Corrosion and wear resistant nickel alloy
Assignee: Furukawa Electric Co Ltd
•
Filing: 1968-12-27
•
Granted: 1972-05-02
•
Expires: 1988-12-27
Abstract
Abstract Corrosion and wear resistant nickel alloys are disclosed wherein 1-50 at. % of the Ni atoms is substituted by one or more of Fe, Mo, Co and Cr and 0-10 at. % of Ti atoms is substituted by Zr. The Ni atoms and Ti atoms are contained in an alloy consisting of 45-53 at. % of Ti and the remainder of Ni.
Inventors
- 👤 Akira Negishi
- 👤 Kiyoshi Takayanagi
- 👤 Masaru Ikeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 04:39
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/006; C22C; C22C14/00; C22C19/00; C22C19/007
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
50 words
The corrosion and wear resistant nickel alloy of claim 1, consisting of 47-52 at. % of Ti and the remainder of Ni, 1-25 at. % of Ni atoms being substituted by a metal selected from the group consisting of Mo and Cr, said alloy being easy to hot- and cold-work.
Claim 2
Dependent Claim
56 words
The corrosion and wear resistant nickel alloy of claim 1, consisting of 48-52 at. % of Ti and the remainder of Ni, 1-20 at. % of Ni atoms being substituted by a metal selected from the group consisting of Mo and Cr, said alloy being easier to hot-and cold-work than the nickel alloy of claim 2.
Claim 3
Dependent Claim
28 words
The corrosion and wear resistant nickel alloy of claim 1, wherein 0.1-7 at. % of Ti atoms are substituted by Zr, said alloy having a high mechanical strength.
Claim 4
Dependent Claim
56 words
The corrosion and wear resistant nickel alloy of claim 1, consisting of 49.5-50.5 at. % of Ti and the remainder of Ni, 2-20 at. % of Ni atoms being substituted by a metal selected from the group consisting of Mo and Cr, said alloy having excellent corrosion resistance and being particularly easy to hot- and cold-work.
Claim 5
Dependent Claim
71 words
The corrosion and wear resistant nickel alloy of claim 1, consisting of 50.7-52 at. % of Ti and the remainder of Ni, 1-20 at. % of Ni atoms being substituted by a metal selected from the group consisting of Mo and Cr, and 0.1-5 at. % of Ti atoms are substituted by Zr, said alloy having a high mechanical strength and excellent corrosion resistance and being easy to hot- and cold-work.
Claim 6
Dependent Claim
58 words
The corrosion and wear resistant nickel alloy of claim 1, consisting of 48-49 at. % of Ti and the remainder of Ni, 1-20 at. % of Ni atoms being substituted by a metal selected from the group consisting of Mo and Cr, said alloy being capable of improving its mechanical strength by means of quenching and tempering processes.
Claim 7
Dependent Claim
59 words
The corrosion and wear resistant nickel alloy of claim 1, consisting of 48-48.6 at. % of Ti and the remainder of Ni, 1-5 at. % of Ni atoms being substituted by a metal selected from the group consisting of Mo and Cr, said alloy being capable of further improving its mechanical strength by means of quenching and tempering processes.
Claim 8
Dependent Claim
51 words
The corrosion and wear resistant nickel alloy of claim 1, wherein 1-50 at. % of the nickel atoms are replaced by Mo only and 5-95 at. % of said replacing Mo atoms are replaced by at least one of Fe and Co, said alloy having excellent corrosion resistance and cold workability.
Claim 9
Dependent Claim
33 words
The corrosion and wear resistant nickel alloy of claim 9, wherein said replacing Mo atoms are replaced by Fe and Co such that Mo, Fe and Co have an atomic ratio of 1:1:1.
Claim 10
Dependent Claim
45 words
The corrosion and wear resistant alloy of claim 1, wherein 1-50 at. % of the nickel atoms are replaced by Mo only and 5-95 at. % of said replacing Mo atoms are replaced by Fe only, said alloy having excellent corrosion resistance and cold workability.
Claim 11
Dependent Claim
29 words
The corrosion and wear resistant alloy of claim 11, wherein said replacing Mo atoms are replaced by Fe such that Mo and Fe have an atomic ratio of 2:3.
Claim 12
Dependent Claim
47 words
The corrosion and wear resistant nickel alloy of claim 1, wherein 1-50 at. % of the nickel atoms are replaced by Mo only and 5-95 at. % of said replacing Mo atoms are replaced by Co, said alloy having the most excellent corrosion resistance and cold workability.
Claim 13
Dependent Claim
20 words
The corrosion and wear resistant nickel alloy of claim 13, wherein the atomic ratio between Mo and Co is 2:3.
Claim 14
Dependent Claim
29 words
The corrosion and wear resistant nickel alloy of claim 1, wherein 1-50 at. % of the nickel atoms are replaced by Mo and Cr whose atomic ratio is 1:1.
Claim 15
Dependent Claim
31 words
The corrosion and wear resistant nickel alloy of claim 1, wherein 1-50 at. % of the nickel atoms are replaced by Cr only, said alloy having the most excellent wear resistance.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1975-05-02 | 1975-11-01 | 1976-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1979-05-02 | 1979-11-01 | 1980-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1983-05-02 | 1983-11-01 | 1984-05-02 | $7700.00 | Window Closed / Lapsed |