisting of an alkali metal fluoride, an alkaline earth metal fluoride, aluminum fluoride, lanthanum fluoride, the hydrogen fluorides of said metals, and the inorganic complex fluorides thereof, and a metal metaphosphate selected from the group consisting of an alkali metal metaphosphate, an alkaline earth metal metaphosphate and aluminum metaphosphate, the fluoride content of said glass being at least about 5 %, by weight, the silver oxide content of said glass being between 0.0001 % and 15.0 %, by weight, and the metaphosphate content including the silver metaphosphate content of said glass being between 95.0 % and 0.5 %, by weight.