Steel sheet having a nickel composite film and a method for manufacturing the same
Assignee: Nippon Steel Corp
•
Filing: 1973-09-10
•
Granted: 1975-07-15
•
Expires: 1993-09-10
Abstract
Abstract A steel sheet is cleaned and coated with a particular treating solution. This solution is obtained by adding Mo, W, Cu or K ion to Ni ion as the respective aqueous solutions. The film formed thereon is excellent in anti-corrosion property and paintadherence property and the product steel sheet is suitable for use as a can or container for drinks, etc.
Inventors
- 👤 Hidejiro Asano
- 👤 Yashichi Ohyagi
- 👤 Takatoshi Egawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:27
CPC Classifications
B; B05; B05D; B05D3/00; B05D3/10; B05D3/102; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12937; Y10T428/12951; Y10T428/12972
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
133 words
A METHOD FOR THE MANUFACTURE OF A STEEL SHEET HAVING A NICKEL COMPOSITE FILM WHICH COMPRISES SUBJECTING A SURFACE OF A STEEL SHEET TO A CLEANING TREATMENT, COATING AN AQUEOUS SOLUTION ON SAID CLEANED SURFACE, SAID AQUEOUS SOLUTION BEING OBTAINED BY ADDING TO AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF NICKEL AT LEAST ONE MEMBER SELECTED FROM THE GROUP CONSISTING OF AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF MOLYBDENUM, AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF TUNGSTEN, AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF COPPER AND AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF POTASSIUM, HEATING THE SAME IN THE ATMOSPHERE OF A NON-OXIDIZING GAS, AND THEREBY FORMING ON SAID STEEL SHEET A FILM CONSISTING OF NICKEL AND AT LEAST ONE MEMBER SELECTED FROM MOLYBDENUM, TUNGSTEN, COPPER AND POTASSIUM.
Claim 2
Independent Claim
133 words
A METHOD FOR THE MANUFACTURE OF A STEEL SHEET HAVING A NICKEL COMPOSITE FILM WHICH COMPRISES SUBJECTING A SURFACE OF A STEEL SHEET TO A CLEANING TREATMENT, COATING AN AQUEOUS SOLUTION ON SAID CLEANED SURFACE, SAID AQUEOUS SOLUTION BEING OBTAINED BY ADDING TO AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF NICKEL AT LEAST ONE MEMBER SELECTED FROM THE GROUP CONSISTING OF AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF MOLYBDENUM, AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF TUNGSTEN, AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF COPPER AND AN AQUEOUS SOLUTION CONTAINING A METALLIC ION OF POTASSIUM, HEATING THE SAME IN THE ATMOSPHERE OF A NON-OXIDIZING GAS, AND THEREBY FORMING ON SAID STEEL SHEET A FILM CONSISTING OF NICKEL AND AT LEAST ONE MEMBER SELECTED FROM MOLYBDENUM, TUNGSTEN, COPPER AND POTASSIUM.
Claim 3
Dependent Claim
18 words
A method according to claim 1 in which the heaTing is held at temperatures between 200*C and 750*C.
Claim 4
Dependent Claim
19 words
A method according to claim 1 in which the coating is held by means of spraying, rolling or dipping.
Claim 5
Dependent Claim
17 words
A method according to claim 1 in which a surface active agent is added in the coating.
Claim 6
Dependent Claim
38 words
A method according to claim 1 in which the amount adhering from the treatment with aqueous solution is 1g/l to 100g/l for the nickel ion, and 20g/l or less for the molybdenum, tungsten, copper or potassium ion, respectively.
Claim 7
Dependent Claim
28 words
A steel sheet having a nickel composite film containing at least one member selected from the group consisting of molybdenum, tungsten, copper and potassium in the nickel film.
Claim 8
Dependent Claim
28 words
A steel sheet having a nickel composite film containing at least one member selected from the group consisting of molybdenum, tungsten, copper and potassium in the nickel film.
Claim 9
Dependent Claim
44 words
A steel sheet having a nickel composite film consisting of two layers, the lower layer being iron-nickel alloy and the upper layer being a mixed film of nickel with one or more member selected from the group consisting of molybdenum, tungsten, copper and potassium.
Claim 10
Dependent Claim
44 words
A steel sheet having a nickel composite film consisting of two layers, the lower layer being iron-nickel alloy and the upper layer being a mixed film of nickel with one or more member selected from the group consisting of molybdenum, tungsten, copper and potassium.
Claim 11
Dependent Claim
38 words
A method according to claim 5 in which the amount adhering from the treatment with aqueous solution is 5g/l to 25g/l for the nickel ion and 5g/l or less for the molybdenum, tungsten, copper or potassium ion, respectively.
Claim 12
Independent Claim
118 words
A method for the manufacture of a steel sheet having a nickel composite film which comprises subjecting a surface of a steel sheet to a cleaning treatment, coating an aqueous solution on said cleaned surface, said aqueous solution being obtained by adding to an aqueous solution of nickel acetate at least one member selected from the group consisting of an aqueous solution of ammonium molybdate, an aqueous solution of ammonium tungstate, an aqueous solution of copper acetate and an aqueous solution of tri-potassium phosphate, heating the same in the atmosphere of a non-oxidizing gas, and thereby forming on said steel sheet a film consisting of nickel and at least one member selected from molybdenum, tungsten, copper and potassium.
Claim 13
Independent Claim
118 words
A method for the manufacture of a steel sheet having a nickel composite film which comprises subjecting a surface of a steel sheet to a cleaning treatment, coating an aqueous solution on said cleaned surface, said aqueous solution being obtained by adding to an aqueous solution of nickel acetate at least one member selected from the group consisting of an aqueous solution of ammonium molybdate, an aqueous solution of ammonium tungstate, an aqueous solution of copper acetate and an aqueous solution of tri-potassium phosphate, heating the same in the atmosphere of a non-oxidizing gas, and thereby forming on said steel sheet a film consisting of nickel and at least one member selected from molybdenum, tungsten, copper and potassium.
Claim 14
Dependent Claim
18 words
A method according to claim 9 in which the heating is held at temperatures between 200*C and 750*C.
Claim 15
Dependent Claim
19 words
A method according to claim 9 in which the coating is held by means of spraying, rolling or dipping.
Claim 16
Dependent Claim
17 words
A method according to claim 9 in which a surface active agent is added to the coating.
Claim 17
Dependent Claim
38 words
A method according to claim 9 in which the amount adhering from the treatment with aqueous solution is 1g/l to 100g/l for the nickel ion and 20g/l or less for the molybdenum, tungsten, copper and potassium ion, respectively.
Claim 18
Dependent Claim
38 words
A method according to claim 13 in which the amount adhering from the treatment with aqueous solution is 5g/l to 25g/l for the nickel ion and 5g/l or less for the molybdenum, tungsten, copper or potassium ion, respectively.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1978-07-14 | 1979-01-13 | 1979-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1982-07-14 | 1983-01-13 | 1983-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1986-07-14 | 1987-01-13 | 1987-07-15 | $7700.00 | Window Closed / Lapsed |