Soft magnetic material

Claim 1

A SOFT MAGNETIC MATERIAL FORMED BY INTIMATELY MIXING, A SINTERING AT A TEMPERATURE IN THE RANGE FROM APPROXIMATELY 2160*F. TO APPROXIMATELY 2240*F., FE2O3 ABOUT 54 MOL PERCENT, ZNO ABOUT 17 MOL PERCENT, MNO2 ABOUT 27 MOL PERCENT, MGSIO2 ABOUT 1 MOL PERCENT, AND SILICA ABOUT 1 MOL PERCENT, MIXING SAID MATERIALS WITH AN ORGANIC BINDER AND LUBRICANT ABOUT 1 PERCENT BY WEIGHT AND WITH THE MOISTURE SUFFICIENT TO PRODUCE A PLASTIC MASS, FORMING TO THE DESIRE SHAPE, DRYING AND SINTERING AT THE SAID TEMPERATURE IN AIR, IN WHICH THE EXCESS OF AIR IS IN THE RANGE OF 20 TO 40%, AND COOLING THE MATERIAL AS RAPIDLY AS POSSIBLE, WITHOUT CAUSING FRACTURE OF THE BODY, AT APPROXIMATELY 25*C. PER MINUTE, AND GRINDING AWAY THE SURFACE LAYER AT VARIOUS POINTS LEAVING A CONDUCTING PATH OF CONTROLLABLE RESISTANCE VALUE AND THEREBY PROVIDING A MEANS FOR PRODUCING AN INDUCTANCE AND RESISTANCE IN PARALLEL OR SERIES IN A SINGLE COMPONENT.