Method for manufacturing ingots of high-melting ferroalloys and metal alloys with good forming properties
Assignee: Vereinigte Edelstahlwerke AG
•
Filing: 1974-05-28
•
Granted: 1976-01-06
•
Expires: 1994-05-28
Abstract
Abstract Ingots of high-melting ferroalloys and metal alloys with good forming properties are obtained by melting a consumable electrode in a slag bath in an ingot mold while cooling the ingot mold and providing a high pressure gas inert to the slag above the slag bath. The apparatus is a trisectional pressure chamber including an ingot mold which may be surrounded by a pressure container, a bell-type distributing device surrounding and extending above the mold, a cap for the distributing device through which a guide rod for a consumable electrode is introduced into the mold and a gland mounted in the cap for sealing the pressure chamber.
Inventors
- 👤 Josef Frehser
- 👤 Christian Kubisch
- 👤 Karl Swoboda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:19
CPC Classifications
C; C22; C22B; C22B9/00; C22B9/16; C22B9/18; B; B22; B22D; B22D23/00; B22D23/06; B22D23/10
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
139 words
A method of manufacturing ingots of high-melting ferroalloys and metal alloys having favorable formability and a fine grain solidification texture comprising: melting at least one consumable electrode in a slag bath in an ingot mold; cooling the ingot mold wall with a liquid metal; providing a gas inert to the slag under a pressure of at least 20 atmospheres above the slag; and adjusting the cooling of the ingot mold in the area of the immersed electrode to retain the liquid condition of the slag, and in the area of the ingot mold wall to retain the solid condition of the slag, both conditions being retained during the melting phase to obtain an area of solid slag between the ingot mold wall and liquid slag area of a dimension of between 1/100 and 1/10 of the ingot mold diameter.
Claim 2
Independent Claim
139 words
A method of manufacturing ingots of high-melting ferroalloys and metal alloys having favorable formability and a fine grain solidification texture comprising: melting at least one consumable electrode in a slag bath in an ingot mold; cooling the ingot mold wall with a liquid metal; providing a gas inert to the slag under a pressure of at least 20 atmospheres above the slag; and adjusting the cooling of the ingot mold in the area of the immersed electrode to retain the liquid condition of the slag, and in the area of the ingot mold wall to retain the solid condition of the slag, both conditions being retained during the melting phase to obtain an area of solid slag between the ingot mold wall and liquid slag area of a dimension of between 1/100 and 1/10 of the ingot mold diameter.
Claim 3
Dependent Claim
26 words
The method according to claim 1, wherein the liquid metal used to cool the ingot mold is sodium having a temperature of between 350°C and 650°C.
Claim 4
Dependent Claim
16 words
The method according to claim 1, wherein the electrode is continuously melted in the slag bath.
Claim 5
Dependent Claim
32 words
The method according to claim 1, further comprising adding a nitrogen-containing substance in finely divided form with a maximum grain size of 6 mm to the slag bath during the melting phase.
Claim 6
Dependent Claim
16 words
The method according to claim 4, wherein the nitrogen-containing substance is added in a pre-heated condition.
Claim 7
Dependent Claim
25 words
The method according to claim 4, wherein the nitrogen-containing substance has a melting point at least 50°C lower than the temperature of the slag bath.
Claim 8
Dependent Claim
35 words
The method according to claim 4, wherein the nitrogen-containing substance is a mixture of chromium nitride and manganese nitride and wherein chromium and manganese are present in the same ratio as in the consumable electrode.
Claim 9
Dependent Claim
32 words
The method according to claim 1, further comprising adding a ferroalloy in a finely divided form with a maximum grain size of 6 mm to the slag bath during the melting phase.
Claim 10
Dependent Claim
39 words
The method according to claim 1, further comprising adding a substance which when melted produces the ingot composition in a finely divided form with a maximum grain size of 6 mm to the slag bath during the melting phase.
Claim 11
Dependent Claim
34 words
The method according to claim 1, further comprising adding an alkaline earth metal in a finely divided form with a maximum grain size of 6 mm to the slag bath during the melting phase.
Claim 12
Dependent Claim
40 words
The method according to claim 1, further comprising adding a material having the same composition as the consumable electrode in a finely divided form with a maximum grain size of 6 mm to the slag bath during the melting phase.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-05 | 1979-07-07 | 1980-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-05 | 1983-07-07 | 1984-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-05 | 1987-07-07 | 1988-01-06 | $7700.00 | Window Closed / Lapsed |