Process of manufacturing ceramic ferrites

Claim 1

IN A METHOD OF REPRODUCIBLY MANUFACTURING FERRITIC CERAMIC PRODUCTS WITH CORRESPONDING ELECTRIC AND MAGNETIC PROPERTIES FROM DRY MATERIALS, THE STEPS OF MIXING A BATCH OF PARTICLES CONSISTING ESSENTIALLY OF 20-80% FE2O3, 20-80, MGO, AND 0-4% MNO WITH VOLATILE LIQUID HYDROCARBON SOLVENT AND WITH A FATTY ACID CONTAINING 4-18 CARBON ATOMS TO FORM A SLURRY WITH THE SURFACES OF THE PARTICLES HAVING LIPOPHILIC PROPERTIES, THE ACID BEING FROM 2-10% OF THE WEIGHT OF THE BATCH, REMOVING EXCESS SOLVENT TO DRY THE RESULTING PRODUCT, HOMOGENTIZING THE RESULTING PRODUCT WITH A SMALL AMOUNT OF SAID SOLVENT SUFFICIENT TO MAKE THE LAST SAID PRODUCT INTO A SHAPABLE PLASTIC MASS, HOMOGENIZING THE PLASTIC MASS, FORMING THE HOMOGENIZED PLASTIC MASS INTO A SHAPE, AND FIRING SAID SHAPE AT A TEMPERATURE OF APPROXIMATELY 1200*-1450* C. TO SOLIDIFY IT.