Film-forming silicone emulsion composition
Assignee: Momentive Performance Materials Japan LLC
•
Filing: 1994-08-23
•
Granted: —
•
Expires: 2014-08-23
Abstract
Abstract A film-forming silicone emulsion composition which forms a film exhibiting a good adhesion to various substrates, and having a good water repellency and good release properties, comprising the following components which are mixed and dispersed: (A) a silicone emulsion comprising: (a) a specific organopolysiloxane containing at least one amino group or epoxy group per molecule; (b) an emulsifying agent; and (c) water; and (B) a specific hydrolyzable silane containing at least one functional group per molecule.
Inventors
- 👤 Hiroyoshi C/O Toshiba Shimotsu
- 👤 Toshihiro C/O Toshiba Takahashi
- 👤 Sachiko C/O Toshiba Yusa
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-08 12:19
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/04; C09D183/06; C09D183/08
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
148 words
A film-forming silicone emulsion composition comprising the following components which are mixed and dispersed: (A) a silicone emulsion comprising: (a) an organopolysiloxane represented by the following general formula: wherein R¹'s each represents the same or different C₁₋₂₀ monovalent hydrocarbon group or hydrogen atom; R²'s each represents a hydroxyl group or a hydrolyzable group; R³'s each represents an amino-containing group or an epoxy-containing group; and a, b and c satisfy the relationships of 0 < a < 3, 0 ≦ b < 2, and 0 < c ≦ 1, respectively, containing at least one amino group or epoxy group per molecule; (b) an emulsifying agent; and (c) water; and (B) a hydrolyzable silane containing at least one functional group per molecule wherein said functional group is an amino-containing group if R³ in the component (A) is an epoxy-containing group, or an epoxy-containing group if R³ is an amino-containing group.
Claim 2
Dependent Claim
95 words
A film-forming silicone emulsion composition as claimed in claim 1, which further comprises: (C) a silicone emulsion comprising: (d) an organopolysiloxane represented by the following general formula: wherein R⁴'s each represents the same or different C₁₋₂₀ monovalent hydrocarbon group hydrogen atom; R⁵'s each represents a hydroxyl group or a hydrolyzable group; and d and e satisfy the relationships of 0 < d < 3, 0 < e < 2, and 1.9 < d + e < 2.2, containing at least one hydroxyl group or hydrolyzable group per molecule; (e) an emulsifying agent; and (f) water.
Claim 3
Dependent Claim
25 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein the organopolysiloxane of component (a) has a molecular weight of from 500 to 500,000.
Claim 4
Dependent Claim
31 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein the emulsifying agent of component (b) is nonionic surface active agents, anionic surface active agents or cationic surface active agents.
Claim 5
Dependent Claim
38 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein the emulsifying agent of component (b) is used in an amount of from 5 to 100 parts by weight per 100 parts by weight of component (a).
Claim 6
Dependent Claim
36 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein water of component (c) is used in an amount of from 50 to 500 parts by weight per 100 parts by weight of component (a).
Claim 7
Dependent Claim
25 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein the hydrolyzable silane of component (B) is an epoxy-containing alkoxysilane or an amino-containing alkoxysilane.
Claim 8
Dependent Claim
38 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein the hydrolyzable silane of component (B) is used in an amount of from 5 to 300 parts by weight per 100 parts by weight of component (a).
Claim 9
Dependent Claim
25 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein the organopolysiloxane of component (d) has a molecular weight of from 500 to 500,000.
Claim 10
Dependent Claim
37 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein the organopolysiloxane of component (d) is used in an amount of from 5 to 200 parts by weight per 100 parts by weight of component (a).
Claim 11
Dependent Claim
31 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein the emulsifying agent of component (e) is nonionic surface active agents, anionic surface active agents or cationic surface active agents.
Claim 12
Dependent Claim
38 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein the emulsifying agent of component (e) is used in an amount of from 5 to 100 parts by weight per 100 parts by weight of component (d).
Claim 13
Dependent Claim
34 words
A film-forming silicone emulsion composition as claimed in claim 1, wherein water of component (f) is used in an amount of from 50 to 100 parts by eight per 100 parts of component (d).